Filler-free skidproof resin paint and its preparation method and use

A resin coating, no filler technology, used in polyurea/polyurethane coatings, coatings, etc., can solve the problems of short non-slip life, high cost, poor adhesion, etc., and achieve transparency, soft elasticity, long service life, and strong adhesion. Effect

Active Publication Date: 2016-01-20
旭川新材料(广东)股份有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the low surface energy of silicone rubber and poor adhesion to plastics, it cannot be used in environments where the base material is plastic
Therefore, the exi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filler-free skidproof resin paint and its preparation method and use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Based on the total mass of the coating system 100wt%, 5wt% adhesion promoter Lanco-IntercoatVPP155 (Germany Lubrizol) is added to 35wt% solvent (by mass ratio, xylene: butyl acetate: ethyl acetate: diacetone alcohol = 1 :2:6:1), stirred at room temperature for 40min until fully dissolved, then added 50wt% epoxy modified polyether polyurethane resin elastic (M W =400g / mol, epoxy equivalent Ev=100g / eq), 1wt% leveling agent BYK333 (Germany BYK chemical), 1wt% wetting agent TEGOWET245 (Germany Digao), continue to stir for 30min, and add 3wt% catalyst ( Dibutyltin dilaurate (dibutyltin dilaurate, prepared as a toluene solution with a concentration of 10%)) was stirred evenly, and then 5 wt% curing agent HB100 (Basf, Germany) was added, and the anti-skid coating was obtained after stirring evenly. Transfer to the watering can, under the condition of 0.2~10MPa, the surface pretreatment (the surface treatment of the conventional substrate in this field includes: cleaning agent ...

Embodiment 2

[0038] Calculate with the total mass of the coating system 100wt%: 1wt% adhesion promoter Lanco-IntercoatVPP155 (Germany Lubrizol) is added to 35wt% solvent (by mass ratio, xylene: butyl acetate: ethyl acetate: diacetone alcohol=1 :2:6:1), stirred at room temperature for 40min to dissolve completely, then added 54wt% epoxy modified polyether polyurethane resin elastic (M W =400g / mol, epoxy equivalent Ev=100g / eq), 1wt% leveling agent BYK333 (Germany BYK chemical), 1wt% wetting agent TEGOWET245 (Germany Digao), continue to stir for 30min, and add 3wt% catalyst ( Dibutyltin dilaurate (dibutyltin dilaurate, prepared as a toluene solution with a concentration of 10%)) was stirred evenly, and then 6 wt% curing agent HB100 (Basf, Germany) was added, and the anti-skid coating was obtained after stirring evenly. Transfer to the watering can, under the condition of 0.2~10MPa, the surface pretreatment (the surface treatment of the conventional substrate in this field includes: cleaning a...

Embodiment 3

[0040] Calculating with 100wt% of the total mass of the coating system: add 9wt% adhesion promoter Lanco-IntercoatVPP155 (Germany Lubrizol) to 35wt% solvent (by mass ratio, xylene: butyl acetate: ethyl acetate: diacetone alcohol = 1 :2:6:1), stirred at room temperature for 40min until fully dissolved, then added 47wt% epoxy modified polyether polyurethane resin elastic (M W =400g / mol, epoxy equivalent Ev=100g / eq), 1wt% leveling agent BYK333 (Germany BYK chemical), 1wt% wetting agent TEGOWET245 (Germany Digao), continue to stir for 30min, and add 3wt% catalyst ( Dibutyltin dilaurate (dibutyltin dilaurate, prepared as 10% toluene solution) was stirred evenly, and then 4wt% curing agent HB100 (Germany BASF) was added and stirred evenly to obtain the anti-skid coating. Transfer to the watering can, under the condition that the air pressure of the spray gun is 0.2~10MPa, the surface treatment (the surface treatment of the conventional substrate in this field includes: cleaning agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Epoxy equivalentaaaaaaaaaa
Epoxy equivalentaaaaaaaaaa
Epoxy equivalentaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of skidproof resin paint and discloses filler-free skidproof resin paint and its preparation method and use in fields of catering industry, home life and automobile industry and especially in field of food and drink pallet skid resistance. The filler-free skidproof resin paint comprises, by mass, 20-70% of elastic resin, 1-15% of a curing agent, 10-70% of a solvent and 3-30% of an auxiliary agent. The elastic resin rich in high activity groups such as hydroxyl undergoes a reaction to produce a polymer with a special molecular structure so that adhesion of the elastic resin to a base is improved, mechanical properties are improved, soft and elastic characteristics are retained and impact strength and wear resistance are improved. The filler-free skidproof resin paint is free of a skidproof filler. The coating of the filler-free skidproof resin paint has thickness of 30-100 microns, a friction coefficient of 0.90, a skidproof angle of 45 degrees, good adhesion to a base, good flexibility and elasticity, water and oil resistance, ultraviolet radiation resistance and a long service life.

Description

technical field [0001] The invention belongs to the field of anti-slip resin coatings, and in particular relates to a sprayable non-slip anti-slip resin coating without fillers, a preparation method thereof and applications in the fields of catering, home life, automobile industry and the like, and is especially suitable for anti-slipping of catering trays. Background technique [0002] At present, most of the existing anti-skid coatings at home and abroad use epoxy resin or polyurethane as binder, and use quartz sand, corundum, metal inorganic salts, ordinary polyurethane particles or rubber particles as anti-skid fillers. This kind of anti-slip coating can achieve the anti-slip effect by adding anti-slip fillers to make the surface of the coating rough and increase the coefficient of friction. However, the filler has poor stability in the coating system, and the problem of filler settlement or swelling and delamination of rubber particles is prone to occur. Moreover, due t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/08C09D175/06C09D175/14C09D7/12
Inventor 郑辉张毅冲马文石罗熙雯杨建群
Owner 旭川新材料(广东)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap