Novel metal oxide iron-copper composite modified quartz sand filter material, and preparation method and application thereof
A composite modification, quartz sand technology, applied in chemical instruments and methods, silicon compounds, separation methods, etc., to achieve the effect of improving efficiency, reducing energy consumption, and achieving the best removal effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0052] Example 1 Preparation of metal oxide iron copper composite modified quartz sand filter material
[0053] 1. Materials required for the preparation of metal oxide composite modified sand
[0054] (1) The required materials are shown in Table 1.
[0055] Table 1
[0056]
[0057] (2) Handling of test materials
[0058] Ordinary quartz sand (RQS): sieve the diameter of 0.9~1.43mm, immerse in HCl solution of pH=1 for 24h, then wash with distilled water to neutrality, then dry in 110℃ oven, cool at room temperature and put into polyethylene bottle In standby.
[0059] Iron trichloride modifier (FeCl 3 ): Accurately weigh 270.5g of ferric chloride hexahydrate (analytical purity) and dissolve it in distilled water, transfer to a 500mL volumetric flask, dilute the distilled water to 500mL, shake well, the concentration of the solution of ferric chloride is 2.000mol / L . The amount of ferric chloride added per gram of quartz sand is called the ferric chloride dosing ratio C 1 , Unit mL·g...
Example Embodiment
[0079] Example 2 BET specific surface area and morphology of metal oxide iron copper composite modified quartz sand filter material
[0080] 1. The size of the specific surface area reflects the size of the particle load capacity, and the size of the specific surface area passes through S BET Value to measure. Use the BET specific surface area tester F-Sorb2400 to measure the specific surface area of ordinary quartz sand and metal composite oxide modified sand, and calculate the ratio of the specific surface area of the modified sand to the specific surface area of ordinary quartz sand. The effect of sex. From Table 6, the specific surface area of metal oxide composite modified sand is 8.96 times that of ordinary quartz sand.
[0081] Table 6 BET specific surface area measurement results of filter sand
[0082]
[0083] 2. The physical picture of metal oxide composite modified sand figure 2 The metal oxide composite modified sand has a particle size range of 0.9mm to 1.4...
Example Embodiment
[0084] The SEM image of the metal oxide composite modified sand image 3 , Combining Table 6 and image 3 (a) The surface of ordinary quartz sand is flat, the specific surface area is small, and the adsorption capacity is small. image 3 (b) and (c) are SEM images of composite modified quartz sand surface magnified 5000 and 10000 times. It can be seen that the surface of metal oxide composite modified sand has very clear and dense pores with a specific surface area of 0.959, which is ordinary quartz 8.96 times that of sand, it has a larger adsorption capacity than ordinary quartz sand. The substance attached to the surface of the modified quartz sand is Fe 2 O 3 And CuO, making metal oxides successfully modified on the surface of ordinary quartz sand, Fe 3+ And Cu 2+ The positive charge on the surface of ordinary quartz sand is increased, which has a very good adsorption effect on negatively chargeable organic pollutants in water. Example 3 Removal of humic acid by static adso...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap