A kind of water-based inorganic negative ion paint and preparation method thereof

A negative ion coating, inorganic technology, applied in the direction of alkali metal silicate coatings, coatings, etc., can solve the problems of poor storage stability, high radiation, poor water resistance, etc. The effect of poor water resistance

Active Publication Date: 2018-05-11
四川弘达瑞涂料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention adopts special mica as anion-generating material, uses zinc oxide and organosilicon polymerized solution-modified sodium silicate as a film-forming curing binder and adds pigments and fillers to produce a non-toxic, tasteless, high-anion-generating, strong adhesion, Inorganic anion coatings with multiple functions such as fire retardant, scrub resistance, abrasion resistance, weather resistance, acid and alkali resistance, etc., overcome the shortcomings of traditional anion coatings with high radiation, and also overcome the two-component traditional inorganic coatings that require curing agents. The shortcomings of easy cracking, poor water resistance and poor storage stability have the functions of negative ion coatings and inorganic coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A water-based inorganic anion coating, in parts by weight, including the following main components: 15 parts of water, 0.1 parts of wetting agent, 0.5 parts of dispersant, 0.5 parts of defoamer, 2 parts of film-forming aids, 0.5 parts of antifreeze, 0.8 parts of thickener, 22 sodium silicate solution, 0.6 parts of inorganic dispersant, 25 parts of pigments and fillers, 15 parts of special mica powder, 2 parts of zinc oxide, 16 parts of silicone polymer solution .

[0035] A preparation method of water-based inorganic anion coating, including the following steps:

[0036] (1) In parts by weight, sequentially add water, wetting agent, dispersant, 60% defoamer, film forming aid, antifreeze, 25% thickener, sodium silicate solution, inorganic dispersant to the mixer Stir, the stirring speed is 300 rpm, the stirring time is 15 minutes;

[0037] (2) Adjust the stirring speed to 1500 rpm, add pigments and fillers, and stir for 15 minutes;

[0038] (3) Continue to add special mica pow...

Embodiment 2

[0049] A water-based inorganic anion coating, in parts by weight, including the following main components: 18 parts of water, 0.1 parts of wetting agent, 0.5 parts of dispersant, 0.5 parts of defoamer, 2 parts of film-forming aids, 0.5 parts of antifreeze, 0.8 parts of thickener, 20 parts of sodium silicate solution, 0.25 parts of inorganic dispersant, 20 parts of pigments and fillers, 25 parts of special mica powder, 2 parts of zinc oxide, 20 parts of organic silicon polymer solution .

[0050] A preparation method of water-based inorganic anion coating, including the following steps:

[0051] (1) In parts by weight, add water, wetting agent, dispersant, 60% defoaming agent, film forming aid, antifreeze, 25% thickener, sodium silicate solution, inorganic Stir the dispersant, the stirring speed is 350 rpm, and the stirring time is 18 minutes;

[0052] (2) Adjust the stirring speed to 1500 rpm, add pigments and fillers, and stir for 15 minutes;

[0053] (3) Continue to add special mi...

Embodiment 3

[0064] A water-based inorganic anion coating, in parts by weight, including the following main ingredients: 20 parts of water, 0.1 parts of wetting agent, 0.5 parts of dispersant, 0.5 parts of defoaming agent, 1 part of film forming aid, 0.5 parts of antifreeze, 0.8 parts of thickener, 22 sodium silicate solution, 0.6 parts of inorganic dispersant, 20 parts of pigments and fillers, 15 parts of special mica powder, 1.5 parts of zinc oxide, 20 parts of organic silicon polymer solution .

[0065] A preparation method of water-based inorganic anion coating, including the following steps:

[0066] (1) In parts by weight, add water, wetting agent, dispersant, 60% defoaming agent, film forming aid, antifreeze, 25% thickener, sodium silicate solution, inorganic The dispersant is stirred, the stirring speed is 300 rpm, and the stirring time is 15 minutes;

[0067] (2) Adjust the stirring speed to 1500 rpm, add pigments and fillers, and stir for 20 minutes;

[0068] (3) Continue to add specia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides an inorganic negative ion coating and a preparation method thereof. Special mica powder is added to a coating formula, so that the aims of releasing negative ions and not generating radiological hazards are achieved. Meanwhile, a sodium silicate solution is modified through zinc oxide and an organic silicon solution, so that a coating film has super-strong adhesion and hardness, fireproof and flame-retardant properties, water resistance, stability and high temperature resistance. The obtained coating does not contain an organic solvent or other toxic or harmful substance and is an environment-friendly product.

Description

Technical field [0001] The invention relates to inorganic coatings, belonging to the field of high molecular polymers, and in particular to inorganic negative ion coatings and a preparation method thereof. Background technique [0002] Negative ion coatings improve the living environment due to the characteristics of anion generation, and are favored by people, especially in cities with severe air pollution. People with strong health and environmental awareness are the first choice for decoration. In addition, the advantages of inorganic coatings such as high hardness, weather resistance, stain resistance, air permeability, fire resistance, flame retardancy, mildew resistance, and insecticide are favored by consumers. The raw materials used are rich in sources and low in price, so it has a broad market prospect. [0003] Water-based inorganic coatings are mainly silicates, which can be divided into potassium silicate, lithium silicate, sodium silicate and silica sol according to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/04C09D7/61
CPCC09D1/04C09D7/61C09D7/65
Inventor 陈威
Owner 四川弘达瑞涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com