Montmorillonite material for livestock and poultry

A montmorillonite and montmorillonite technology, which is applied in the field of montmorillonite feed preparations for livestock and poultry, can solve the problems of unfavorable feed absorption and utilization, affecting feed palatability, low absorption and utilization rate, etc., so as to save feed cost and improve convenience. The effect of strong adsorption capacity

Inactive Publication Date: 2015-12-30
云南鑫乾矿业有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the nutrition and functionality of livestock and poultry feed, various mineral elements and trace elements, such as potassium, calcium, sodium, magnesium, iron, copper, zinc, etc., are added to the feed in the prior art, resulting in high feed cost, Moreover, the mineral elements and trace elements added in the feed generally exist in the form of inorganic compounds, and the absorption and utilization rate by livestock and poultry is low.
[0006] In addition, montmorillonite is odorless, but has an obvious earthy taste. If the powdered montmorillonite is directly mixed with the diet or feed, the palatability of the feed will be affected due to the earthy taste of the montmorillonite itself, which is not conducive to Feed absorption and utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Montmorillonite material for livestock and poultry

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A montmorillonite agent for livestock and poultry, characterized in that it is made of the following raw materials in parts by weight: 100 parts of natural montmorillonite, 50 parts of table salt, 0.8 part of sodium carboxymethyl cellulose, water 30 parts, this montmorillonite agent is prepared by the following method:

[0022] (1) Grinding 100 parts of natural montmorillonite into fine powder with a fineness of 200 mesh;

[0023] (2) Dissolving the salt and sodium carboxymethyl cellulose in the above parts by weight in water;

[0024] (3) Mix montmorillonite fine powder and aqueous solution, and stir to form montmorillonite agent;

[0025] (4) Pass the montmorillonite agent through a feed granulator to form granules with a particle size of 2mm.

[0026] The per 1000g montmorillonite preparation prepared in this embodiment contains 5g of potassium, 2g of calcium, 1g of sodium, 3g of magnesium, 10g of iron, 0.01g of copper, 0.09g of zinc, 0.3g of manganese and 0.02g of...

Embodiment 2

[0033] A montmorillonite agent for livestock and poultry, characterized in that it is made of the following raw materials in parts by weight: 100 parts of natural montmorillonite, 10 parts of table salt, 0.2 part of sodium carboxymethyl cellulose, water 20 parts, this montmorillonite agent is prepared by the following method:

[0034] (1) Grinding the above-mentioned natural montmorillonite into fine powder with a fineness of 600 mesh;

[0035] (2) Dissolving the salt and sodium carboxymethyl cellulose in the above parts by weight in water;

[0036] (3) Mix montmorillonite fine powder and aqueous solution, and stir to form montmorillonite agent;

[0037] (4) Pass the montmorillonite agent through a feed pellet machine to form granules with a particle size of 3mm.

[0038] The per 1000g montmorillonite agent prepared in this embodiment contains 6.5g of potassium, 3.5g of calcium, 1.8g of sodium, 3.6g of magnesium, 13g of iron, 0.03g of copper, 0.12g of zinc, 0.38g of manganes...

Embodiment 3

[0040] A montmorillonite agent for livestock and poultry, characterized in that it is made of the following raw materials in parts by weight: 100 parts of natural montmorillonite, 30 parts of table salt, 0.6 part of sodium carboxymethyl cellulose, 25 parts of ionized water, this montmorillonite agent is prepared by the following method:

[0041] (1) Grinding the above-mentioned natural montmorillonite into fine powder with a fineness of 400 mesh;

[0042] (2) Dissolving the salt and sodium carboxymethyl cellulose in the above parts by weight in water;

[0043] (3) Mix montmorillonite fine powder and aqueous solution, and stir to form montmorillonite agent;

[0044] (4) Pass the montmorillonite agent through a feed granulator to form granules with a particle size of 2mm.

[0045] The per 1000g montmorillonite agent prepared in this embodiment contains 6g of potassium, 3g of calcium, 1.5g of sodium, 3.4g of magnesium, 12g of iron, 0.02g of copper, 0.1g of zinc, 0.35g of manganes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a montmorillonite material for livestock and poultry, and belongs to the technical field of montmorillonite processing. The montmorillonite material is prepared from the following raw materials in parts by weight: 100 parts of natural montmorillonite, 10-50 parts of salt, 0.2-0.8 part of sodium carboxymethylcellulose, and 20-30 parts of water. The montmorillonite material is prepared through the following method: (1) grinding natural montmorillonite into fine powder with a fineness of 200-600 meshes; (2) dissolving salt and sodium carboxymethylcellulose in water; (3) mixing the montmorillonite fine powder with the water solution, and stirring the obtained mixture so as to obtain a montmorillonite material; and (4) preparing the montmorillonite material into particles with a particle size of 2-3 mm by a feed granulator. The montmorillonite material disclosed by the invention has the beneficial effects that the material can promote the absorption and utilization of feeds, can improve the palatability of montmorillonite, and can effectively prevent the diarrhea of livestock and poultry and promote the growth of livestock and poultry, and the like.

Description

technical field [0001] The invention relates to the technical field of montmorillonite processing and utilization, in particular to a montmorillonite material agent for livestock and poultry. Background technique [0002] Montmorillonite (montmod Uonite), also known as microcrystalline kaolinite, is a layered structure, flaky crystal silicate clay ore, named after it was first discovered in Montmorillonite, France. Montmorillonite is an important clay mineral, generally massive or earthy, with a molecular formula of (Al,Mg)2[Si4O10](OH)2 nH2O, with an aluminum-oxygen octahedron in the middle and silicon-oxygen tetrahedra up and down. Clay minerals with a three-layer sheet structure contain water and some exchange cations between the crystal structure layers, have a high ion exchange capacity, and have a high water absorption and expansion capacity. Montmorillonite crystals belong to the monoclinic crystal system containing water Layered structure Silicate minerals. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A23K1/175A23K1/00
Inventor 施如贵张文富
Owner 云南鑫乾矿业有限公司