Anti-dazzle glass etching liquid and preparation method thereof

A technology of anti-glare glass and etching solution, which is applied in the field of anti-glare glass etching solution and its preparation, which can solve the problems of high cost and instability of etching solution, and achieve the effect of good etching effect, low cost and high transmittance

Active Publication Date: 2016-09-21
ZHENGZHOU UNIVERSITY OF AERONAUTICS
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the deficiencies of the above technical problems, provide an anti-glare glass etching solution and its preparation method, to overcome the high cost and unstable defects of the existing etching solution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of antiglare glass etchant, is made up of the raw material of following percentage by weight: H 2 SO 4 8.2%, Na 2 SiF 6 1.8%, ZnCl 2 4.5%, NH 4 HF 2 21.5%, CaF 2 4.2%, (NH 4 ) 2 SO 4 4.2%, BaSO 4 2.5%, viscosity modifier 1.8%, lauryl glucoside 2.2% and water 49.1%.

[0015] The preparation method of anti-glare glass etching solution: comprises the following steps: adding water into H 2 SO 4 In, stir well and add Na 2 SiF 6 , NH 4 HF 2 and CaF 2 , stir well and then add ZnCl 2 , (NH 4 ) 2 SO 4 and BaSO 4 Stir evenly, then add a viscosity modifier (a 1:2 mixture of montmorillonite and silica sol) and dodecyl glucoside, stir evenly, and then age to obtain an anti-glare glass etching solution.

[0016] Use the etching solution prepared above to treat the glass according to the following methods: ① Clean the glass; ② Treat the cleaned glass in the etching solution for 30-120 seconds; ③ Cool down; ④ Spray cleaning and constant temperatu...

Embodiment 2

[0018] A kind of antiglare glass etchant, is made up of the raw material of following percentage by weight: H 2 SO 4 8.6%, Na 2 SiF 6 2%, ZnCl 2 5%, NH 4 HF 2 22.1%, CaF 2 3.8%, (NH 4 ) 2 SO 4 3.8%, BaSO 4 2.3%, viscosity modifier 1.6%, surfactant 1.8% and water 49%.

[0019] The preparation method of anti-glare glass etching solution: comprises the following steps: adding water into H 2 SO 4 In, stir well and add Na 2 SiF 6 , NH 4 HF 2 and CaF 2 , stir well and then add ZnCl 2 , (NH 4 ) 2 SO 4 and BaSO 4 Stir evenly, then add a viscosity modifier (1:1 mixture of propylene glycol and polyvinyl alcohol) and dodecyl glucoside, stir evenly, and then age to obtain an anti-glare glass etching solution.

[0020] Use the etching solution prepared above to treat the glass according to the following methods: ① Clean the glass; ② Treat the cleaned glass in the etching solution for 30-120 seconds; ③ Cool down; ④ Spray cleaning and constant temperature drying....

Embodiment 3

[0022] A kind of antiglare glass etchant, is made up of the raw material of following percentage by weight: H 2 SO 4 9.6%, Na 2 SiF 6 2.2%, ZnCl 2 5.5%, NH 4 HF 2 22.5%, CaF 2 3.6%, (NH 4 ) 2 SO 4 3.6%, BaSO 4 2.1%, viscosity modifier 1.6%, surfactant 1.6% and water 47.7%.

[0023] The preparation method of anti-glare glass etching solution: comprises the following steps: adding water into H 2 SO 4 In, stir well and add Na 2 SiF 6 , NH 4 HF 2 and CaF 2 , stir well and then add ZnCl 2 , (NH 4 ) 2 SO 4 and BaSO 4 Stir evenly, then add a viscosity modifier (montmorillonite) and dodecyl glucoside, stir evenly, and then age to obtain an anti-glare glass etching solution.

[0024] Use the etching solution prepared above to treat the glass according to the following methods: ① Clean the glass; ② Treat the cleaned glass in the etching solution for 30-120 seconds; ③ Cool down; ④ Spray cleaning and constant temperature drying.

[0025] Anti-glare glass test...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hazeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an anti-dazzle glass etching liquid and a preparation method thereof. The anti-dazzle glass etching liquid comprises the following raw materials in percentage by weight: 8.2-9.6% of H2SO4 (sulfate), 1.8-2.2% of Na2SiF6 (sodium fluosilicate), 4.5-5.5% of ZnCl (zinc chloride), 21.5-22.5% of NH4HF2 (ammonium bifluoride), 3.6-4.2% of CaF (calcium fluoride), 3.6-4.2% of (NH4)2SO4 (ammonium sulfate), 2.1-2.5% of BaSO4 (barium sulfate), 1.6-1.8% of viscosity adjuster, 1.8-2.2% of dodecyl glucoside, and 45-55% of water. The anti-dazzle glass etching liquid has the advantages that the defects of high cost and instability of the existing etching liquid are overcome; the cost is low, the surface particles of the product are fine, and the transmittance is high.

Description

technical field [0001] The invention relates to the technical field of anti-glare glass preparation, in particular to an anti-glare glass etching solution and a preparation method thereof. Background technique [0002] Glass is widely used in daily life because of its advantages such as high strength, excellent optical properties, and good long-term working stability (not easy to age). However, due to the high reflectivity of the glass surface, it often causes "glare attack", which is what we often call "light pollution". And trouble; when we stop in front of the glass window to explore the scenery inside the window, the reflection of the glass surface often prevents us from clearly observing the scenery inside the window, etc., all of which are caused by the light reflection on the glass surface. To reduce the impact of light emitted by the glass, matting the glass can have a good effect. [0003] Anti-glare glass can reduce the interference of ambient light, reduce the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C15/00
CPCC03C15/00
Inventor 禹建丽李金钟
Owner ZHENGZHOU UNIVERSITY OF AERONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap