Ultralight rubber foam colloid particles and preparation method thereof

A technology of rubber foaming and colloidal particles, which is applied in the field of shoe material manufacturing, can solve the problems of poor softness and folding resistance, unsatisfactory wear resistance, and poor flexibility, etc., and achieve good folding resistance and cold resistance, and high quality Ultra-light, reduced density effect

Inactive Publication Date: 2016-12-21
许文谈
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) has a certain degree of lightening and easy molding, but the softness and folding resistance of the material are not good, even if part of the softness meets the requirements Its strength is still poor, especially the wear resistance is not ideal, and when the wear resistance is improved, the flexibility of the material becomes worse, and the anti-skid performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preferred ultra-light rubber foam rubber particles of the present invention include the following raw materials in parts by mass:

[0028] CPE / CM (chlorinated polyethylene) 30 parts by weight,

[0029] POE (polyolefin elastomer) 15 parts by weight,

[0030] EPDM (ethylene-propylene-diene rubber) 8 parts by weight,

[0031] 12 parts by weight of EVA (ethylene vinyl acetate),

[0032] 9 parts by weight of natural rubber,

[0033] Filling material (light calcium carbonate) 7 parts by weight,

[0034] 0.28 parts by weight of stearic acid,

[0035] Zinc stearate 0.52 parts by weight,

[0036] 0.53 parts by weight of DCP crosslinking agent,

[0037] Zinc oxide 0.7 parts by weight,

[0038] 1.11 parts by weight of AC blowing agent,

[0039] 1.85 parts by weight of anti-wear agent.

[0040] Its preparation method is as follows, comprises the following steps:

[0041] (1) First put the main material into the internal mixer to start blending and banburying until the...

Embodiment 2

[0045] The preferred ultra-light rubber foam rubber particles of the present invention include the following raw materials in parts by mass:

[0046] CPE / CM (chlorinated polyethylene) 28 parts by weight,

[0047] POE (polyolefin elastomer) 12 parts by weight,

[0048] EPDM (ethylene propylene diene monomer) 9 parts by weight,

[0049] EVA (ethylene vinyl acetate) 11 parts by weight,

[0050] 7 parts by weight of isoprene rubber,

[0051] Filling material (talcum powder) 6 parts by weight,

[0052] 0.32 parts by weight of stearic acid,

[0053] Zinc stearate 0.55 parts by weight,

[0054] 0.55 parts by weight of DCP crosslinking agent,

[0055] Zinc oxide 0.8 parts by weight,

[0056] 1.15 parts by weight of AC blowing agent,

[0057] 1.95 parts by weight of anti-wear agent.

[0058] The preparation method of the ultra-light rubber styrofoam is the same as that of Example 1.

[0059] In the present invention, the use ratio of each component of the main material is pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of shoe material manufacturing, and provides ultralight rubber foam colloid particles. The ultralight rubber foam colloid particles are prepared from, by weight, 20-40 parts of CPE-CM (chlorinated polyethylene), 12-18 parts of POE (polyolefin elastomers), 6.4-9.6 parts of EPDM (ethylene-propylene-diene monomer), 9.6-14.4 parts of EVA (ethylene vinyl acetate), 8-12 parts of natural rubber or isoprene rubber, 5.6-8.4 parts of filler, 0.24-0.36 part of stearic acid, 0.48-0.72 part of zinc stearate, 0.48-0.72 part of a DCP cross-linking agent, 0.64-0.96 part of zinc oxide, 0.96-1.44 parts of an AC foaming agent and 1.6-2.4 parts of a wear-resistant agent. Accordingly, the problems that an existing shoe material is poor in flexibility, fold resistance, anti-skid property and wear resistance, large in weight and like are solved.

Description

technical field [0001] The invention relates to the technical field of shoe material manufacturing, in particular to an ultra-light rubber foam granule and a preparation method thereof. Background technique [0002] Most of the existing EVA adopts the production method of POE modified materials. The modified materials are suitable for injection molding and compression molding. They can be widely used in shoe outsoles, sporting goods and other light industrial products. The ingredients are composed of 50-95% EVA, 5-40% POE (polyolefin elastomer), 5-20% talcum powder or CaCO3, metal oxide 1-2%, lubricant 0.1-1%, peroxide (bridging agent) 0.4-1%, 1-4% of azo foaming agent and appropriate amount of pigment are mixed by internal mixer, auxiliary mixing by open mixer, pelletizing, injection molding or compression molding. The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) has a certain degree of lightening and easy molding, but the softness and fold...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L23/08C08L23/16C08L7/00C08K13/02C08K3/26C08K5/09C08K5/098C08K3/22C08J9/10
CPCC08L23/286C08J9/103C08J2203/04C08J2323/28C08J2423/08C08L2203/14C08L2205/02C08L2205/035C08L23/0815C08L23/16C08L7/00C08K13/02C08K2003/265C08K5/09C08K5/098C08K2003/2296
Inventor 许文谈
Owner 许文谈
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap