High-performance forward permeable membrane and electrostatic spinning preparation method thereof

A forward osmosis membrane, high-performance technology, applied in the field of membrane separation, can solve the problems of unsatisfactory salt cutoff rate of forward osmosis membrane, complex hydrophilic and hydrophobic interpenetrating nanofiber method, etc., to achieve hydrophilic improvement, increase water flux and The effect of salt cutoff and simple preparation process

Inactive Publication Date: 2016-07-06
INST OF URBAN ENVIRONMENT CHINESE ACAD OF SCI
View PDF4 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent CN103768959A introduces a forward osmosis membrane supported by hydrophilic-hydrophobic intertransfer network nanofibers. Researchers hope to improve the hydrophilicity of the membrane by interspersing hydrophilic nanofibers in hydrophobic nanofibers and re...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance forward permeable membrane and electrostatic spinning preparation method thereof
  • High-performance forward permeable membrane and electrostatic spinning preparation method thereof
  • High-performance forward permeable membrane and electrostatic spinning preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Dissolve 0.05g carbon nanotubes in a mixed solvent of 10g N-N dimethylformamide (DMF) and NN dimethylacetamide (DMAc) (DMF: DMAc=1:1), and configure a carbon concentration of 0.5% Nanotube solution: Dissolve 1g of polyacrylonitrile (PAN) in the above mixed solution and stir evenly to prepare a spinning solution with a concentration of 10%. The carbon nanotube / PAN solution was added to the syringe, the flow rate of the syringe was adjusted to 1.2 mL / h, and the distance between the syringe and the receiving device was 15 cm, and the nanofibers were prepared by spinning under 15 kV high voltage electrostatic. The obtained composite fiber membrane is dried in an oven at 60° C. for 12 hours, and the dried composite fiber membrane is laminated through a laminator to obtain a compacted composite fiber membrane.

[0028] Take the above-mentioned compacted composite fiber membrane as a support layer, soak it in a 3% m-phenylenediamine (MPD) aqueous solution for 2 minutes, take ...

Embodiment 2

[0033] Dissolve 0.35g carbon nanotubes in a mixed solvent of 10g N-N dimethylformamide (DMF) and NN dimethylacetamide (DMAc) (DMF: DMAc=3:1), and configure a carbon concentration of 3.5% Nanotube solution: Dissolve 1.5g of polyacrylonitrile (PAN) in the above mixed solution and stir evenly to prepare a spinning solution with a concentration of 15%. The carbon nanotube / PAN solution was added to the spinning jet head, the flow rate of the spinning jet head was adjusted to 1.5 mL / h, the spinning jet head was 20 cm away from the receiving device, and the nanofibers were prepared by spinning under 25kV high voltage electrostatic. The obtained composite fiber membrane is placed in an oven at 70° C. and dried for 8 hours, and the dried composite fiber membrane is laminated through a laminator to obtain a compacted composite fiber membrane.

[0034] Take the above-mentioned compacted composite fiber membrane as a supporting layer, soak it in a 1% o-phenylenediamine aqueous solution f...

Embodiment 3

[0037] Dissolve 0.5 g of carbon nanotubes in 10 g of tetrahydrofuran to prepare a 5% carbon nanotube solution; dissolve 1.2 g of a mixture of polyacrylonitrile and polyvinyl alcohol (mass ratio 1:1) in the above mixed solution, Stir evenly to obtain a spinning solution with a concentration of 12%. Add the carbon nanotube / (PAN+PVA) solution into the spinning jet head, adjust the flow rate of the spinning jet head to 1mL / h, the spinning jet head is 10cm away from the receiving device, and spin it under 20kV high voltage electrostatic. fiber. The obtained composite fiber membrane is placed in an oven at 70° C. and dried for 8 hours, and the dried composite fiber membrane is laminated through a laminator to obtain a compact composite fiber membrane.

[0038] Take the above-mentioned compacted composite fiber membrane as a supporting layer, soak it in a 5% bisphenol aqueous solution for 3.5 minutes, take it out, remove the excess solution on the surface, and then place it in 5% i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Water contact angleaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of membranes, and discloses a high-performance forward permeable membrane and an electrostatic spinning preparation method thereof. The method comprises the steps that a hydrophilic nano material and a hydrophilic macromolecular polymer are mixed and dissolved, an electrostatic spinning technique is adopted for preparing a composite nanofiber membrane; then the laminated composite nanofiber membrane is adopted as a supporting layer, an interfacial polymerization technology is utilized for synthesizing a dense skin layer on the surface of the supporting layer, and the forward permeable membrane supported by the nanofiber membrane is prepared. The prepared forward permeable membrane is high in water flux and salt rejection, and internal concentration polarization can be effectively relieved through the support-shaped structure and communicated pores of the forward permeable membrane.

Description

Technical field [0001] The invention belongs to the technical field of membrane separation, and specifically relates to a high-performance forward osmosis membrane and an electrostatic spinning preparation method thereof. Background technique [0002] Forward osmosis (FO) is a concentration-driven membrane separation technology. Its main feature is that the process driving force is osmotic pressure, low energy consumption, and good economic benefits. Compared with the traditional pressure-driven membrane separation technology, such as reverse osmosis, nanofiltration and microfiltration, the forward osmosis process also has the advantages of lighter membrane pollution, simple membrane process and equipment. At present, forward osmosis technology has been applied in the fields of energy, seawater desalination, pharmaceutical industry, wastewater treatment and food processing. As forward osmosis has attracted more and more attention, the preparation method of forward osmosis membra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D71/06B01D69/10B01D69/12B01D67/00B01D61/00C02F1/44
CPCY02A20/131B01D71/06B01D61/002B01D67/0002B01D69/105B01D69/12B01D2323/02B01D2323/39B01D2325/36C02F1/445
Inventor 郑煜铭潘淑芳钟鹭斌
Owner INST OF URBAN ENVIRONMENT CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap