PC/PET alloy material prepared by utilization of waste PC and PET materials

A kind of alloy material and waste technology, applied in the field of PC/PET alloy materials, can solve the problems of low impact resistance, poor fluidity, poor toughness of PC/PET, etc., achieve good toughness and impact strength, good visual effect, and good flame retardancy The effect of the function

Inactive Publication Date: 2016-09-14
HUIAN WEIKE ELECTRONICS TECH CO LTD
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PC / PET has poor toughness and low impact resistance. In addition, it also has the disadvantages of being easily aged. Poor performance and other shortcomings, can no longer be used outdoors, product reliability is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Roughly wash and rinse the recovered waste PC and PET materials in the pool, and then enter the rotary washing machine and add cleaning agent for 1.5 hours.

[0025] (2) Dehydrate and dry the cleaned waste PC and PET materials through a dehydrator.

[0026] (3) Put the waste PC and PET materials that have been dehydrated and dried into a fine grinder and crush them into small pieces of about 3cm.

[0027] (4) Weigh 55g of glass fiber, 45g of magnesium salt whiskers, 70g of butyl stearate, 130g of lead stearate, 50g of diphenyl phosphate, and 50g of polydimethylsiloxane, and then add them into a high-speed mixer to fully Mix for 10 minutes, then feed the mixed materials into a twin-screw extruder for melt blending at 270° C. and a melting time of 20 minutes, and then cool to prepare a composite material masterbatch.

[0028] (5) Weigh 350g of PC and 250g of PET after drying treatment and add them to the composite material masterbatch, and add them into a high-speed ...

Embodiment 2

[0032] (1) Roughly wash and rinse the recovered waste PC and PET materials in the pool, and then enter the rotary washing machine and add cleaning agent for 1.5 hours.

[0033] (2) Dehydrate and dry the cleaned waste PC and PET materials through a dehydrator.

[0034] (3) Put the waste PC and PET materials that have been dehydrated and dried into a fine grinder and crush them into small pieces of about 3cm.

[0035] (4) Weigh 110g of glass fiber, 90g of magnesium salt whiskers, 70g of butyl stearate, 130g of lead stearate, 25g of diphenyl phosphate, and 25g of polydimethylsiloxane, and then add them into a high-speed mixer to fully Mix for 30 minutes, then feed the mixed materials into a twin-screw extruder for melt blending at 290° C. and a melting time of 40 minutes, and then cool to prepare a composite material masterbatch.

[0036](5) Weigh 250g of PC and 300g of PET after drying treatment and add them to the composite material masterbatch, and add them into a high-speed ...

Embodiment 3

[0040] (1) Roughly wash and rinse the recovered waste PC and PET materials in the pool, and then enter the rotary washing machine and add cleaning agent for 1.5 hours.

[0041] (2) Dehydrate and dry the cleaned waste PC and PET materials through a dehydrator.

[0042] (3) Put the waste PC and PET materials that have been dehydrated and dried into a fine grinder and crush them into small pieces of about 3cm.

[0043] (4) Weigh 55g of glass fiber, 45g of magnesium salt whiskers, 70g of butyl stearate, 130g of lead stearate, 25g of diphenyl phosphate, and 25g of polydimethylsiloxane, and then add them into a high-speed mixer to fully Mix for 25 minutes, then feed the mixed materials into a twin-screw extruder for melt blending at 280° C. and a melting time of 30 minutes, and then cool to prepare a composite material masterbatch.

[0044] (5) Weigh 250g of PC and 400g of PET after drying treatment and add them to the composite material masterbatch, and add them into a high-speed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PC / PET alloy material prepared by the utilization of waste PC and PET materials. a preparation method of the PC / PET alloy material comprises the following steps: washing and crushing waste polycarbonate and poly(ethylene terephthalate) resin materials, adding auxiliaries such as a lubricant, a fire retardant, a fortifier and the like, fully mixing, and heating and conducting compression moulding forming to prepare the polycarbonate / poly(ethylene terephthalate) resin alloy material. The prepared material has high heat resistance, good toughness and impact strength and good flame retardancy, and is not easy to crack.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PC / PET alloy material prepared from waste PC and PET materials. Background technique [0002] Polyethylene terephthalate (PET) has excellent properties such as high strength, heat resistance, and abrasion resistance, and is very popular in the textile industry and other industries. At present, PET fiber has become the most productive variety among synthetic fibers. In addition, PET is also widely used in the field of packaging and film due to its excellent mechanical strength, light weight, chemical solvent resistance, barrier properties and excellent transparency. Although PET has many excellent properties, there are also some shortcomings, such as poor impact resistance, slow crystallization speed, uneven crystal structure, easy water absorption, large shrinkage of molded products, rough surface of products, etc., which limit its wide application. , which is cause...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08L83/04C08K13/04C08K7/14C08K7/08C08K5/523C08K5/098C08J3/22
CPCC08L69/00C08J3/226C08J2367/02C08J2369/00C08J2467/02C08J2469/00C08J2483/04C08K2201/014C08L67/02C08L2201/02C08L2201/08C08L2205/03C08L2207/20
Inventor 王少平
Owner HUIAN WEIKE ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com