A waterproof sealing and airtight technology, applied in chemical instruments and methods, adhesives, other chemical processes, etc., can solve the problems affecting the perspective of insulating glass, self-explosion, shortened service life, etc., and is suitable for large-scale industrial application. Good application prospect and good airtight performance

Inactive Publication Date: 2017-02-22
张德轩
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Condensation or frost on the inner surface of the glass will seriously affect the perspective of the insulating glass and reduce the heat insulation performance of the insulating glass. At the same time, long-term condensation or frost will cause mildew on the inner surface of the glass and cause white spots
At present, the service life of domestic insulating glass is greatly shortened due to some technical problems. Some products will frequently appear fogging, condensation, frosting, and self-explosion. These phenomena lead to the durability, safety, heat insulation, and sound insulation of insulating glass. discount

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Weigh 15 parts of polydimethylsilane, 7 parts of polyisobutylene, 6 parts of 3-hydroxybutyronitrile, 4 parts of vinyl triethoxysilane, and 3 parts of (γ-aminopropyl) triethoxysilane , 2 parts of bis(3-triethoxysilylpropyl) tetrasulfide, 2 parts of polydimethylsiloxane, 1 part of trimethylsilane, 3 parts of vinyltrimethoxysilane, 1 part of borosilicate , 3 parts of allyl orthosilicate, 5 parts of methyl p-isopropoxybenzoate, 3 parts of 2-ethylacryloyl chloride, 5 parts of sodium metaaluminate, 4 parts of di-isooctyl phthalate;

[0021] (2) Add polydimethylsilane, polyisobutylene, 3-hydroxybutyronitrile, and vinyltriethoxysilane into a high-speed mixer to preheat to 110°C, stir and mix for 15 minutes at a stirring speed of 1500 rpm, and then Add (γ-aminopropyl) triethoxysilane, bis(3-triethoxysilylpropyl) tetrasulfide, polydimethylsiloxane, and trimethylsilane in sequence, vacuumize, and sinter in vacuum. The sintering temperature is 450° C., and the sintering time i...

Embodiment 2

[0028] (1) Weigh 18 parts of polydimethylsilane, 10 parts of polyisobutylene, 9 parts of 3-hydroxybutyronitrile, 5 parts of vinyltriethoxysilane, and 4 parts of (γ-aminopropyl) triethoxysilane , 2 parts of bis(3-triethoxysilylpropyl) tetrasulfide, 3 parts of polydimethylsiloxane, 2 parts of trimethylsilane, 4 parts of vinyltrimethoxysilane, 2 parts of borosilicate , 4 parts of allyl orthosilicate, 7 parts of methyl p-isopropoxybenzoate, 4 parts of 2-ethylacryloyl chloride, 6 parts of potassium pyroantimonate, 5 parts of diethyl phthalate;

[0029] (2) Add polydimethylsilane, polyisobutylene, 3-hydroxybutyronitrile, and vinyltriethoxysilane into a high-speed mixer to preheat to 110°C, stir and mix for 15 minutes at a stirring speed of 1700 rpm, and then Add (γ-aminopropyl) triethoxysilane, bis(3-triethoxysilylpropyl) tetrasulfide, polydimethylsiloxane, and trimethylsilane in sequence, vacuumize, and sinter in vacuum. The sintering temperature is 500° C., and the sintering time...

Embodiment 3

[0036] (1) Weigh 22 parts of polydimethylsilane, 13 parts of polyisobutylene, 11 parts of 3-hydroxybutyronitrile, 7 parts of vinyl triethoxysilane, and 5 parts of (γ-aminopropyl) triethoxysilane , 3 parts of bis(3-triethoxysilylpropyl) tetrasulfide, 3 parts of polydimethylsiloxane, 2 parts of trimethylsilane, 5 parts of vinyltrimethoxysilane, 2 parts of borosilicate , 6 parts of allyl orthosilicate, 9 parts of methyl p-isopropoxybenzoate, 4 parts of 2-ethylacryloyl chloride, 7 parts of aluminum sulfate, 5 parts of dioctyl adipate;

[0037] (2) Add polydimethylsilane, polyisobutylene, 3-hydroxybutyronitrile, and vinyltriethoxysilane into a high-speed mixer to preheat to 110°C, stir and mix for 15 minutes at a stirring speed of 1900 rpm, and then Add (γ-aminopropyl) triethoxysilane, bis(3-triethoxysilylpropyl) tetrasulfide, polydimethylsiloxane, and trimethylsilane in sequence, vacuumize, and sinter in vacuum. The sintering temperature is 550° C., and the sintering time is 5 ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-leakproofness waterproof sealant for hollow glass. The sealant is prepared from, by weight, 15-25 parts of polydimethylsilane, 7-15 parts of polyisobutene, 6-13 parts of 3-hydroxyl butyronitrile, 4-9 parts of vinyl triethoxy silane, 3-6 parts of (gamma-aminopropyl)triethoxy silane, 2-3 parts of di(3-triethoxysilylpropyl)tetrasulfide, 2-4 parts of polydimethylsiloxane, 1-3 parts of trimethyl silicane, 3-6 parts of vinyl trimethoxy silane, 1-3 parts of borosilicate, 3-7 parts of allyl orthosilicate, 5-10 parts of p-isopropoxy methyl benzoate, 3-5 parts of 2-ethyl acryloyl chloride, 5-8 parts of crosslinking agent and 4-6 parts of plasticizer. The prepared high-leakproofness waterproof sealant for the hollow glass is good in leakproofness and has waterproofness. Meanwhile, the invention further discloses a corresponding preparation method.

Description

technical field [0001] The invention relates to the technical field of insulating glass, in particular to a highly airtight waterproof sealant for insulating glass and a preparation method thereof. Background technique [0002] As a high-efficiency energy-saving product, insulating glass has been widely used in buildings. In other industries such as railway transportation, the amount of refrigeration industry is gradually increasing. Insulating glass consists of two or more pieces of glass, separated by a spacer and sealed with a sealant to form a glass processing product with a dry gas space between the glasses. The hollow glass has a dry gas or inert gas in the cavity and cannot communicate with the outside world. The gas is convected, thus playing a good heat insulation effect. However, when the ambient temperature is reduced to such that the temperature of the glass surface is lower than the dew point of the gas in the air layer, the water vapor in the air layer will c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J183/16C09J123/20C09J151/08C09J11/04C09J11/06C09K3/10
CPCC09J183/16C08L2205/02C08L2205/035C09J11/04C09J11/06C09K3/10C09K2003/1081C08L83/04C08L23/22C08L51/08C08K13/02C08K5/11C08K5/12C08K3/38C08K3/24
Inventor 张德轩
Owner 张德轩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap