High-flame-retardancy composite calcium carbonate and preparation method thereof

A composite calcium carbonate, high flame retardant technology, used in chemical instruments and methods, dyed polymer organic compound treatment, dyed organic silicon compound treatment, etc. problems, to achieve the effect of high application value, low production cost and stable quality

Inactive Publication Date: 2017-01-25
中玺新材料(安徽)有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the application field of calcium carbonate, most of the products belong to the category of polymers. However, the surface of calcium carbonate particles is distributed with strong hydrophilic hydroxyl groups, which is alkaline, and the interface properties of organic polymer matrix materials are different and compatible. It is difficult to disperse evenly in the matrix material and form a strong bonding force with the matrix material, resulting in interface defects between the two materials and reducing some mechanical properties of the composite material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A high flame-retardant composite calcium carbonate and a preparation method thereof, comprising the following raw materials in parts by weight: 50 parts of calcium carbonate, 2 parts of unsaturated polyester resin, 1 part of magnesium hydroxide, 1 part of kaolin, 3 parts of styrene, organic 4 parts of silicon-modified acrylic resin, 2 parts of glycerin, 1 part of pure benzene, 1 part of isobutanol, 5 parts of modifier, and an appropriate amount of water; wherein the modifier is made of the following raw materials in parts by weight: nano-dioxide 30 parts of silicon, 2 parts of iron and titanium powder, 3 parts of carbon fiber, 2 parts of silicon acrylic emulsion, 1 part of barium sulfate, 3 parts of sodium sulfite, 2 parts of isophorone;

[0018] Its preparation method comprises the following steps:

[0019] (1) Mix calcium carbonate, unsaturated polyester resin, magnesium hydroxide, and kaolin evenly into a sand mill, grind to 300-400 mesh, and obtain a premix for use;...

Embodiment 2

[0024] A high flame-retardant composite calcium carbonate and a preparation method thereof, comprising the following raw materials in parts by weight: 80 parts of calcium carbonate, 4 parts of unsaturated polyester resin, 3 parts of magnesium hydroxide, 3 parts of kaolin, 5 parts of styrene, organic 6 parts of silicon-modified acrylic resin, 3 parts of glycerin, 1.5 parts of pure benzene, 2 parts of isobutanol, 8 parts of modifier, and an appropriate amount of water; wherein the modifier is made of the following raw materials in parts by weight: nano-dioxide 50 parts of silicon, 4 parts of iron and titanium powder, 5 parts of carbon fiber, 5 parts of silicon acrylic emulsion, 3 parts of barium sulfate, 5 parts of sodium sulfite, 4 parts of isophorone;

[0025] Its preparation method comprises the following steps:

[0026] (1) Mix calcium carbonate, unsaturated polyester resin, magnesium hydroxide, and kaolin evenly into a sand mill, grind to 300-400 mesh, and obtain a premix f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-flame-retardancy composite calcium carbonate and a preparation method thereof; the high-flame-retardancy composite calcium carbonate is prepared from calcium carbonate, unsaturated polyester resin, magnesium hydroxide, kaolin, styrene, organosilicon-modified acrylic resin, glycerol, pure benzene, isobutanol, a modifier, and suitable water; the preparation method of the high-flame-retardancy composite calcium carbonate includes the steps of (1) preparing premix for use; (2) preparing a mixed liquid; (3) preparing a modifier; (4) mixing the premix, the mixed liquid and the modifier, stirring well, grinding, drying, and crushing to obtain superfine powder. By combining the calcium carbonate with materials having good comprehensive properties, such as styrene, unsaturated polyester resin, magnesium hydroxide and organosilicon-modified acrylic resin, the production process is modified; by using the modifier and the like, high flame retardancy of the composite is effectively improved; the production process is simple, the production cycle is short, the quality is stable, the production cost is low, and the high-flame-retardancy composite calcium carbonate and the preparation method are high in applicable value.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a highly flame-retardant composite calcium carbonate and a preparation method thereof. Background technique [0002] Calcium carbonate is an inorganic compound, CaCO 3 Commonly known as: limestone, limestone, stone powder, marble, etc., which are formed by the combination of calcium ions and carbonate ions, are an important class of functional inorganic fillers. It is easy to process and non-toxic, and can significantly improve the processing performance and physical properties of materials and reduce production costs. It is widely used in plastics, rubber, coatings, papermaking and other fields. [0003] In the application field of calcium carbonate, most of the products belong to the category of polymers. However, the surface of calcium carbonate particles is distributed with strong hydrophilic hydroxyl groups, which is alkaline, and the interface properties of organic polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09C1/02C09C3/04C09C3/06C09C3/08C09C3/10C09C3/12
CPCC09C1/022C09C3/006C09C3/041C09C3/043C09C3/06C09C3/08C09C3/10C09C3/12
Inventor 詹德军
Owner 中玺新材料(安徽)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products