Abrasion-resisting raw lacquer coating for concentration table and preparation method thereof

Abstract

The invention discloses an abrasion-resisting raw lacquer coating for a concentration table and a preparation method thereof. The abrasion-resisting raw lacquer coating is prepared from, by mass, 60%-75% of raw lacquer, 10%-18% of plant microcrystalline cellulose, 8%-15% of modifying agent, 1%-7% of dispersing agent, 5%-8% of diluent, 2%-5% of functional aids and 0.5%-1.5% of coupling agent. According to the brasion-resisting raw lacquer coating for the concentration table and the preparation method thereof, the plant microcrystalline cellulose, the raw lacquer and other auxiliaries are reasonably compounded, so that the defect that the construction condition requirement of the raw lacquer is high and thus a specific temperature and humidity environment is needed is overcome, the raw lacquer coating cannot be affected by the temperature and humidity and can be cured under the low-temperature and low-humidity conditions, normal temperature construction is achieved, the construction period of the raw lacquer can be shortened, and the production cost of the raw lacquer is reduced; moreover, the advantages that the raw lacquer is good in abrasion resistance and moderate in friction force are reserved. Verification proves that the abrasion-resisting raw lacquer coating has excellent corrosion resistance, and is good in acid resistance, water resistance and medium resistance.

Description

technical field [0001] The invention belongs to the technical field of wear-resistant coatings. More specifically, it relates to a wear-resistant raw lacquer coating for a mineral dressing shaker and a preparation method thereof. Background technique [0002] The beneficiation shaking table is used as a gravity separation equipment, which has been widely used in the separation of placer gold and other minerals, mainly for gold or coal preparation. The beneficiation shaking table can make the ore particles move in different directions according to their density and particle size, and fan out from the ore feeder along the diagonal, and then discharge along the edge of the bed in sequence. The ore discharge line is very long, which can accurately produce A variety of products with different qualities are produced, such as concentrate, sub-concentrate, medium concentrate and tailings. The surface performance of the shaker, especially the wear resistance, is one of the most imp...

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defects and deficiencies of existing raw lacquers that are greatly affected by temperature and humidity, dry slowly under low temperature and low humidity conditions, and need to be constructed under constant temperature and humidity conditions, and provide a kind of lacquer that is not affected by temperature and humidity. The wear-resistant raw lacquer coating applied under low temperature and low humidity conditions overcomes the defects that raw lacquer construction conditions are high and requires a specific temperature and humidity environment. It can be dried and solidified at room temperature, which can shorten the construction period of raw lacquer and reduce production costs. The advantages of raw lacquer wear resistance and moderate friction