Anti-cracking treatment method for rattan

A treatment method, rattan technology, applied in wood treatment, electric wood treatment, wood treatment details, etc., can solve the problems that rattan cannot keep its original color, consumes a lot of energy, and is easy to crack, so as to improve the anti-mildew effect and reduce The effect of cracking rate and easy processing and molding

Inactive Publication Date: 2017-02-15
阜南县环宇柳木工艺制品有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, rattan has high strength and toughness, and is very suitable as a raw material for wicker. Rattan is the main raw material. The fresh rattan that has just been felled cannot be used directly, and it needs to be treated before it can be used. In the prior art, high temperature is usually used. The treatment method consumes a lot of energy, and the treated rattan cannot keep its original color, and it is easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] A rattan anti-cracking treatment method, comprising the following steps:

[0017] (1) Put the rattan in an environment with an ambient humidity of 65-68%, a temperature of 8-10°C, and no light for 48 hours. When it is placed for the 20th hour, it will be given the first light for 4 hours at the same time. At 40 hours, give the second light for 5 hours at the same time, and the light intensity of the two times is 800 lux; through this treatment, the toughness and tightness of rattan fibers can be greatly improved, and it can effectively prevent peeling of rattan and prevent weaving. When the rattan breaks or cracks;

[0018] (2) Place the treated rattan in warm water at 38-40°C for 2-4 hours, take it out, cool it to room temperature naturally, and then refrigerate it at 1°C for 6 hours; it can keep the rattan in its original color and improve The stability of the primary color of the rattan surface;

[0019] (3) dissolving chitosan in saturated carbon dioxide aqueous s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-cracking treatment method for a rattan. The method comprises the following steps: treating the rattan in a dark environment of which the humidity is 65% to 68% and the temperature is 8 to 10 DEG C, and irradiating twice; subsequently soaking the rattan in warm water and putting in cold storage; dissolving chitosan in a saturated carbon dioxide water solution to prepare a solution for soaking the rattan; and treating the rattan by utilizing low-temperature plasma generated by dielectric barrier discharge at atmospheric pressure. In comparison with an existing rattan treatment method, the method disclosed by the invention has the advantages that a knitted product made from the rattan treated by the method disclosed by the invention is not deformed, free of cracks and very comfortable to skin in use; the bearing capacity is increased; the dimensional stability is good; decrustation of the rattan can be effectively prevented; after the rattan is knitted, the strength of the rattan is gradually restored and is increased by 2% to 3% in comparison with the original strength; the treated rattan is quite good in corrosion prevention effect, good in rattan softening effect and harder to mildew and damage in use; the knitted product prepared by the rattan treated by the method disclosed by the invention is free of mildew and worm damages and can be kept in the original color within at least 8 years.

Description

technical field [0001] The invention relates to the field of wicker treatment, in particular to a rattan anti-crack treatment method. Background technique [0002] A vine with tough, extremely long stature. The outer skin of the rattan is smooth in color, smooth to the touch, and has excellent elasticity, which seems contemptuous but not contemptuous. It is also commonly used to weave rattan baskets, rattan boxes and other daily utensils. Among them, rattan has high strength and toughness, and is very suitable as a raw material for wicker. Rattan is the main raw material. The fresh rattan that has just been felled cannot be used directly, and it needs to be treated before it can be used. In the prior art, high temperature is usually used. The treatment method consumes a lot of energy, and the treated rattan cannot keep its original color, and it is easy to crack. Contents of the invention [0003] In order to overcome the above-mentioned deficiencies, the invention prov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K9/00B27K5/00B27K3/02B27K3/52B27K5/06
CPCB27K9/002B27K3/02B27K3/52B27K5/00B27K5/002B27K5/06B27K2240/20
Inventor 徐学朋
Owner 阜南县环宇柳木工艺制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap