Rubber composition and application thereof

A technology of rubber composition and styrene-butadiene rubber, which is applied in the direction of building structure, building components, building insulation materials, etc., can solve the problems of poor flex fatigue resistance, poor processing safety, poor processing stability, etc., and achieve physical and mechanical properties Good, long-term stable performance, high cross-linking vulcanization efficiency

Active Publication Date: 2016-07-20
NANJING SIKAI RUBBER & PLASTIC PROD CO LTD
View PDF9 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is poor flex fatigue resistance and prone to blooming
Although the effective vulcanization system formula with high TMTD is widely used, it has poor processing stability and serious frosting
(3) Dynamic equilibrium vulcanization system, usually a vulcanization system with anti-vulcanization reduction performance, the dynamic performance is better than that of effective and semi-effective vulcanization system, but it cannot reach the dynamic performance of conventional vulcanization system
[0021] In the manufacture of heavy and thick products that require fatigue resistance, such as tires and track plates, a compounding system with sulfur is usually required. Although the compounding system with sulfur has good fatigue resistance and tear resistance, it has poor heat and aging resistance and poor processing safety. The anti-scorch agent CTP and p-phenylenediamine anti-aging agent in the formula are almost standard, and these materials are harmful or suspected harmful substances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber composition and application thereof
  • Rubber composition and application thereof
  • Rubber composition and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0094] General application of the present invention: butadiene rubber, natural rubber and styrene-butadiene rubber account for more than 70-85% of the rubber (raw rubber) weight, 100% is certainly more possible, and other ingredients are generally polymer materials containing ethylenic bonds; other ingredients Such as a small amount of binary or EPDM rubber, polypropylene, maleic anhydride binary or EPDM rubber (EPDM is a copolymer of ethylene, propylene or / and a small amount of non-conjugated diene, or other olefin low Polymer), does not exclude the use of other recycled rubber, secondary rubber powder (which can also be included in the filler system), etc.

[0095] The peroxide initiator is (1) di-tert-butyl peroxide, benzoyl peroxide, lauroyl peroxide; (2) hydroperoxide (cumene hydroperoxide, tert-butyl hydroperoxide); (3) Dialkyl peroxide (di-tert-butyl peroxide, dicumyl peroxide); (4) tert-butyl peroxybenzoate, tert-butyl peroxy-tert-valerate; (5) peroxide Oxidized methy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a rubber composition. The rubber composition is prepared from the ingredients in parts by mass: 80-120 parts of crude rubber, 1-5 parts of peroxide initiator, 2-15 parts of bridging agent, 0.1-1 part of free-radical absorption and release regulator and reinforcing and anti-aging agents, wherein the crude rubber comprises any one to any three of polybutadiene rubber, natural rubber and styrene-butadiene rubber and accounts for 70 percent or more of mass of the crude rubber. According to the rubber composition and the application thereof, a formula of the rubber composition and adjuvants for product cross-linking and the like is provided, so that the requirements of a technical scheme for representatives, i.e., tires, shoe materials and wear resisting plates on good properties and good industrial adaptability effect can be met; cost and environmentally-friendliness can be taken into account simultaneously.

Description

1. Technical field [0001] The invention relates to a rubber composition, that is, a crosslinking formulation of a rubber product, as well as a preparation method and application. 2. Background technology [0002] Butadiene rubber (China's output has a million tons) and natural rubber and styrene-butadiene rubber are general-purpose rubber. The products mainly cover tires, shoe soles, plates and pipes. They are the largest products in rubber. The vulcanization process has been developed for many years and Mature history; vulcanizing agent is called bridging agent. .In the industry, it is also called bridging agent according to the explanation of HG / T3060-1988 (1997) "Non-carbon black compounding agent term for rubber": vulcanizing agent; curing agent--a substance that can vulcanize (crosslink) rubber. Divided into inorganic and organic categories. The former category includes sulfur, sulfur monochloride, selenium, tellurium and so on. The latter category includes sulfur-co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/00C08L7/00C08L9/06C08L91/06C08L21/00C08L23/16C08L95/00C08L23/12C08L23/06C08K13/02C08K3/36C08K5/3445C08K5/098C08K5/14
CPCC08K3/36C08K5/098C08K5/14C08K5/3445C08K13/02C08L7/00C08L9/00C08L9/06C08L2201/02C08L2205/025C08L2205/03C08L2205/035C08L91/06C08L21/00C08L23/16C08L95/00C08L23/12C08L23/06
Inventor 盛钧
Owner NANJING SIKAI RUBBER & PLASTIC PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com