Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Antioxidant plastic color masterbatch and preparation method thereof

A color masterbatch and anti-oxidation technology, which is applied in the field of anti-oxidation plastic color masterbatch and its preparation, can solve the problems of no anti-oxidation effect, poor coloring effect, short storage time, etc., and achieve good coloring effect and easy The effect of storage and long storage time

Inactive Publication Date: 2016-11-09
WUHU TIANXIONG NEW MATERIAL TECH
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the existing plastic color masterbatch has poor coloring effect, no anti-oxidation effect, easy to fade, and the storage time is not long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-oxidation plastic color masterbatch, made of the following raw materials in parts by weight: 16 parts of titanium dioxide, 10 parts of carbon black, 25 parts of iron oxide red, 12 parts of iron oxide yellow, 7 parts of phthalocyanine blue, 6 parts of phthalocyanine green, 13 parts of polyester fiber, 15 parts of sodium stearate, 6 parts of vinyl bis stearamide, 14 parts of microcrystalline paraffin wax, 22 parts of oxidized polyethylene wax, 7 parts of nano activated carbon, butyl hydroxy anise 4 parts of ether, 22 parts of 2,6-di-tert-butyl-p-cresol, 10 parts of diphenylamine, 20 parts of p-phenylenediamine, 6 parts of dodecanethiol, 18 parts of hydroquinone, 20 parts of thiobisphenol And 36 parts of polyvinyl chloride.

[0024] A preparation method of an anti-oxidation plastic color masterbatch, comprising the following steps:

[0025] 1) Mix 16 parts of titanium dioxide, 10 parts of carbon black, 25 parts of iron oxide red, 12 parts of iron oxide yellow, 7 p...

Embodiment 2

[0034] An anti-oxidation plastic color masterbatch, made of the following raw materials in parts by weight: 18 parts of titanium dioxide, 12.5 parts of carbon black, 27.5 parts of iron oxide red, 13 parts of iron oxide yellow, 8 parts of phthalocyanine blue, 8 parts of phthalocyanine green, 15.5 parts of polyester fiber, 17.5 parts of sodium stearate, 8 parts of vinyl bis stearamide, 16 parts of microcrystalline paraffin, 24 parts of oxidized polyethylene wax, 8 parts of nano activated carbon, butyl hydroxy anise 6 parts of ether, 25 parts of 2,6-di-tert-butyl-p-cresol, 12.5 parts of diphenylamine, 22.5 parts of p-phenylenediamine, 7 parts of dodecanethiol, 20 parts of hydroquinone, 22.5 parts of thiobisphenol And 38 parts of polyvinyl chloride.

[0035] A preparation method of an anti-oxidation plastic color masterbatch, comprising the following steps:

[0036] 1) Mix 18 parts of titanium dioxide, 12.5 parts of carbon black, 27.5 parts of iron oxide red, 13 parts of iron oxi...

Embodiment 3

[0045] An anti-oxidation plastic color masterbatch, made of the following raw materials in parts by weight: 20 parts of titanium dioxide, 15 parts of carbon black, 30 parts of iron oxide red, 14 parts of iron oxide yellow, 9 parts of phthalocyanine blue, 10 parts of phthalocyanine green, 18 parts of polyester fiber, 20 parts of sodium stearate, 10 parts of vinyl bis stearamide, 18 parts of microcrystalline paraffin, 26 parts of oxidized polyethylene wax, 9 parts of nano activated carbon, butyl hydroxy anise 8 parts of ether, 28 parts of 2,6-di-tert-butyl-p-cresol, 15 parts of diphenylamine, 25 parts of p-phenylenediamine, 8 parts of dodecanethiol, 22 parts of hydroquinone, 25 parts of thiobisphenol And 40 parts of polyvinyl chloride.

[0046] A preparation method of an anti-oxidation plastic color masterbatch, comprising the following steps:

[0047] 1) Mix 20 parts of titanium dioxide, 15 parts of carbon black, 30 parts of iron oxide red, 14 parts of iron oxide yellow, 9 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses antioxidant plastic color masterbatch. The antioxidant plastic color masterbatch is prepared from, by weight, 16-20 parts of titanium dioxide, 10-15 parts of carbon black, 25-30 parts of iron oxide red, 12-14 parts of iron oxide yellow, 7-9 parts of phthalocyanine blue, 6-10 parts of phthalocyanine green, 13-18 parts of polyester fibers, 15-20 parts of sodium stearate, 6-10 parts of N,N-ethylene bis-stearamide, 14-18 parts of microcrystalline wax, 22-26 parts of oxidized polyethylene wax, 7-9 parts of activated carbon nanoparticles, 4-8 parts of butyl hydroxy anisd, 22-28 parts of butylated hydroxytoluene, 10-15 parts of diphenylamine, 20-25 parts of p-phenylenediamine, 6-8 parts of dodecyl mercaptan, 18-22 parts of p-dihydroxybenzene, 20-25 parts of thio-bis-phenol and 36-40 parts of polyvinyl chloride. The antioxidant plastic color masterbatch is good in coloring effect, has an antioxidant effect, cannot fade and is long in storage time.

Description

technical field [0001] The invention relates to an anti-oxidation plastic color masterbatch and a preparation method thereof. Background technique [0002] Color masterbatch is a mixture of resin and a large amount of pigment (up to 50%) or dyes to make a high concentration of color. Color masterbatch, also known as color species, is an aggregate made by uniformly loading super-normal pigments or dyes in resin. When processing, a small amount of color masterbatch and uncolored resin is mixed to achieve the colored resin or product with the designed pigment concentration. [0003] Color masterbatch is a high-concentration colored pellet made of colorants, carrier resins, dispersants, coupling agents, surfactants, and plasticizers; in addition to the above raw materials, functional color masterbatches must be added according to functional requirements. Stabilizer, antistatic agent, flame retardant, foaming agent and other additives. Functional color masterbatch is a masterb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/30C08L67/00C08L91/06C08K13/02C08K3/22C08K3/04C08K5/098C08K5/20
CPCC08L27/06C08K2201/011C08K2201/014C08L2201/08C08L2205/035C08L2205/16C08L2310/00C08L23/30C08L67/00C08L91/06C08K13/02C08K2003/2241C08K3/04C08K2003/2272C08K5/098C08K5/20
Inventor 黄雄关
Owner WUHU TIANXIONG NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com