Preparation method of a novel oxidized cellulose hemostatic product

A technology for oxidizing cellulose and cellulose, which is applied in the fields of pharmaceutical formulation, application, and medical science, and can solve problems such as harmfulness to the human body and the environment, and achieve the effects of strong liquid absorption, improved product performance, and reduced oxidation side reactions

Active Publication Date: 2018-08-21
ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the general sponge is composed of polystyrene, polyurethane and other substances, which are harmful to the human body and the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Wood fiber is used as raw material, and the fiber fineness is 0.5 denier.

[0039] 1. The cellulose fibers are pretreated with a 1% sodium hydroxide solution, and after removing possible impurities, the surface of the fibers is further activated with an alkali solution.

[0040] 2. After pretreatment and activation, wash with deionized water until neutral, and air-dry the obtained cellulose product to obtain raw materials.

[0041] 3. Use 5% sodium hydroxide solution as a solvent, the dosage of cellulose product is 3% (in sodium hydroxide solution), then add 2% urea (in sodium hydroxide solution) and 2% ZnO ( (calculated as sodium hydroxide solution), fully dissolved at -15°C, and the system becomes viscose.

[0042] 4. After the fiber is completely dissolved in the solution and becomes viscose, slowly add the pore-forming agent sodium sulfate, and continue to stir for 20 minutes to make it a mixture of cellulose.

[0043] 5. Pour the cellulose mixture into the mold f...

Embodiment 2

[0055] Viscose fiber is used as raw material, and the fiber fineness is 1.0 denier.

[0056] 1. Pretreat the cellulose fibers with a 3% sodium hydroxide solution to remove impurities on the surface of the fibers, and then activate the surface of the fibers with an alkali solution.

[0057] 2. After pretreatment and activation, wash with deionized water until neutral, and air-dry the obtained cellulose product to obtain raw materials.

[0058] 3. Use 10% sodium hydroxide solution as a solvent, and the dosage of cellulose product is 5% (in sodium hydroxide solution), then add 2% urea (in sodium hydroxide solution) and 2% ZnO ( Calculated as sodium hydroxide solution), fully dissolved at -5°C, the system becomes viscose.

[0059] 4. After the fiber is completely dissolved in the solution and becomes viscose, slowly add the pore-forming agent sodium sulfate, and continue to stir for 20 minutes to make it a mixture of cellulose.

[0060] 5. Pour the cellulose mixture into the mol...

Embodiment 3

[0072] Cotton fiber is used as raw material, and the fiber fineness is 3.0 denier.

[0073] 1. Pretreat the cellulose fibers with a 5% sodium hydroxide solution, remove impurities on the surface of the fibers, and then activate the surface of the fibers with an alkali solution.

[0074] 2. After pretreatment and activation, wash with deionized water until neutral, and air-dry the obtained cellulose product to obtain raw materials.

[0075] 3. Use 20% sodium hydroxide solution as a solvent, the amount of cellulose product is 10% (in sodium hydroxide solution), then add 2% urea (in sodium hydroxide solution) and 2% ZnO ( (calculated as sodium hydroxide solution), fully dissolved at 5°C, and the system becomes viscose.

[0076] 4. After the fiber is completely dissolved in the solution and becomes viscose, slowly add the pore-forming agent sodium sulfate, and continue to stir for 20 minutes to make it a mixture of cellulose.

[0077] 5. Pour the cellulose mixture into the mold ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to View More

Abstract

Disclosed is a method for preparing an oxidized cellulose hemostatic product, including using a sodium hydroxide solution with the concentration of 1 to 5% to pre-process a cellulose product; after removing lignins or impurities on the fiber surface, using an alkaline solution to activate the fiber surface further; after the activating treatment, using demin-water for washing until it is neutral and drying the obtained cellulose product in air to obtain a raw material; using a sodium hydroxide solution with the concentration of 5 to 20% as a solvent; adding the cellulose product, carbamide and ZnO that are 3 to 10%, 2% and 2% of the sodium hydroxide solution respectively.

Description

technical field [0001] The invention relates to the field of cellulose hemostatic products, in particular to a preparation method of a novel oxidized cellulose hemostatic product (hemostatic sponge). Background technique [0002] Cellulose is a macromolecular polysaccharide composed of glucose. Insoluble in water and general organic solvents. It is the main component of plant cell walls. Cellulose is the most widely distributed and most abundant polysaccharide in nature, accounting for more than 50% of the carbon content in the plant kingdom. The cellulose content of cotton is close to 100%, which is the purest natural cellulose source. . Cellulose is a natural polymer compound formed by linking D-glucopyranose. [0003] Oxidized cellulose and oxidized regenerated cellulose, due to their good biocompatibility and degradability, can be used as hemostatic gauze products in the medical field. After the oxidized cellulose is made into medical gauze, its carboxyl group can cr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L24/08
CPCA61L24/0036A61L24/08A61L2400/04C08B15/04C08L1/04
Inventor 张治国索艳格黄伟孙伟庆
Owner ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com