An environmentally friendly flooring technology, applied in the field of waterproof and environmentally friendly flooring, can solve the problems of unusable covering materials, low compressive strength, easy aging, etc., achieve good thermal insulation function, improve compressive strength, and strong impact resistance Effect
Inactive Publication Date: 2016-04-27
王威淞
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The waterproof material used for construction in the prior art cannot adapt to changes in climate and temperature. It becomes soft in summer and becomes brittle in winter, which is prone to cracks and causes water leakage; it is easy to age
Moreover, it is harmful to human health and the environment, high comprehensive cost, low cost performance, short service life, and weak adhesion
The compressive strength of building materials is relatively low, so it cannot be used for load-bearing walls, nor can it be used for building exterior surface covering materials
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] A kind of waterproof environment-friendly floor, it is characterized in that, each component of raw material is composed as follows according to weight part:
[0017] 50 parts of waste plastics, 12 parts of crushed plants, 3 parts of oxidized premix, 10 parts of wood powder, 3 parts of diatomaceous earth, 15 parts of peat, 8 parts of filler, 4 parts of methacrylate, 2 parts of cellulose acetate, 4 parts of interface modifier, 2 parts of magnesium oxide powder, 3 parts of bamboo fiber, 3 parts of stearic acid, 0.3 parts of ferrous sulfate, 3 parts of adhesive;
[0018] The oxidation premix is a mixture of aluminum hydroxide, red clay and iron oxide slag in a weight ratio of 1:1:2.
[0019] Further, the crushed plant is a mixture of hay and corn stalks in a weight ratio of 2:3.
[0020] Further, the filler is a mixture of oil shale, fly ash and perlite in a weight ratio of 2:3:3.
[0021] Further, the interface modifier is a mixture of magnesium silicate and kaolin wi...
Embodiment 2
[0023] A kind of waterproof environment-friendly floor, it is characterized in that, each component of raw material is composed as follows according to weight part:
[0024] 50 parts of waste plastics, 15 parts of crushed plants, 5 parts of oxidized premix, 15 parts of wood powder, 5 parts of diatomaceous earth, 20 parts of peat, 12 parts of filler, 6 parts of methacrylate, 4 parts of cellulose acetate, 5 parts of interface modifier, 4 parts of magnesium oxide powder, 4 parts of bamboo fiber, 4 parts of stearic acid, 0.5 part of ferrous sulfate, 6 parts of adhesive;
[0025] The oxidation premix is a mixture of aluminum hydroxide, red clay and iron oxide slag in a weight ratio of 1:1:2.
[0026] Further, the crushed plant is a mixture of hay and corn stalks in a weight ratio of 2:3.
[0027] Further, the filler is a mixture of oil shale, fly ash and perlite in a weight ratio of 2:3:3.
[0028] Further, the interface modifier is a mixture of magnesium silicate and kaolin wi...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a waterproof environment-friendly floor comprising the following raw material components in parts by weight: 50 parts of waste plastics, 12-15 parts of a plant crushed material, 3-5 parts of an oxidized premixed material, 10-15 parts of a wood chip powder, 3-5 parts of diatomite, 15-20 parts of peat, 8-12 parts of a packing, 4-6 parts of metacrylic acid ester, 2-4 parts of cellulose acetate, 4-5 parts of an interface modifier, 2-4 parts of a magnesium oxide powder, 3-4 parts of a bamboo fiber, 3-4 parts of stearic acid, 0.3-0.5 part of ferrous sulfate, and 3-6 parts of an adhesive. With utilization of the waste plastics, the wastes are utilized and turned into treasure, and the purposes of energy saving and environmental protection are achieved. The oxidized premixed material and the plant crushed material are in synergistic effect, so that the compressive strength and toughness of the material can be improved, and the obtained material is not easy to age and has the waterproof, fireproof and sound insulation functions; the interfacial modification agent can adapt to changes in weather temperatures, so that cracks are not easily produced, water leakage is not caused, and the floor has strong acid and alkali resistance, strong impact resistant ability, and good heat-preservation heat-insulation functions.
Description
technical field [0001] The invention belongs to the technical field of indoor material production, and in particular relates to a waterproof and environment-friendly floor. Background technique [0002] There are many classifications of floors, classified by structure: natural landscape Fengshui floor, solid wood floor, reinforced composite wood floor, solid wood composite floor, bamboo wood floor, cork floor, etc.; classified by use: floor for household occasions, floor for commercial occasions, Anti-static floor, outdoor floor, special floor for stage dance, special floor for sports hall, special floor for track and field, etc.; classified by environmental protection level: E1 grade floor, E0 grade floor, JAS star standard F4 star floor, etc. In the Chinese market, there are some special geothermal floors. In fact, as long as the base material is stable, no cracking, no deformation, high environmental performance, heat preservation and heat conduction, even pure solid wood...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more