A method for preparing high specific capacity shuttle-shaped copper oxide electrode material

A copper oxide, shuttle-like technology, used in hybrid capacitor electrodes, copper oxide/copper hydroxide, nanotechnology, etc., can solve the problems of limited use, high cost, toxicity, etc., and achieve narrow particle size distribution, broad application prospects, Responsive and efficient effect

Active Publication Date: 2017-07-28
CENT SOUTH UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ruthenium oxide has been extensively studied for active electrode applications due to its high theoretical capacity (approximately 2000F G -1 ) around 1.4V in the potential window, but their usefulness is limited due to the high integer cost and toxic nature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing high specific capacity shuttle-shaped copper oxide electrode material
  • A method for preparing high specific capacity shuttle-shaped copper oxide electrode material
  • A method for preparing high specific capacity shuttle-shaped copper oxide electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] First need to weigh 1mmol CuCl 2 , into a 50mL beaker, then add 40mL deionized water, stir, then add 1mmol Na 2 CO 3 and 1mL of triethylamine solution, stirred for 10 minutes, then ultrasonicated for 5 minutes, and then directly put into the microwave oven, set the power to 300W, and the time was 20 minutes, and washed several times with deionized water and absolute ethanol, and then in Dry in an oven at 60°C for 6 hours to obtain a copper oxide nanoshuttle sample. Such as figure 1 Shown product is identified as copper oxide through X-ray powder diffraction; Carry out morphology analysis to copper oxide with scanning electron microscope (SEM), from figure 2 It can be seen that its morphology is nanoshuttle. Excellent electrochemical cycle performance and specific capacitance can be obtained from image 3 see.

Embodiment 2

[0037] First need to weigh 1mmol CuCl 2 , into a 50mL beaker, then add 40mL deionized water, stir, then add 1mmol Na 2 CO 3 and 1mL of triethylamine solution, stirred for 10 minutes, then ultrasonicated for 5 minutes, and then directly put into the microwave oven, set the power to 200W, and the time was 20 minutes, and washed several times with deionized water and absolute ethanol, and then in Dry in an oven at 60°C for 6 hours to obtain a copper oxide nanoshuttle sample. The morphology of copper oxide was analyzed by transmission electron microscopy (TEM). Figure 4 It can be seen that its morphology is nanoshuttle.

Embodiment 3

[0039] First need to weigh 1mmol CuCl 2 , into a 50mL beaker, then add 40mL deionized water, stir, then add 1mmol Na 2 CO 3 and 1mL of triethylamine solution, stirred for 10 minutes, then ultrasonicated for 5 minutes, and then directly put into the microwave oven, set the power to 400W, and the time was 20 minutes, and washed several times with deionized water and absolute ethanol, and then in Dry in an oven at 60°C for 6 hours to obtain a copper oxide nanoshuttle sample. The morphology of copper oxide was analyzed by transmission electron microscopy (TEM). Figure 5 It can be seen that its morphology is nanoshuttle.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a high specific capacity shuttle-shaped copper oxide electrode material. The method is to add soluble carbonate and triethylamine into the copper salt solution, ultrasonically disperse it, and then process it with microwaves to obtain a special shuttle electrode material. Copper oxide nanoparticles with similar morphology, the method is efficient, simple, easy to operate, and meets the requirements of industrial production; the prepared shuttle-shaped copper oxide nanoparticles have the characteristics of high purity, uniform particle size, and excellent electrochemical performance. The field of capacitor electrode materials has broad application prospects.

Description

technical field [0001] The invention relates to a method for preparing a high specific capacity shuttle-shaped copper oxide electrode material, which belongs to the field of metal oxide nanometer material preparation. Background technique [0002] With the rapid development of the global economy, the depletion of fossil fuels and increasing environmental pollution, there is an urgent need for efficient, clean and sustainable energy sources, as well as new technologies related to energy conversion and storage. Therefore, supercapacitors (also known as electrochemical capacitors) are characterized by high power, faster response time and a near-infinite life cycle with reasonable energy density, which is the advantage of both traditional dielectric capacitance and energy storage batteries. electrical energy storage device. The current development direction of supercapacitors should focus on the use of environmentally friendly materials, increased power and energy density, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01G3/02B82Y40/00H01G11/46
CPCY02E60/13
Inventor 刘小鹤刘涛马仁志邱冠周
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap