Preparation method of N-polyvinylcaprolactam solution taken as kinetic hydrate inhibitor

A technology for vinyl caprolactam and hydrate inhibitor, which is applied in the field of preparation of poly-N-vinyl caprolactam solution, can solve the problems of increased production cost, increased solvent consumption, complicated process, etc., and achieves improved production efficiency and improved compounding performance, the effect of reducing environmental pollution

Inactive Publication Date: 2016-03-30
GANSU RES INSTION OF CHEM IND GRICI
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large concentration at the end of the synthetic polymer reaction of this method, the viscosity of the reaction system increases, and post-treatment operations such as dissolution, precipitation, and purification are

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] Weigh 300g of N-vinylcaprolactam, measure 500ml of methanol, add to a 1000ml three-necked flask, pass nitrogen protection, stir and heat to dissolve, dissolve 0.6g of azobisisopropylimidazoline hydrochloride in 100ml of methanol, Add dropwise to a three-necked flask, raise the temperature to 65° C., stir and react for 6 hours; lower the temperature to 30° C., add 400 ml of methanol, and stir for about 0.5 hours to obtain a poly-N-vinyl caprolactam methanol solution.

[0016] Tests by the high-pressure method show that the polymer solution has a good inhibitory effect on natural gas hydrate, and the inhibition time is about 18.8 hours.

Example Embodiment

[0017] Example 2

[0018] Weigh 300g of N-vinylcaprolactam, measure 500ml of methanol, add to a 2000ml three-necked flask, pass nitrogen protection, stir and heat to dissolve, dissolve 0.6g azobisisopropylimidazoline hydrochloride in 100ml methanol, Dropped into a three-necked flask, heated to 65°C, stirred for 6h; cooled to 30°C, added 600ml methanol and stirred for about 0.5h to obtain a methanol solution of poly-N-vinylcaprolactam.

[0019] The high-pressure test shows that the polymer solution has a good inhibitory effect on natural gas hydrate, and the inhibition time is about 18.5 hours.

Example Embodiment

[0020] Example 3

[0021] Weigh 300g of N-vinylcaprolactam, measure 500ml of methanol, add to a 2000ml three-necked flask, pass nitrogen protection, stir and heat to dissolve, dissolve 0.6g azobisisopropylimidazoline hydrochloride in 100ml methanol, Dropped into a three-necked flask, heated to 65°C, stirred for 6h; cooled to 30°C, added 800ml methanol and stirred for about 0.5h to obtain a poly-N-vinylcaprolactam methanol solution.

[0022] Tests by the high-pressure method show that the polymer solution has a good inhibitory effect on natural gas hydrate, and the inhibition time is about 18.3 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of an N-polyvinylcaprolactam solution taken as a kinetic hydrate inhibitor. According to the invention, N-vinylcaprolactam is taken as a monomer, azo diisopropyl imidazoline hydrochloride is taken as an initiating agent, polyvinylcaprolactam is obtained via solution polymerization, methyl alcohol or ethanediol is taken as a solvent, and reaction is carried out for 2 to 12h at 55 to 85 DEG C with stirring; an obtained product is cooled to 30 to 45 DEG C, the solvent is added for uniform stirring so as to obtain the N-polyvinylcaprolactam solution. The finished product is a solution, so that post-treatment operation such as dissolving, precipitating, and purifying are avoided, post-treatment technology is simplified, production period is shortened, production efficiency is increased, and production cost is reduced; and at the same time application of toxic solvent is avoided, and environment pollution is reduced. Inhibition performance of hydrates is not influenced by the N-polyvinylcaprolactam solution, N-polyvinylcaprolactam compounding performance is improved, a plurality of solution forms can be prepared based on market requirements, and industrial application prospect is promising.

Description

technical field [0001] The invention belongs to the field of organic synthesis chemistry, and relates to a preparation method of a poly-N-vinyl caprolactam solution used as a kinetic hydrate inhibitor. Background technique [0002] Gas hydrates form crystals with a cage-like structure similar to dry ice, often causing blockages in pipes, valves and equipment. The traditional method of inhibiting hydrate is to use thermodynamic method, that is, inject methanol, ethylene glycol and other alcohols or add electrolytes to change the thermodynamic equilibrium conditions of hydrate to control the formation of hydrate. However, the large amount of inhibitor used, high cost, high toxicity and difficult to recycle will cause serious environmental pollution. [0003] Poly-N-vinylcaprolactam (PNVCL) is a temperature-sensitive (thermo-sensitive) polymer with a low critical solution temperature (LCST), which has the advantages of good biocompatibility and low biotoxicity. It has been wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F126/06C08F2/06
CPCC08F126/06C08F2/06
Inventor 耿来红徐世栋潘炳庆刘茵
Owner GANSU RES INSTION OF CHEM IND GRICI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap