A technology for steel surface and treatment agent, applied in the direction of metal material coating process, etc., can solve the problem that the anti-oxidation, anti-corrosion, anti-acid and moisture-proof functions of anti-rust agents are not strong enough, the appearance and mechanical properties of steel parts are damaged, rust and anti-corrosion The problem of inconvenient cleaning of the agent can be achieved to increase the anti-rust performance, good lubricity, and the effect of isolating moisture and moisture.

Inactive Publication Date: 2016-09-07
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Corrosion of steel is a problem often encountered in production and life. Rusting of steel not only damages the appearance and mechanical properties of steel parts, but also has a certain impact on the use of products. After rusting, the product life is short. Moreover, the corroded steel is easy to break during use and cannot be used normally.
In order to effectively improve the performance of steel, it is necessary to carry out certain treatment on the surface of the steel to effectively increase the antirust performance of the steel surface. Although the existing rust-removing preservatives have a certain antirust effect, the effect is not good and cannot be used to treat the steel. Anti-rust for a long time, and it is inconvenient to clean the rust-removing preservatives used now, and the anti-oxidation, anti-corrosion, acid and moisture-proof functions of the existing anti-rust agents are not strong enough, which brings troubles to actual use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A water-based treatment agent for steel surface, characterized in that it includes 19 parts of disodium hydrogen phosphate, 28 parts of glycerin, 55 parts of phosphoric acid, 25 parts of zinc oxide, 40 parts of zinc nitrate, 15 parts of magnesium chloride, 3 parts of defoaming agent, and 38 parts of tea leaves 23 parts of radish slices, 16 parts of silicon dioxide, 22 parts of glycerin, 14 parts of manganese dihydrogen phosphate, 16 parts of polyethylene glycol, 26 parts of epoxy soybean oil, 6 parts of petroleum acid, 7 parts of fungicide, 6 parts of o-methylaniline and 10 parts of sodium hexametaphosphate.

[0019] The bactericide is a mixture of tebuconazole, cyproconazole, metconazole, difenoconazole and flusilazole.

[0020] The defoamer is a mixture of emulsified silicone oil, high-carbon alcohol fatty acid ester complex, and polyoxyethylene polyoxypropylene pentaerythritol ether.

[0021] The production method is as follows: 1) After pulverizing 23 parts of radi...

Embodiment 2

[0030]A water-based treatment agent for steel surfaces, including 24 parts of disodium hydrogen phosphate, 24 parts of glycerin, 63 parts of phosphoric acid, 15 parts of zinc oxide, 46 parts of zinc nitrate, 7 parts of magnesium chloride, 7 parts of defoamer, 33 parts of tea leaves, and radish slices 26 parts, 13 parts of silicon dioxide, 25 parts of glycerin, 11 parts of manganese dihydrogen phosphate, 19 parts of polyethylene glycol, 21 parts of epoxy soybean oil, 9 parts of petroleum acid, 4 parts of fungicide, o-methylaniline 8 parts and 9 parts of sodium hexametaphosphate.

[0031] The fungicide is a mixture of cyproconazole, hexaconazole, metconazole, difenoconazole and flusilazole.

[0032] The defoamer is a mixture of emulsified silicone oil, high-carbon alcohol fatty acid ester complex, and polyoxyethylene polyoxypropylene pentaerythritol ether.

[0033] The production method is as follows: 1) After crushing 26 parts of radish slices, put the mixture into an extrusio...

Embodiment 3

[0042] A water-based treatment agent for steel surfaces, including 20 parts of disodium hydrogen phosphate, 26 parts of glycerin, 60 parts of phosphoric acid, 18 parts of zinc oxide, 43 parts of zinc nitrate, 11 parts of magnesium chloride, 6 parts of defoaming agent, 35 parts of tea leaves, and radish slices 26 parts, 14 parts of silicon dioxide, 23 parts of glycerin, 11 parts of manganese dihydrogen phosphate, 19 parts of polyethylene glycol, 23 parts of epoxy soybean oil, 8 parts of petroleum acid, 6 parts of fungicide, o-methylaniline 7 parts and 9 parts of sodium hexametaphosphate.

[0043] The bactericide is a mixture of tebuconazole, cyproconazole, hexaconazole, metconazole and flusilazole.

[0044] The defoamer is a mixture of emulsified silicone oil, high-carbon alcohol fatty acid ester complex, and polyoxyethylene polyoxypropylene pentaerythritol ether.

[0045] The production method is as follows: 1) After pulverizing 26 parts of radish slices, put the mixture into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a steel surface waterborne treatment agent and a production method. The steel surface waterborne treatment agent comprises 19-24 parts of disodium hydrogen phosphate, 24-28 parts of glycerin, 55-63 parts of phosphoric acid, 15-25 parts of zinc oxide, 40-46 parts of zinc nitrate, 7-15 parts of magnesium chloride, 3-7 parts of antifoaming agents, 33-38 parts of tea leaves, 23-26 parts of radish pieces, 13-16 parts of silicon dioxide, 22-25 parts of glycerin , 11-14 parts of manganous dihydrogen phosphate, 16-19 parts of polyethylene glycol, 21-26 parts of epoxidized soybean oil, 6-9 parts of petroleum acid, 4-7 parts of bactericides, 6-8 parts of o-toluidine and 9-10 parts of sodium hexametaphosphate. The special additives are contained in the steel surface waterborne treatment agent and can permeate into matter such as rust, corrosives, oil stains and mud stains, stripping of a connector is relieved, the connector is easy to clean, dirt such as incrustations and dust attached to a steel surface can be effectively removed, an antirust oil film is reserved on the steel surface or the surface of other materials, moisture and water can be effectively isolated, and the service life of the connector can be effectively prolonged.

Description

technical field [0001] The invention relates to the technical field of industrial organic cleaning agents, in particular to a steel surface water-based treatment agent and a production method. Background technique [0002] Corrosion of steel is a problem often encountered in production and life. Rusting of steel not only damages the appearance and mechanical properties of steel parts, but also has a certain impact on the use of products. After rusting, the product life is short. Moreover, the corroded steel is easy to break during use and cannot be used normally. In order to effectively improve the performance of steel, it is necessary to carry out certain treatment on the surface of the steel to effectively increase the antirust performance of the steel surface. Although the existing rust-removing preservatives have a certain antirust effect, the effect is not good and cannot be used to treat the steel. Anti-rust for a long time, and it is inconvenient to clean the rust-re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/08C23C22/13
CPCC23G1/083C23C22/13
Inventor 王和山朱建林王和东
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap