Hydrophobic polymer cement waterproof coating and preparation method thereof

A waterproof coating and polymer technology, applied in the field of waterproof coatings, can solve the problems of waterproof, moisture-proof, anti-aging, pollution resistance and weather resistance, strong water absorption of the coating film, etc., to reduce water absorption, increase hydrophobicity, increase The effect of compactness

Inactive Publication Date: 2016-01-27
四川正大未来建筑科技有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of water-repellent polymer cement waterproof coating and its preparation method, aim to solve existing waterproof coating existing waterproof, moisture-proof, anti-aging, anti-pollution and weather resistance are relatively poor, coating film water absorption stronger question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic polymer cement waterproof coating and preparation method thereof
  • Hydrophobic polymer cement waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] In order to make the objectives, technical solutions and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with embodiments. It should be understood that the specific embodiments described herein are only used to explain the present invention, but not to limit the present invention.

[0018] The present invention uses styrene-butyl methacrylate copolymer emulsion as the main film-forming material, cement and quartz stone as the secondary film-forming material, and is equipped with defoamer, film-forming aid, plasticizer, leveling agent, Anti-corrosion and anti-fungal agent and other auxiliary film-forming substances, using sodium methyl silicate as the hydrophobic functional auxiliary, a two-component water-based hydrophobic architectural waterproof coating made by a reasonable ratio, and its performance is organic and inorganic Compound waterproof material.

[0019] The application principle of the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hydrophobic polymer cement waterproof coating and a preparation method thereof. The hydrophobic polymer cement waterproof coating is prepared from, by weight, 433 parts of polymer emulsion, 5 parts of plasticizer, 5 parts of defoaming agents, 1.6 parts of thickener PRM-300, 0.8 part of multifunctional additive, 4 parts of methyl sodium silicate, 266 parts of 42.5 Portland cement, 145 parts of 8# quartz sand and 145 parts of 10# quartz sand. After curing and film forming, the coating film has the waterproof and hydrophobic actual effects at the same time, and has the good capillary crystalline performance, the reverse capillary effect is achieved, the excellent hydrophobic layer is formed, and meanwhile the minimum inflation function and compactness increasing function are achieved; the methyl sodium silicate is added as a hydrophobic agent, and due to the fact that the methyl belongs to hydrophobic groups, the hydrophobicity of waterproof coating is increased after film formation, the compactness of the coating is increased, the waterproof, dampproof, anti-aging and anti-fouling performance and weather resistance of the waterproof coating film are improved, and the hydroscopicity of the coating film is lowered.

Description

Technical field [0001] The invention belongs to the technical field of waterproof coatings, and in particular relates to a hydrophobic polymer cement waterproof coating and a preparation method thereof. Background technique [0002] There are two types of waterproof materials on the market: one is polyurethane waterproof coatings. Such materials are generally made of polyurethane and coal tar as raw materials. Its volatile tar gas is very toxic and difficult to remove, so it was banned in China in 2000. The polyurethane waterproof coating that is still on sale uses bitumen instead of coal tar as a raw material. However, when using this kind of paint, it is generally diluted with organic solvents such as toluene and xylene, which also contains toxicity; the other type is polymer cement-based waterproof paint. It is composed of a variety of water-based polymer emulsions and high-quality cement mixed with various additives. The flexibility of the polymer (resin) and the rigidity ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/42C04B103/65C04B111/27
Inventor 王友顺冯先勇聂绍贵
Owner 四川正大未来建筑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap