Porcelain brick with three-dimensional decorative effect and preparation method thereof

A decorative effect, porcelain tile technology, applied in the field of architectural ceramics, can solve the problems of high cost, lack of three-dimensional texture expression of pattern texture, large amount of batter and color additives, etc., to achieve the goal of reducing dosage, rich texture, and saving consumption Effect

Active Publication Date: 2019-03-29
HANGZHOU NABEL CERAMIC +2
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of high cost caused by the large amount of batter and color aid in the prior art, and the lack of three-dimensional texture expression of the pattern texture, and to provide a more environmentally friendly and economical porcelain tile with richer decorative effects. Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Prepare porcelain brick body powder according to the conventional method, and prepare 4 kinds of color powder for standby;

[0038] (2) Prepare porcelain tile fabrics. Both fabrics A and B are made of feldspar-based barren materials and kaolin-based plastic materials. However, auxiliary colorants are introduced into fabric B and wet ball milling. The slurries of the two fabrics are uniform. The fineness is controlled to be within 0.5% of the 325 mesh sieve, and the specific gravity is 1.8g / cm 3 , where the dry material of surface paste A and auxiliary admixtures are wet ball-milled into a slurry that meets the performance requirements of leaching, and the dry materials of fabric B and auxiliary admixtures are wet-ball-milled to meet the performance requirements of the slurry, then dried at 800°C Calcined to make dry powder, and mixed with printing oil and auxiliary additives to prepare printed fabrics that meet the printing performance, and set aside. The chemical ...

Embodiment 2

[0048] (1) Prepare the porcelain brick body powder according to the conventional method, and prepare 5 kinds of color powder for later use;

[0049] (2) Preparation of porcelain tile fabrics, fabrics A and B are made of feldspar-based barren materials and kaolin-based plastic materials.

[0050] Ingredients, but the auxiliary coloring agent is introduced into the fabric B, wet ball milling, the fineness of the slurry of the two fabrics is controlled to be 325 mesh, the sieve balance is within 0.5%, and the specific gravity is 1.7g / cm 3 , where the dry material of the surface paste A and the auxiliary admixture are wet ball milled into a slurry that meets the performance requirements of leaching, and the dry material of the fabric B and the auxiliary admixture are wet ball milled to meet the performance requirements of the slurry and then dried at 900 ° C Calcined to make dry powder, and mixed with printing oil and auxiliary additives to prepare printed fabrics that meet the pr...

Embodiment 3

[0060] (1) Prepare porcelain brick body powder according to the conventional method, and prepare 3 kinds of color powder for later use;

[0061] (2) Prepare porcelain tile fabrics. Both fabrics A and B are made of feldspar-based barren materials and kaolin-based plastic materials. However, auxiliary colorants are introduced into fabric B and wet ball milling. The slurries of the two fabrics are uniform. The fineness is controlled to be within 0.5% of the 325 mesh sieve, and the specific gravity is 1.9g / cm 3 , where the dry material of surface paste A and auxiliary admixtures are wet-ball-milled into a slurry that meets the performance requirements of leaching, and the dry materials of fabric B and auxiliary admixtures are wet-ball-milled to meet the performance requirements of the slurry and dried at 1000°C Calcined to make dry powder, and mixed with printing oil and auxiliary additives to prepare printed fabrics that meet the printing performance, and set aside. The chemical...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a porcelain tile with three-dimensional decoration effects and a manufacturing method of the porcelain tile. The manufacturing method comprises the following steps of (1) preparing semifinished product powder of the porcelain tile by a conventional method; (2) preparing a surface material of the porcelain tile; (3) preparing a semifinished product of the porcelain tile; (4) drying the semifinished product; (5) sprinkling surface pulp A; (6) printing a surface material B; (7) performing drying after the surface material is applied; (8) jetting permeation ink; (9) performing firing; and (10) grinding edges. The porcelain tile and the manufacturing method thereof disclosed by the invention have the beneficial effects that the problems that the cost is increased because the consumption of the surface pulp and the consumption of dyeing assistant agents are high, and pattern grains lack of three-dimensional grain expression in the prior art are solved, besides, the technical problems that bottoms are exposed and the porcelain tile is not aesthetic due to deep processing of fluting, chamfering and the like of existing porcelain color-penetrated tiles are solved, and the manufacturing method of the porcelain tile which is environmental-friendly, economic and rich in decoration effects is provided.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a porcelain tile with a three-dimensional decorative effect and a preparation method thereof. Background technique [0002] At present, in order to achieve the effect of imitating natural stone or wood grain, the "bleeding" polishing technology is generally used in the bleed porcelain tile products, and the bleed process has experienced from screen printing bleed liquid containing soluble salt to spray penetration Ink upgrade. Chinese patent CN102795892B introduces a kind of bleed porcelain tile and its production method. By pouring porcelain polishing slurry on the surface of the green body layer, the penetration depth of bleed salt can be reduced from 2~3mm of traditional bleed brick to 0.3mm. ~0.5mm, which expands the types of flower salt used and enriches the color; on the other hand, it reduces the grinding thickness of the polishing process and reduces the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89B44C1/24
Inventor 余爱民夏昌奎甄燕萍樊叶利余剑峰余惠朱爱余曹承鑫
Owner HANGZHOU NABEL CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com