Preparation method of odor-free correction liquid
A correction fluid, odorless technology, applied in the direction of coating, etc., can solve the problems of toxic chemicals, free in the air, odorless, etc., and achieve the effect of simple preparation method, good rewritability, and good covering property
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0017] First, weigh 20g of potato starch and 100mL of deionized water into a beaker, and use a 500W microwave oven to microwave for 180s, then add 0.3g of ammonium persulfate to the beaker to prepare a mixed solution, heat the mixed solution to 55°C, keep the temperature for 50min, and use The mass fraction is 5% sodium hydroxide solution to adjust the pH of the mixed solution to 8.0, then add 0.6g dicyandiamide to the beaker, let it stand for 3h, continue to heat to 90°C, keep the temperature for 30min, and use a mass fraction of 5% sodium hydroxide Adjust the pH of the mixed solution to 8.0, cool to room temperature to obtain a cross-linked modified starch oxidized adhesive, and set aside; then weigh 4g of zinc oxide, add it to a pulverizer, and pass it through a 300-mesh sieve. Add the powder and 20mL deionized water to the Erlenmeyer flask, stir at 300r / min for 20min, add 0.2g sodium dodecylbenzenesulfonate and 4g titanium dioxide to the Erlenmeyer flask, continue stirring ...
example 2
[0020] First weigh 25g of potato starch and 130mL of deionized water into a beaker, and microwave it in a 500W microwave oven for 190s, then add 0.35g of ammonium persulfate into the beaker to prepare a mixed solution, heat the mixed solution to 58°C, keep the temperature for 55min, and use The mass fraction is 5% sodium hydroxide solution to adjust the pH of the mixture to 8.5, then add 0.8g of dicyandiamide to the beaker, let it stand for 3.5 hours, continue to heat to 93°C, keep the temperature for 35min, and oxidize it with a mass fraction of 5% hydroxide Adjust the pH of the mixed solution to 8.5 with sodium solution, cool to room temperature to obtain a cross-linked modified oxidized starch adhesive, and set aside; then weigh 4.5g of zinc oxide, add it to a pulverizer, and pass it through a 300-mesh sieve. Add zinc oxide powder and 25mL deionized water to the Erlenmeyer flask, stir at 350r / min for 25min, add 0.25g sodium dodecylbenzenesulfonate and 4.5g titanium dioxide t...
example 3
[0023]First weigh 30g of potato starch and 160mL of deionized water into a beaker, and microwave it in a 500W microwave oven for 200s, then add 0.4g of ammonium persulfate into the beaker to prepare a mixed solution, heat the mixed solution to 60°C, keep the temperature for 60min, and use The mass fraction is 5% sodium hydroxide solution to adjust the pH of the mixed solution to 9.0, then add 0.9g dicyandiamide to the beaker, let it stand for 4h, continue to heat to 95°C, keep the temperature for 40min, and use a mass fraction of 5% sodium hydroxide Adjust the pH of the mixed solution to 9.0, cool to room temperature to obtain a cross-linked modified starch oxidized adhesive, and set aside; then weigh 5g of zinc oxide, add it to a pulverizer, and grind it through a 300-mesh sieve. Add the powder and 30mL of deionized water to the Erlenmeyer flask, stir at 400r / min for 30min, add 0.3g of sodium dodecylbenzenesulfonate and 5g of titanium dioxide to the Erlenmeyer flask, continue ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap