Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Compound oil paint flocculating agent where bacterial cellulose shell-core structures are added

A technology of bacterial cellulose and shell-core structure, applied in flocculation/sedimentation water/sewage treatment, water/sludge/sewage treatment, biological water/sewage treatment, etc., can solve problems such as poor effect and achieve good reactivity , Improve flocculation activity, improve the effect of adsorption

Inactive Publication Date: 2017-04-26
TIANCHANG YINHU PAINT
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Yang Shuangshuang obtained a better flocculation strain FL-2 through a series of separation and screening in the article "Study on the Flocculation of Paint Wastewater by Microbial Flocculants". The culture conditions are 30°C, pH 9, shaker speed 160r / min, the carbon source of the culture medium is glucose, the mixed nitrogen source is sodium nitrate, ammonium chloride and urea, the inorganic salt is magnesium sulfate, and gelatin Good flocculation effect was achieved when Bacillus frozen sample was mixed, but the effect was not good when the two kinds of microorganisms were mixed with inorganic flocculants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A kind of compound paint flocculant that adds bacterial cellulose shell-core structure, comprises the following steps:

[0023] (1) Separation and purification of strains

[0024] Put the paint wastewater in the later stage of treatment into a sterile Erlenmeyer flask, store it at 4°C, and sterilize the seed culture at 121°C. After cooling, take 100 μL of wastewater and inoculate it into 100ml of seed medium, and expand at a constant temperature of 37°C. Cultivate for 24 hours, then dilute the culture solution to 10, 10, 10, 10, 10, and 10 times respectively, and then spread each diluted bacterial suspension on the separation medium, culture at a constant temperature of 37°C for 24 hours, and pick out the cells with good morphology. After the initial isolation of the colonies, the selected bacteria were inoculated in the seed medium, incubated at a constant temperature of 37°C for 24 hours, the culture solution of each bacteria was diluted, separated and purified by str...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compound oil paint flocculating agent where bacterial cellulose shell-core structures are added. The following steps including the first step of strain separation and purification, the second step of strain screening, the third step of strain fermentation and cultivation and the fourth step of compound magnetic microsphere preparation are included. The preparation process is simple, the compound oil paint flocculating agent can be suitable for industrialized large-scale production, can be repeatedly used and can reduce cost, the problems that the flocculating efficiency is poor and sediment sinks in circulating water are effectively solved, and the long-term effective safe operation of the circulating water is ensured.

Description

technical field [0001] The invention relates to the technical field of paint flocculants, in particular to a composite paint flocculant added with bacterial cellulose shell-core structure. Background technique [0002] With the development of the automobile industry and furniture manufacturing industry, the amount of spray paint is increasing, so there will be a lot of paint mist that cannot be applied to the workpiece and become "overspray" paint, and the amount of overspray reaches 25-60 %. These coatings contain a large amount of volatile organic solvents, which endanger human health and seriously pollute the surrounding environment and air. Spraying is a process in which the paint is evenly dispersed into fine particles through a spray gun or a disc atomizer under pressure or centrifugal force, and finally the paint mist particles are applied to the surface of the object. The oversprayed paint mist usually enters the circulating water, and the circulating water is take...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F3/34C02F1/52C02F1/28C02F1/48C02F103/14
CPCC02F1/28C02F1/48C02F1/52C02F3/34C02F2103/14
Inventor 祝盆鑫祝秀凤汪鹏程孙巨福戴宇钧
Owner TIANCHANG YINHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products