Preparation method of antibacterial PVC polyester coated filament

A technology of covering silk and antioxidants, applied in the chemical post-treatment of synthetic polymer rayon filament, yarn, textiles and papermaking, etc., can solve the problems of many components and complicated processes, and achieve enhanced stiffness and saving. Energy resources, the effect of shortening processing time

Active Publication Date: 2017-02-08
浙江西大门新材料股份有限公司
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the polyester yarn used in curtain production achieves the purpose of coloring by coating the colorant on its surface. When antibacterial performance is required, a single antibacterial masterbatch is added to impart antibacterial performance, resulting in many processing components and complicated processes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The invention discloses a preparation method of antibacterial PVC polyester coated yarn, which mainly comprises two steps of preparing a masterbatch and coating the masterbatch with polyester yarn.

[0028] The preparation of color masterbatch comprises the following steps:

[0029] a, in parts by mass, weigh each component raw material;

[0030] b. Put the raw materials of each component into the high-speed mixer for high-speed mixing;

[0031] c. After stirring and cooling to 50 degrees, transfer to the hopper, and the hopper is sent into the main engine hopper through the conveying device;

[0032] d. Cut into particles by a granulator, that is, masterbatch.

[0033] The speed of high-speed mixing is 700-800 rpm.

[0034] The steps of polyester filament coating masterbatch are:

[0035] a. The filaments are put into the filament frame, passed through the tensioner positioning device into the mold, and the mold is loaded into the shunt

[0036] b. Put the masterb...

Embodiment 1

[0054] A kind of preparation method of antibacterial PVC polyester covering silk, comprises the following steps:

[0055] 1) Preparation of color masterbatch

[0056] a. In parts by mass, weigh the raw materials of the following components

[0057] 69 parts of polyvinyl chloride, 6 parts of pigment, 8 parts of dispersant, 4 parts of antioxidant, 5 parts of flame retardant, 8 parts of nano-zinc oxide surface grafted powder;

[0058] b. Put the raw materials of each component into the high-speed mixer for high-speed mixing;

[0059] c. After stirring and cooling to 50 degrees, transfer to the hopper, and the hopper is sent into the main engine hopper through the conveying device;

[0060] d. Cut into particles by a granulator, that is, masterbatch;

[0061] 2), coating

[0062] a. The filaments are put into the filament frame, passed through the tensioner positioning device into the mold, and the mold is loaded into the shunt

[0063] b. Put the masterbatch into the hopper,...

Embodiment 2

[0067] Preparation of nano zinc oxide surface graft powder:

[0068] a. Take 3 parts of silane coupling agent KH-570, 4 parts of tridecafluorooctyltrimethoxysilane, add 120 parts of ethanol; water = 4:1 aqueous solution of absolute ethanol, hydrolyze at room temperature for 1 hour; Add 14 parts of nano-zinc oxide dried at 120°C for 12 hours, add 30 parts of ethanol; water = 4:1 aqueous solution of absolute ethanol, ultrasonically disperse for 30 minutes; then mix the two into a flask, heat up to 80°C while stirring, and react for 12 hours After the reaction is finished, cool to room temperature, centrifuge the reactant at 4000r / min for 20min, and wash repeatedly with absolute ethanol to remove unreacted coupling agent; put it into a desiccator after fully drying in a vacuum oven to obtain surface-modified nano Zinc oxide white powder;

[0069] b. Take 10 parts of surface-modified nano-zinc oxide powder, add 84 parts of absolute ethanol, and ultrasonically disperse for 30 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an antibacterial PVC polyester coated filament. The method consists of: 1) color masterbatch preparation: weighing the following raw materials; putting the raw materials into a high-speed mixer to conduct high speed mixing; carrying out stirring cooling to 50DEG C, then transferring the mixture into a hopper, and sending the hopper into a host hopper by a conveying device; cutting the mixture into particles by a pelletizer, thus obtaining color masterbatch; 2) coating: putting polyester filament into a filament rack, penetrating a mold by a tensioner positioning device, and mounting the mold into a diverter; adding the color masterbatch into a hopper, carrying out heating plasticizing, then bringing the color masterbatch to the diverter by a host motor; letting a traction disc drive the polyester filament to perform coating through the diverter; and conducting cooling with cooling water, then bringing the filament into an automation line, performing detection, and then conducting rolling-up. The carrier resin with polyvinyl chloride as the color masterbatch is added with an antibacterial nano material, the polyester filament is colored, and is also endowed with good antibacterial properties. The stiffness handfeel of the polyester filament is enhanced, and the finishing process of additional application of a stiffening agent in a follow-up processing process of polyester window decorations can be eliminated.

Description

technical field [0001] The invention relates to a preparation method of an antibacterial PVC polyester coated yarn, which belongs to the field of coated yarns of synthetic fiber filaments. Background technique [0002] At present, the output of polyester fiber in my country exceeds 10 million tons, one third of which needs to be dyed. The dye dyeing method will discharge 40 million tons of colored sewage every year. The light fastness of dyeing, washing, perspiration, sublimation, etc. The fastness is far lower than that of pre-spinning coloring, and has not adapted to the needs of social development and improvement of people's living standards. Pre-spinning coloring of polyester is a new technology that melts or disperses color masterbatch in polyester spinning stock solution for melt spinning to directly produce colored polyester fibers. It is the most effective way to save polyester dyeing. [0003] With the improvement of people's living standards, people pay more and mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/10C08K13/02C08K3/22C08K5/098C08K5/03C08K5/523C08F292/00D01F11/08D02G3/04D02G3/36
CPCC08F292/00C08L27/06C08L2203/12D01F11/08D02G3/045D02G3/36D10B2321/041D10B2331/04C08L51/10C08K13/02C08K2003/2241C08K5/098C08K5/03C08K5/523
Inventor 沈华锋侯兵方王炜强柳建华严宝金李伦成
Owner 浙江西大门新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com