A kind of natural filter stick granular material and its preparation method and application

A particulate material and filter rod technology, applied in applications, e-liquid filters, tobacco, etc., can solve problems such as poor processability, negative impact on cigarette smoking, and complex filter particle technology, so as to prevent further changes, improve richness, The effect of easy availability of raw materials

Active Publication Date: 2018-09-11
YUNNAN XINYUN TECH DEV CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the deficiencies of the prior art, provide a kind of natural filter stick granular material and its preparation method and application, and use corn smut, which causes a large amount of economic losses in agricultural production, to prepare cigarette particles , not only the source of raw materials is guaranteed, but also can turn harm into wealth, improve the economic income of growers on the basis of recovering economic losses, and solve the problem of conventional filter particles with complicated process, poor processability, and negative impact on cigarette smoking etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of natural filter stick granular material and its preparation method and application
  • A kind of natural filter stick granular material and its preparation method and application
  • A kind of natural filter stick granular material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Take a number of incomplete metamorphosis corn ears infected by smut, put them in a microwave oven to inactivate the pathogenic bacteria, roast them until fragrant, then crush them, and pass them through a 100-mesh sieve to obtain protein powder. Mix the saturated sodium citrate solution into the protein powder at a mass ratio of 1:1, mix evenly and then granulate, screen the 20-40 mesh granules and dry them at 72°C until the water content is 8%±2%. The Zimbabwean tobacco extract was dissolved in 75% alcohol, sprayed onto the particle surface at a mass ratio of 0.05%, and the fragrance-loaded particles were sealed and stored in a constant temperature and humidity chamber (temperature 25°C, humidity 40%) to balance for 5 hours.

[0035] Select the tow specification of Y3.0 / 35000, add the prepared natural filter rod granular material to it, roll the rod in the filter rod forming machine according to the amount of 1.5mg / mm, and then combine the formed rod with the same The...

Embodiment 2

[0041] Take a number of incomplete metamorphosis corn ears infected by smut, put them in a microwave oven to inactivate the pathogenic bacteria, roast them until fragrant, then crush them, and pass them through a 100-mesh sieve to obtain protein powder. Mix the saturated sodium chloride solution into the protein powder at a mass ratio of 1:2, mix evenly and then granulate, screen the 20-40 mesh granules and dry them at 70°C until the water content is 8%±2%. The extract of Yunyan tobacco was dissolved in 75% alcohol, sprayed on the surface of the particles at a mass ratio of 0.12%, and the particles loaded with incense were sealed and stored in a constant temperature and humidity chamber (temperature 25°C, humidity 40%) to balance for 5 hours.

[0042] Select the tow specification of Y3.0 / 35000, add the prepared natural filter rod granular material to it, roll the rod in the filter rod forming machine according to the amount of 1.5mg / mm, and then combine the formed rod with the ...

Embodiment 3

[0048]Take a number of incomplete metamorphosis corn ears infected by smut, put them in a microwave oven to inactivate the pathogenic bacteria, roast them until fragrant, then crush them, and pass them through a 100-mesh sieve to obtain protein powder. Mix saturated sodium citrate and saturated sodium chloride solution into the protein powder in a mass ratio of 1:1.5 (the mixing ratio of saturated sodium citrate and saturated sodium chloride aqueous solution is 1:1), mix well, granulate and shape, and screen The 20-40 mesh particles are dried at 70°C until the water content is 8%±1%. The Brazilian tobacco extract was dissolved in 75% alcohol, sprayed onto the particle surface at a mass ratio of 0.2%, and the incense-loaded particles were sealed and stored in a constant temperature and humidity chamber (temperature 25°C, humidity 40%) to balance for 5 hours.

[0049] Select the tow specification of Y3.0 / 35000, add the prepared natural filter rod granular material to it, roll th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a natural filter rod particle material as well as a preparation method and application thereof, and belongs to the technical field of a cigarette material. The method comprises the following steps: processing multiple corn ears which are infected by sporisorium reiliana and are in incomplete metamorphosis with microwave before producing black powder, grinding the corn ears and screening the ground corn ears by virtue of a 100-mesh sieve so as to obtain protein powder; then, adding one or two of sodium citrate and sodium chloride saturated solutions to the protein powder according to ratio of (1-3) to 1, uniformly mixing and granulating, and drying particles of 20-40 meshes at 70 DEG C until moisture content is 6-10%; and finally, flavoring with a tobacco extract so as to obtain the natural filter rod particle material. The particle material has rough surface and large specific surface area, and meanwhile the particle material reserves natural fragrance of corn and mellow taste of tobacco, so that the particle material, when adsorbing harmful substances in the cigarette, can enrich cigarette aroma and improve the sweetness of the cigarette. The preparation method disclosed by the invention is simple in process and strong in operability, and the preparation method achieves recycling of wastes, so as to give new and higher utilization value to corns which are originally killed due to diseases; therefore, the invention has a good application prospect.

Description

technical field [0001] The invention belongs to the technical field of cigarette materials, and in particular relates to a natural adsorption particle material added to a cigarette filter rod, a preparation method and application thereof. Background technique [0002] With the continuous enhancement of health awareness of cigarette consumers, the "coke reduction and harm reduction" of cigarettes has become an important issue in the research and development of cigarette production. As a new type of material, cigarette filter particles are more and more widely used in the actual production of cigarettes. middle. However, there are still many problems in the existing granules. For example, activated carbon granules, which are most widely used in production, are loosely combined with the tow, easily fall off and pollute shredded tobacco, and have high hardness, which is easy to damage the blade for cutting filter rods during the production process. In addition, particles made o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A24D3/04A24D3/14A24D3/16A24D3/02
Inventor 李玲冯伟博杨刘斌聂铭陈学艳和志伟蔡清婷
Owner YUNNAN XINYUN TECH DEV CO LTD