Heat-resistant nylon 66 as-spun filament and indirect spinning method thereof, and application of as-spun filament in producing high-elasticity weft

A technology of winding yarn and nylon, which is applied in the field of weft yarn manufacturing, can solve the problems of easy loss or decomposition, elastic elongation and strength loss, difficult to grasp and operate, and achieve easy grasp and operation, low production cost, and satisfactory required effect

Inactive Publication Date: 2017-01-25
山东合信科技股份有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] (1) The existing nylon 66 winding yarn has poor heat resistance;
[0007] (2) The existing nylon 66 winding yarn has insufficient spinning fineness, low fiber strength and low fiber elongation;
[0008] (3) The existing nylon 66 winding yarn has poor mechanical properties, after heat treatment at 240°C, the elastic elongation and strength are lost, and the heat resistance is poor;
[0009] (4) The heat-resistant agent used in the existing nylon 66 winding yarn has poor stability and is prone to loss or decomposition;
[0010] (5) The existing production method of nylon 66 winding yarn is high in production cost, complicated in method, and difficult to master and operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1 A kind of heat-resistant nylon 66 winding yarn

[0041] The heat-resistant nylon 66 winding yarn includes copper acetate and potassium iodide, and the addition ratio of copper acetate and potassium iodide is 1.5:1, that is, 1:3.

Embodiment 2

[0042] Embodiment 2 A kind of heat-resistant nylon 66 winding yarn

[0043] The heat-resistant nylon 66 winding yarn includes copper acetate and potassium iodide, and the addition ratio of copper acetate and potassium iodide is 1:8.

Embodiment 3

[0044] Embodiment 3 A kind of heat-resistant nylon 66 winding yarn

[0045] The heat-resistant nylon 66 winding yarn includes copper acetate and potassium iodide, and the addition ratio of copper acetate and potassium iodide is 1:20.

[0046] Through repeated practice by the applicant, the various performance indicators of the ratio of raw materials used in embodiment 2 are better than those of embodiment 1 and embodiment 3, and embodiment 2 is the optimal embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides a heat-resistant nylon 66 as-spun filament which comprises nylon 66 and a heat-resistant agent in a ratio of (100-1000):1; and the heat-resistant agent comprises copper acetate and potassium iodide in a ratio of 1:(3-20). The invention also provides an indirect spinning method of the heat-resistant nylon 66 as-spun filament and application of the heat-resistant nylon 66 as-spun filament in producing high-elasticity weft. The production cost of the heat-resistant nylon 66 as-spun filament is greatly lowered; and the copper acetate has favorable heat stability in the polymerization or spinning process, and can not be lost or decomposed, so that the heat resistance is greatly enhanced. Thus, after the spun weft is subjected to 240-DEG C heat treatment for 3 minutes, the high power is 312cN, and the elongation percentage is 245%; and after gum dipping, the high power is greater than 295cN, and the elongation percentage is greater than 228%, thereby completely satisfying the requirements of the radial tire builder fabric for the elastic weft.

Description

technical field [0001] The present invention relates to a nylon winding yarn and its production method and its application in the production of weft yarn, in particular to a heat-resistant nylon 66 winding yarn and its indirect spinning method and its application in the production of high-strength elastic weft yarn, which belongs to weft yarn field of manufacturing technology. Background technique [0002] Cord fabric is a necessary skeleton material in tire production. The radialization of tires represents the latest level and development trend of today's tire industry, and elastic weft yarn is one of the important raw materials for producing radial tire cord fabrics. Ordinary cord fabrics use pure cotton yarns as weft yarns, which have low strength, small elongation, and poor elasticity. During the tire calendering process, the weft yarns are easily broken, causing the warp yarns to be scattered, affecting the quality of the tires, and cannot meet the requirements of high-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/10D02G3/32D02G3/04D01D5/08D01D10/02D01D11/00
CPCD01F6/90D01D5/08D01D10/02D01D11/00D01F1/10D02G3/04D02G3/32D10B2201/02D10B2331/02
Inventor 刘世春
Owner 山东合信科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products