Milk-white environment-friendly type synthesis polymer steel roofing paint

A technology for synthesizing polymers and steel roofs, applied in anti-corrosion coatings, conductive coatings, reflective/signal coatings, etc., can solve the problems of permeability, poor adhesion, difficult to color, and many external dirt, etc., to achieve high resistance Good low temperature performance, excellent adhesion, good permeability

Inactive Publication Date: 2017-02-08
河南省治海建材有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention is mainly concerned with a waterproof material, and the protruding part of the steel structure roof has always been a headache for waterproofing. At present, the waterproof materials on the market, such as silica gel, APP and other coatings, are complex in construction, difficult to color, and poor in decorative effect. Poor permeability and adhesion, unstable product performance, short service life, containing a variety of harmful chemical agents, and can not solve the roof leakage problem well
In order to solve the above problems, the applicant applied for an invention patent with the patent name "milky white environment-friendly synthetic polymer waterproof coating" and the patent number "200610099088.2" in 2006. , anti-aging, direct painting, simple construction, and adjustable color, etc. However, after years of research, it has been found that this kind of coating can be used indoors, but when it is used for outdoor steel roof waterproofing, due to the changeable outdoor environment, the use environment is relatively difficult. Poor: It is windy and rainy, and there is a lot of dirt outside. This kind of coating has poor UV resistance and aging resistance outdoors. The product performance is not very stable. After a few years, the product performance is easily damaged and water leakage occurs again. It is urgent to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: Environment-friendly synthetic high polymer steel roof special coating, the raw materials are weighed according to the following parts by weight when the coating is made: 8 parts of polyolefin thermoplastic elastomers, 4 parts of aldehyde and ketone resins, 2 parts of styrene resins, 1 part of silicon powder 1 part of mica powder, 5 parts of rutile titanium dioxide, 1 part of antioxidant 1010, 0.3 part of antioxidant 1076, 1 part of antioxidant 531, 0.5 part of defoamer, 1 part of ultraviolet absorber 327, 5 parts of D40 solvent oil Parts, 30 parts of butyl solvent naphtha.

Embodiment 2

[0015] Embodiment 2: Environment-friendly synthetic high polymer steel roof special coating, the raw materials are taken by weighing the following parts by weight when the coating is made: 15 parts of polyolefin thermoplastic elastomers, 6 parts of aldehyde and ketone resins, 8 parts of styrene resins, 3 parts of silicon powder 5 parts of mica powder, 3 parts of rutile titanium dioxide, 0.7 parts of antioxidant 1010, 0.6 part of antioxidant 1076, 0.8 part of antioxidant 531, 1 part of defoamer, 0.8 part of ultraviolet absorber 327, 20 parts of D40 solvent oil Parts, 15 parts of butyl solvent naphtha.

Embodiment 3

[0016] Embodiment 3: Environment-friendly type synthetic polymer steel roof special coating, when this coating is made, take raw material by the following parts by weight:

[0017] 20 parts of polyolefin thermoplastic elastomer, 8 parts of aldehyde and ketone resin, 12 parts of styrene resin, 5 parts of silicon powder, 10 parts of mica powder, 1 part of rutile titanium dioxide, 0.3 parts of anti-aging agent 1010, 1 part of anti-aging agent 1076, anti-aging agent 0.3 parts of oxygen agent 531, 2.5 parts of defoamer, 0.3 parts of ultraviolet absorber 327, 5-30 parts of D40 solvent naphtha, 5-30 parts of butyl ester solvent naphtha.

[0018] The environment-friendly synthetic polymer steel roof special paint in the above examples is aimed at the use characteristics of steel roof waterproofing. The water leakage phenomenon of the steel structure color steel roof is particularly serious due to installation and construction, roof elastic deformation, roof vibration, etc., and the wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly type synthesis polymer steel roofing paint, which belongs to the field of waterproof construction. The paint comprises the following components: 8-20 parts of a polyolefin thermoplastic elastomer, 4-8 parts of aldehyde ketone resin, 2-12 parts of styrene resin, 1-5 parts of silicon powder, 1-10 parts of mica powder, 1-5 parts of rutile titanium dioxide, 0.3-1 part of an antioxidant 1010, 0.3-1 part of an antioxidant 1076, 0.3-1 part of an anti-oxidant 531, 0.5-2.5 parts of an antifoaming agent, 0.3-1 part of an ultraviolet ray absorber, 5-30 parts of D40 solvent naphtha, and 5-30 parts of butyiate solvent naphtha. The milk-white steel roofing waterproof paint has the characteristics of no toxicity, no harm, no pollution, no containing of noxious materials and harmful components such as pitch and benzene, and realization of free toning. The product performance is stable, the material service life can reach 30 years or more, and has the characteristics of strong adhesion stress, good penetration performance and good elongation percentage.

Description

technical field [0001] The invention relates to a building waterproof material, in particular to a milky white environment-friendly synthetic polymer steel roof special paint. Background technique [0002] Building waterproofing is a measure taken from the building materials and structure to prevent water from penetrating certain parts of the building. Waterproofing is mostly used in roofs, underground buildings, underground parts of buildings, inner chambers and water storage structures that need to be waterproofed. According to the different measures and means adopted, it can be divided into two categories: material waterproof and structural waterproof. The present invention is mainly concerned with a waterproof material, and the protruding part of the steel structure roof has always been a headache for waterproofing. At present, the waterproof materials on the market, such as silica gel, APP and other coatings, are complex in construction, difficult to color, and poor in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/00C09D161/02C09D125/04C09D7/12C09D5/24C09D5/33C09D5/08
CPCC09D123/00C08K2201/014C08L2201/04C08L2201/08C08L2205/03C09D5/004C09D5/08C09D5/24C08L61/02C08L25/04C08K13/02C08K3/34C08K2003/2241C08K5/1345
Inventor 王丽莉
Owner 河南省治海建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products