Composite air purifying filter paper material and filter element using same

An air purification and filter paper technology, applied in the field of air purification, can solve the problem of inability to achieve deodorization and purification, and achieve the effects of improving rapid purification and adsorption performance, increasing removal rate, and increasing contact area.

Inactive Publication Date: 2017-01-18
WUHU MATY AIR CONDITIONING EQUIP CO LTD +1
View PDF4 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purifier filter elements used in conventional air purifier products often disperse activated carbon and other similar particles into plastic parts with a honeycomb structure. Although they can remove odorous gases such as formaldehyde in the indoor environment, they are limited by this structure. Restricted, cannot realize the function of fast deodorization and purification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite air purifying filter paper material and filter element using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1) Activated carbon fiber pre-filter layer 1 is composed of activated carbon fiber and non-woven fabric substrate in a mass ratio of 4:6, and the overall grammage is 40g / m 2 ;

[0031] 2) Adsorption catalytic particle layer 2 is activated carbon supported metal oxide MnO x Mix the Mn precursor manganese nitrate solution with activated carbon, impregnate and stir, impregnate for 24 hours, and then bake at 300°C for 30 minutes to obtain catalyst particles for catalytic oxidation of formaldehyde at room temperature, thus making adsorption catalytic particle layer 2, wherein , The activated carbon is selected to have a CTC of more than 60% and a particle size of 20-100 mesh activated carbon particles, and the mass percentage of catalyst components impregnated is 5%.

[0032] 3) The particle filtering layer 3 selects PP melt-blown filter paper with a filtration efficiency of 95%;

[0033] 4) Coating nano-silver copper bactericide slurry on the surface of PET non-woven fabr...

Embodiment 2

[0039] 1) Activated carbon fiber pre-filter layer 1 is composed of activated carbon fiber and non-woven fabric substrate in a mass ratio of 8:2, and the overall grammage is 50g / m 2 ;

[0040] 2) Adsorption catalytic particle layer 2 is activated carbon supported metal oxide MnO x Mix the Mn precursor manganese acetate tetrahydrate solution with activated carbon, impregnate and stir, impregnate for 24 hours, and then bake at 300°C for 30 minutes to obtain room temperature catalytic oxidation of formaldehyde catalyst particles, thus making adsorption catalytic particle layer 2 , wherein the activated carbon is selected to have a CTC of more than 60% and a particle size of 20-100 mesh activated carbon particles, and the impregnated mass percentage of the catalyst component is 10.0%.

[0041] 3) The particle filtering layer 3 selects PP melt-blown filter paper with a filtration efficiency of 95%;

[0042] 4) Coating nano-silver copper bactericide slurry on the surface of PET non...

Embodiment 3

[0048] 1) Activated carbon fiber pre-filter layer 1 is composed of activated carbon fiber and non-woven fabric substrate in a mass ratio of 4:6, and the overall grammage is 40g / m 2 ;

[0049] 2) Adsorption catalytic particle layer 2 is activated carbon supported metal oxide MnO x Mix the Mn precursor manganese nitrate solution with activated carbon, impregnate and stir, impregnate for 24 hours, and then bake at 300°C for 30 minutes to obtain room temperature catalytic oxidation of formaldehyde catalyst particles, thus making adsorption catalytic particle layer 2, wherein , The activated carbon adopts activated carbon particles with a CTC of more than 60% and a particle size of 20-100 meshes, and the mass percentage of catalyst components impregnated is 5.0%.

[0050] 3) The particle filtering layer 3 selects PP melt-blown filter paper with a filtration efficiency of 95%;

[0051] 4) Coating nano-silver copper bactericide slurry on the surface of PET non-woven fabric, through...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite air purifying filter paper material and a filter element using the same. The composite air purifying filter paper material comprises an active carbon fiber pre-filtering layer, an adsorption catalytic particle layer, a particulate matter filtering layer and a sterilizing supporting layer which are superposed according to any sequence. Compared with the existing filter paper material, the composite air purifying filter paper material is provided with the active carbon fiber pre-filtering layer; an air purifying filter element prepared from the composite air purifying filter paper material can significantly improve quick purification and adsorption performance on pollutant molecules, such as peculiar smell and the like, in the environment, and the removal rate of the whole filter element on gas-state pollutant molecules is increased.

Description

technical field [0001] The invention relates to a composite air purification filter paper material and a filter element using the same, belonging to the field of air purification. Background technique [0002] With the improvement of people's living standards, various new decoration materials are used in indoor home life, causing the problem of indoor environmental pollution to gradually intensify. Among many indoor pollutants, formaldehyde is one of the most serious gas pollutants. It is colorless and has a strong pungent smell. It has been identified as a strong carcinogenic and teratogenic substance by the World Health Organization (WHO). Studies have shown that the release cycle of formaldehyde is as long as three to fifteen years. my country's national indoor air quality standard stipulates that the hygienic standard for formaldehyde in the air of residential and office spaces is 0.10mg / m 3 (GB / T 18883-2002). Long-term exposure to low-dose formaldehyde can easily cau...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/14B01D46/12B01D53/04B01D53/86B01D53/44D21H27/08D21H27/30B32B9/00B32B9/04B32B9/06B32B27/36B32B27/10B32B33/00
CPCB01D39/14B01D46/0028B01D46/0036B01D46/0038B01D46/12B01D53/04B01D53/8687B01D2239/0407B01D2239/0442B01D2239/065B01D2253/102B01D2257/7027B01D2257/708B01D2257/90B01D2257/91B01D2258/06B32B9/00B32B9/047B32B9/06B32B27/10B32B27/36B32B33/00B32B2262/106B32B2307/7145D21H27/08D21H27/30
Inventor 刘智
Owner WUHU MATY AIR CONDITIONING EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products