Radiation-resistant rubber pipe and preparation method thereof

A rubber tube and anti-radiation technology, which is applied in the direction of hoses, pipes, damage protection, etc., can solve problems such as potential safety hazards, and achieve the effects of firm bonding, strong radiation resistance, and solving potential safety hazards

Inactive Publication Date: 2015-12-30
邵素英
View PDF17 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem solved by the present invention is to overcome the defects of the existing corrosion-resistant rubber tubes, using low-density polyethylene (LLDPE), ultra-high molecular weight polyethylene (UHMWPE) and polymer cross-linked polyethylene as the main raw materials, scientifically compounding and After vulcanization of the rubber tube, the lining film is prepared from chemical substances such as polyimide, tetraethylpentamine, α-sulfo fatty acid alkyl ester salt, epoxy resin, SBR latex, rosin, etc., which have excellent bonding properties. Corona treatment is carried out on the bonding surface of the inner lining film and the bonding surface of the rubber tube to enhance its cohesiveness, and the surface layer is compounded with fiberglass reinforced fiber with radiation-proof performance, so that the surface layer of the rubber tube has excellent anti-corrosion properties. Radiation, especially to solve the potential safety hazards caused by ionizing radiation for pipelines transporting oil and natural gas, and finally prepare a kind of rubber with firm bonding of the lining film, which can transport LPG, LNG and strong corrosive chemical solvents, and strong radiation resistance Tube

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A radiation-proof rubber tube, comprising a rubber tube body, the rubber tube body sequentially includes an inner layer, an intermediate layer and a surface layer from the inside to the outside;

[0062] The inner layer is formed by vulcanizing and bonding the EPDM layer and the inner lining film;

[0063] The color of the EPDM rubber is milky white;

[0064] The inner lining film is mainly prepared from the following raw materials in parts by weight: 30 parts of LLDPE, 25 parts of polyvinyl alcohol, 20 parts of UHMWPE, 15 parts of polymer cross-linked polyethylene, 9 parts of polyimide, and 7 parts of tetraethylpentamine , 3 parts of α-sulfo fatty acid alkyl ester salt, 3 parts of epoxy resin, 5 parts of SBR latex, 4 parts of rosin;

[0065] The lining film is blown and stretched to form a film after extruding raw materials by a conventional method, and the thickness of the lining film is 0.42 mm.

[0066]The middle layer is made of EPDM rubber, EPDM cord, polypropyl...

Embodiment 2

[0087] A radiation-proof rubber tube, comprising a rubber tube body, the rubber tube body sequentially includes an inner layer, an intermediate layer and a surface layer from the inside to the outside;

[0088] The inner layer is formed by vulcanizing and bonding the EPDM layer and the inner lining film;

[0089] The color of the EPDM rubber is milky white;

[0090] The inner lining film is mainly prepared from the following raw materials in parts by weight: 20 parts of LLDPE, 20 parts of polyvinyl alcohol, 15 parts of UHMWPE, 10 parts of polymer cross-linked polyethylene, 8 parts of polyimide, and 5 parts of tetraethylpentamine , 2 parts of α-sulfo fatty acid alkyl ester salt, 2 parts of epoxy resin, 4 parts of SBR latex, 3 parts of rosin;

[0091] The lining film is blown and stretched to form a film after extruding raw materials by a conventional method, and the thickness of the lining film is 0.35mm.

[0092] The middle layer is made of EPDM rubber, EPDM cord, polypropyl...

Embodiment 3

[0113] A radiation-proof rubber tube, comprising a rubber tube body, the rubber tube body sequentially includes an inner layer, an intermediate layer and a surface layer from the inside to the outside;

[0114] The inner layer is formed by vulcanizing and bonding the EPDM layer and the inner lining film;

[0115] The color of the EPDM rubber is milky white;

[0116] The inner lining film is mainly prepared from the following raw materials in parts by weight: 40 parts of LLDPE, 30 parts of polyvinyl alcohol, 25 parts of UHMWPE, 20 parts of polymer cross-linked polyethylene, 10 parts of polyimide, and 8 parts of tetraethylpentamine , 4 parts of α-sulfo fatty acid alkyl ester salt, 4 parts of epoxy resin, 6 parts of SBR latex, 5 parts of rosin;

[0117] The lining film is blown and stretched to form a film after extruding raw materials by a conventional method, and the thickness of the lining film is 0.5 mm.

[0118] The middle layer is made of EPDM rubber, EPDM cord, polypropy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a radiation-resistant rubber pipe and a preparation method thereof. According to the radiation-resistant rubber pipe and the preparation method thereof, a lining film is prepared from low-density polyethylene, ultrahigh molecular weight polyethylene and macromolecular cross-linked polyethylene, which serve as raw materials, and chemical substances which have an excellent bonding property after scientific compounding and rubber pipe curing, meanwhile, a lining film bonding face and a rubber pipe bonding face are subjected to corona treatment, and a surface layer is compounded with glass fiber reinforced plastic reinforced fibers with radiation-resistant performance, so that the surface layer of the rubber pipe has excellent radiation resistance, potential safety hazards resulting from the ionizing radiation of a conveying pipeline are solved, and finally, the rubber pipe, which has the firmly-bonded lining film, can be used for conveying LPG, LNG and strongly-corrosive chemical solvents and is high in radiation resistance, is prepared; the ratio of absorption to X rays, gamma rays and various neutrons in nuclear radiation of the rubber pipe can reach up to 97.5-99.5%, and the bonding force (N/25mm) between the lining film and a rubber layer reaches 160-180.

Description

technical field [0001] The invention relates to the preparation of rubber tubes, in particular to a radiation-proof rubber tube and a preparation method thereof. Background technique [0002] After more than 50 years of development, my country's rubber hose belt industry has played an indispensable supporting role in the national economy. Especially with the improvement of my country's mechanization level and the application of new materials, the rubber hose belt industry has continuously penetrated into related fields. The application range and fields of rubber hose belts have been opened up, and the products are widely used in coal, metallurgy, cement, ports, mines, petroleum, automobiles, textiles, light industry, engineering machinery, construction, marine, agriculture, aviation, aerospace and other fields. In recent years, the rubber hose and belt industry has adhered to the scientific development concept, and the product varieties, specifications, and quality have achie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16L11/08F16L57/06F16L58/10F16L58/04F16L57/02F16L59/08B29C71/00
CPCF16L11/081B29C71/0081F16L57/02F16L57/06F16L58/04F16L58/1036F16L59/08
Inventor 邵素英
Owner 邵素英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products