Blended yarn with hemp and cotton multifunctional fiber reinforced by graphene fiber

A graphene fiber, blended yarn technology, applied in the directions of liquid/gas/vapor fiber/sliver/roving treatment, fiber treatment, plant fiber, etc., to achieve the effect of improving internal performance and improving dyeing effect

Active Publication Date: 2016-09-21
YIWU MASHANGSHENG KNIT GOODS CO LTD
View PDF7 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are still few reports on the preparation of cond

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1) Soak the hemp fiber in a pectinase solution with a concentration of 10g / L at room temperature for 30 minutes; then continue to immerse the treated hemp fiber in a chitosan aqueous solution with a concentration of 20g / L, soak for 1 hour, dehydrate and dry ;

[0022] 2) The hemp fiber, bamboo fiber, wool fiber and cotton fiber are soaked in acetone at a mass ratio of 3:1:1:5 for 2 hours, and ultrasonic vibration treatment is performed for 1 hour. After washing, dehydration and drying are carried out to obtain cotton hemp. Multifunctional fiber

[0023] 3) The prepared cotton and linen multifunctional fiber and graphene fiber are mixed and twisted into a mixed yarn at a mass ratio of 100:1.

Embodiment 2

[0025] 1) Soak the hemp fiber in a pectinase solution with a concentration of 50g / L at room temperature for 15 minutes; then continue to immerse the treated hemp fiber in a chitosan aqueous solution with a concentration of 10g / L, soak for 3 hours, dehydrate and dry ;

[0026] 2) The hemp fiber, bamboo fiber, wool fiber and cotton fiber are soaked in acetone at a mass ratio of 5:3:1:10 for 6 hours, and ultrasonic vibration treatment is performed for 1 hour. After washing, they are dehydrated and dried to obtain cotton hemp. Multifunctional fiber

[0027] 3) The prepared cotton and linen multifunctional fiber and graphene fiber are mixed and twisted into a mixed yarn at a mass ratio of 100:5.

Embodiment 3

[0029] 1) Soak the hemp fiber in a pectinase solution with a concentration of 30g / L at room temperature for 20 minutes; then continue to immerse the treated hemp fiber in a chitosan aqueous solution with a concentration of 15g / L, soak for 2 hours, dehydrate and dry ;

[0030] 2) The hemp fiber, bamboo fiber, wool fiber and cotton fiber are soaked in acetone at a mass ratio of 4:2:1:7 for 4 hours, and ultrasonic vibration treatment is carried out for 1 hour. After washing, they are dehydrated and dried to obtain cotton hemp. Multifunctional fiber

[0031] 3) The prepared cotton and linen multifunctional fiber and graphene fiber are mixed and twisted into a mixed yarn at a mass ratio of 100:10.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses blended yarn with hemp and cotton multifunctional fiber reinforced by graphene fiber. The blended yarn is prepared from the following steps that 1, hemp fiber is placed in a pectinase solution to be soaked at normal temperature, continues to be soaked in a chitosan aqueous solution, and then is dehydrated and dried; 2, the hemp fiber, bamboo fiber, wool fiber and cotton fiber are placed in acetone to be soaked while ultrasonically oscillated and are washed, dehydrated and dried to prepare the hemp and cotton multifunctional fiber; 3, the hemp and cotton multifunctional fiber and graphene fiber are mixed uniformly and entwisted into the blended yarn. As the graphene fiber is added for blending, strength and tenacity of the hemp and cotton multifunctional fiber blended yarn are improved, and the specific resistance of the blended yarn is about 10-103 omega*m; after mild biological enzyme treatment, the hemp fiber has the degumming effect and avoid retting degumming caused by chemicals, natural phenolic substances and derivatives thereof contained in the hemp fiber are well reserved, and the effective and natural antibacterial function is achieved.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a graphene fiber-reinforced blended yarn of hemp-cotton multifunctional fiber. Background technique [0002] Conductive fibers have always been a research hotspot for functional fibers, generally referring to resistivity less than 10 8 The fiber of Ω·cm has the functions of conduction, electric heating and anti-electromagnetic radiation, and is usually concentrated in the fields of anti-static clothing or anti-electromagnetic radiation clothing used in special occasions. [0003] The main methods for the manufacture of conductive fibers include: one is to coat the surface of conventional fibers with conductive components, and the other is to mix conductive materials with fiber raw materials and make conductive fibers by spinning. The method of coating the conductive layer on the surface of the fiber is to coat the conductive material containing metal, carbon black o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/04D06B3/02D01F9/12D06M16/00D06M15/03D06M101/06D06M101/12
CPCD01F9/12D02G3/04D06B3/02D06M15/03D06M16/00D06M16/003D06M2101/06D06M2101/12D06M2200/50D10B2101/10D10B2201/01D10B2201/02D10B2201/10D10B2211/02
Inventor 王铀锝
Owner YIWU MASHANGSHENG KNIT GOODS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap