Preparation method of material composition for effectively relieving noise pollution

A material composition and noise pollution technology, which is applied in the field of preparation of material compositions and can solve problems such as the inability to effectively reduce noise hazards and the like

Inactive Publication Date: 2016-10-26
广州市康水科技有限责任公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] For individuals, when encountering noise, covering ears with hands or plugging earholes with cotton balls cannot effectively reduce and prevent noise hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of material composition for effectively relieving noise pollution
  • Preparation method of material composition for effectively relieving noise pollution

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The present invention provides a kind of preparation method of the material composition that effectively reduces noise pollution, is characterized in that, comprises the following steps:

[0025] a) Mix and stir ultra-high molecular weight polyethylene powder, pore-forming agent and sound-insulating medium to obtain a mixture, the weight ratio of the ultra-high-molecular-weight polyethylene powder, pore-forming agent and sound-insulating medium is 100~300:50~ 100:100~150; the sound insulation medium is selected from one or more of modified zeolite, activated attapulgite, modified diatomite, coke powder, pumice powder and montmorillonite powder;

[0026] b) pressing, sintering and cooling the mixture obtained in step a) in a mould;

[0027] The pressing pressure is 0.4MPa-1Mpa; the sintering temperature is 200°C-250°C; the sintering time is 60-120min; the cooling temperature is 40°C-60°C.

[0028] In the present invention, firstly, the ultra-high molecular weight polyet...

Embodiment 1

[0063] (1) Take by weighing 200 g of ultra-high molecular weight polyethylene powder with a particle size of 95 μm. The ultra-high molecular weight polyethylene is the M-I type product of Beijing Dongfang Petrochemical Co., Ltd. Auxiliary No. 2 Factory, and its molecular weight is 1.5 million;

[0064] (2) Take 75g of pore forming agent;

[0065] (3) Taking by weighing the modified and activated zeolite powder 150g of 84 μm particle diameter activated according to the modification and activation mode of the present invention;

[0066] (4) Put the above three powders into a mechanical stirrer and stir for 10 minutes to mix evenly;

[0067] (5) Fill the mixed powder into a tubular mold, press under a hydraulic pressure of 0.7 MPa, and sinter at a temperature of 200° C. for 120 minutes;

[0068] (6) Cool naturally to 50° C. and then release the mold with a siloxane uranium release agent to obtain a material composition for reducing noise pollution.

Embodiment 2

[0070] (1) Take by weighing 200 g of ultra-high molecular weight polyethylene powder with a particle size of 95 μm. The ultra-high molecular weight polyethylene is the M-I type product of Beijing Dongfang Petrochemical Co., Ltd. Auxiliary No. 2 Factory, and its molecular weight is 1.5 million;

[0071] (2) Take 75g of pore forming agent;

[0072] (3) Take by weighing the attapulgite powder 150g of modified and activated attapulgite powder with a particle diameter of 94 μm activated according to the modification and activation mode of the present invention;

[0073] (4) Put the above three powders into a mechanical stirrer and stir for 10 minutes to mix evenly;

[0074] (5) Fill the mixed powder into a tubular mold, press under a hydraulic pressure of 0.7 MPa, and sinter at a temperature of 200° C. for 120 minutes;

[0075](6) Cool naturally to 50° C. and then release the mold with a siloxane uranium release agent to obtain a material composition for reducing noise pollution. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a material composition for effectively relieving noise pollution. The preparation method is characterized by comprising the following steps: a) ultrahigh molecular weight polyethylene powder, a poring agent and a sound insulation medium are mixed to obtain a mixture; the weight ratio of the ultrahigh molecular weight polyethylene powder to the poring agent and to the sound insulation medium is 100-300: 50-100: 100-150; and the sound insulation medium is one or several of modified zeolite, activated attapulgite, modified diatomite, coke powder, pumice powder and montmorillonite powder; and b) the mixture obtained in the step a) is pressed, sintered and cooled in a mold; the pressing pressure is 0.4-1 MPa; the sintering temperature is 200-250 DEG C; the sintering time is 60-120 min; and the cooling temperature is 40-60 DEG C. The prepared material composition can preferably relieve the harm of the noise pollution to people.

Description

technical field [0001] The invention relates to a preparation method of a material composition which can effectively reduce noise pollution. Background technique [0002] Construction site noise, commercial noise, domestic noise, road noise, hip-hop noise, urban rail transit noise and vibrations and other pollution have formed a noise siege, and have become the three major pollution sources alongside air pollution and water pollution. Japan even ranks noise as the first public nuisance, and it is urgent to control noise pollution. [0003] Noise can cause irreversible damage to the two parts of the ear. Sudden noise can break the eardrum and crack the connective bones, malleus, incus and pedal bones in the middle ear, resulting in hearing loss and loss. The cochlea is a part of the inner ear, and there are sensory cells in it. There are about 16,000 of these cells in each ear. They transmit sound stimulation to the nerves to the brain, destroying these cells, that is, destr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C43/00B29C43/58C08L23/06C08K13/06C08K9/02C08K9/04C08K3/34
CPCB29C43/006B29C43/58B29C2043/5808B29C2043/5816C08K3/34C08K3/346C08K9/02C08K9/04C08K13/06C08K2201/003C08K2201/014C08L23/06
Inventor 栾云堂田丹宇曹龙基林春
Owner 广州市康水科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com