Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of oxide solid electrolyte diaphragm

A solid electrolyte and oxide technology, which is applied in the manufacture of electrolyte batteries, non-aqueous electrolyte batteries, electrolyte immobilization/gelation, etc., can solve problems such as easy damage and deformation, achieve flat and compact finished products, and reduce the chance of contamination , The effect of simple process

Active Publication Date: 2020-01-14
NO 63971 TROOPS PLA
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems of pre-pressing the diaphragm before sintering in the traditional solid-state method, easy deformation during the sintering process, and easy damage in the post-processing, etc., and provide a high ionic conductivity with simple process, flat and compact finished product, and easy scale-up Preparation method of oxide solid electrolyte separator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of oxide solid electrolyte diaphragm

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0014] First press Li 7 La 3 Zr 2 o 12 Proportioning, weigh lithium hydroxide (LiOH, excess 15%) 12.3135g, zirconium oxide (ZrO 2 ) 8.8930g, lanthanum oxide (La 2 o 3 ) 17.4594g, put it in a ball mill tank, add 20ml of absolute ethanol, the ball mill speed is 400 rpm, and ball mill for 10h; the obtained slurry is dried at 120°C for 10h, and then ground to obtain the primary oxide material; the primary material is placed in In the corundum crucible in the temperature-controlled furnace, the temperature was rapidly raised to 1150°C and kept for 10 hours; the raw material after high-temperature treatment was directly crushed and mixed evenly by grinding and ball milling, and LLZO powder was obtained after sieving with a 100-mesh sieve. The average particle size measured by laser particle size analyzer is 10.88 microns; the obtained powder is placed in a corundum crucible, placed in a temperature-controlled furnace, and sintered at a high temperature of 1150°C in air for 15 h...

example 2

[0016] Lithium carbonate (Li 2 CO 3 , excess 10%) 10.3704g, zirconia (ZrO2) 8.8930g, lanthanum oxide (La 2 o 3 ) 17.4594g and tantalum oxide (Ta 2 o 5 ) 1.0525g, put it in a ball mill jar, add 20ml of absolute ethanol, the ball mill speed is 400 rpm, and ball mill for 10h; the obtained slurry is dried at 120°C for 10h, and ground to obtain the primary oxide material; the primary material is placed in a control In the corundum crucible in the heating furnace, the temperature was rapidly raised to 1150°C and kept for 10 hours; the raw material after high temperature treatment was directly pulverized and mixed evenly by grinding, ball milling, etc., and LLZO powder was obtained after sieving with a 100-mesh sieve; The powder is placed in a corundum crucible, placed in a temperature-controlled furnace, and sintered at a high temperature of 1150°C in air for 20 hours to obtain a dense oxide solid electrolyte block; the block is cut into a thickness of 1.490mm by a table mill cu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
electrical conductivityaaaaaaaaaa
electrical conductivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an oxide solid electrolyte membrane, belonging to the fields of electrochemical engineering and ceramic industry. In this method, lithium carbonate or lithium hydroxide is used as a lithium source, the pre-prepared solid electrolyte powder is placed in a crucible, and directly sintered at high temperature to obtain a dense block; the block is cut and polished to obtain a solid electrolyte diaphragm Flakes. This method avoids the complicated mold pressing process in the conventional method. First, the mechanical energy is converted into the surface free energy of the powder particles through ball milling, and then the excessive low melting point lithium salt is melted at high temperature to form a liquid phase covering the surface of the powder particles. , Under the action of surface tension, the powder is automatically agglomerated, the surface free energy is reduced, and a dense solid electrolyte block is formed. The method has the advantages of simple process, smooth and dense finished product, easy scale-up, etc., and is especially suitable for the preparation of oxide solid electrolyte diaphragms in solid-state secondary batteries.

Description

technical field [0001] The invention relates to a preparation method of an oxide solid electrolyte diaphragm, which belongs to the fields of electrochemical engineering and ceramic industry. Background technique [0002] Due to the use of organic electrolytes in traditional lithium-ion batteries, there are potential dangers such as combustion and explosion. The new generation of lithium-ion batteries, the so-called "all-solid-state batteries", uses solid electrolytes instead of flammable organic electrolytes, which fundamentally solves the safety problem of batteries. Solid electrolytes can be broadly classified into polymers and inorganic substances. High molecular polymers have low ionic conductivity at room temperature, making it difficult to apply in all-solid-state batteries. Although inorganic solid electrolytes are difficult to produce on a large scale, they have high ionic conductivity, good selectivity, and long service life, and have become the mainstream of rese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/14H01M10/058H01M50/403
CPCH01M10/058H01M2300/0085H01M50/403Y02E60/10Y02P70/50
Inventor 赵鹏程曹高萍文越华徐艳程杰
Owner NO 63971 TROOPS PLA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More