Heat insulation and heat preservation coating for building external wall and preparation method thereof

A technology for heat insulation and building exterior walls, applied in the direction of anti-corrosion coatings, fire-proof coatings, reflection/signal coatings, etc., can solve the problems that are not very mature, and achieve the effects of inhibiting absorption, improving thermal insulation performance, inhibiting radiant heat and conducting heat Effect

Inactive Publication Date: 2017-04-26
广西宾阳县荣良农业科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, there is no mature technology to prepare a light-weight, high fire-resistant, high-weather-resistant, environmentally friendly, non-aging, and long-lasting external thermal insulation coating to achieve the purpose of building energy saving. Continuous research and experimentation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] First, 40 parts of emulsion (a mixture of A-102 silicone acrylic emulsion and A-99 pure acrylic emulsion, the ratio of the two parts by weight is 1.5:1), 1 part of N-methylol acrylamide, 6 parts of fumed silica, 4 parts of water, 1 part of titanate coupling agent (monoalkoxypyrophosphate titanate coupling agent), 7 parts of auxiliary agent (1 part of dithiocarbamate , 1 part cellulose acetate butyrate, 1 part hydroxyethyl cellulose, 4 parts 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate), 7 parts n-butyl acetate, 9 parts of expanded perlite and 5 parts of nanometer calcium carbonate are prepared.

[0039] A kind of thermal insulation paint for building exterior wall, its production method comprises the following steps:

[0040] (1) Add the formulated amount of water and the formulated amount of additives in sequence in the mixer, start stirring, the rotating speed is 1000-1200 rpm, and disperse at high speed for 5-10 minutes;

[0041] (2) Dissolve the titanate coupli...

Embodiment 2

[0044] First, 45 parts of emulsion (a mixture of A-102 silicone acrylic emulsion and A-99 pure acrylic emulsion, the ratio of the two parts by weight is 1.5:1), 1.5 parts of N-methylol acrylamide, 7 parts of fumed silica, 5 parts of water, 1.5 parts of titanate coupling agent (monoalkoxypyrophosphate titanate coupling agent), 12 parts of additives (1.5 parts of pentachlorophenol, 2 parts of acetic acid Cellulose butyrate, 2 parts hydroxyethylcellulose, 5 parts 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate), 8 parts n-butyl acetate, 10 parts expanded pearl Rock, 8 parts of nanometer calcium carbonate, carry out material preparation.

[0045] A kind of thermal insulation paint for building exterior wall, its production method comprises the following steps:

[0046] (1) Add the formulated amount of water and the formulated amount of additives in sequence in the mixer, start stirring, the rotating speed is 1000-1200 rpm, and disperse at high speed for 5-10 minutes;

[0047] (2...

Embodiment 3

[0050] First, 50 parts of emulsion (a mixture of A-102 silicone acrylic emulsion and A-99 pure acrylic emulsion, the ratio of the two parts by weight is 1.5:1), 2 parts of N-methylol acrylamide, 9 parts of fumed silica, 6 parts of water, 2 parts of titanate coupling agent (monoalkoxypyrophosphate titanate coupling agent), 14 parts of auxiliary agent (2 parts of dithiocarbamate , 3 parts cellulose acetate butyrate, 3 parts hydroxyethyl cellulose, 6 parts 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate), 9 parts n-butyl acetate, 12 parts of expanded perlite and 10 parts of nanometer calcium carbonate are prepared.

[0051] A kind of thermal insulation paint for building exterior wall, its production method comprises the following steps:

[0052] (1) Add the formulated amount of water and the formulated amount of additives in sequence in the mixer, start stirring, the rotating speed is 1000-1200 rpm, and disperse at high speed for 5-10 minutes;

[0053](2) Dissolve the titanate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a heat insulation and heat preservation coating for a building external wall. The coating is prepared from 40-50 parts of emulsion, 1-2 parts of N-hydroxymethyl acrylamide, 6-9 parts of fumed silica, 4-6 parts of water, 1-2 parts of a titanate coupling agent, 7-14 parts of auxiliaries, 7-9 parts of acetic acid n-butyl ester, 9-12 parts of expanded perlite and 5-10 parts of nano-calcium carbonate, wherein the emulsion is mixed liquid prepared from A-102 silicone-acrylate emulsion and A-99 pure acrylic emulsion according to the weight ratio of 1.5:1, and the auxiliaries are composed of, by weight, 1-2 parts of a sterilizing and mildew preventing agent, 1-3 parts of a leveling agent, 1-3 parts of a thickening agent and 4-6 parts of a film forming aid. The coating has the advantages of being high in chemical resistance, good in weather resistance and heat insulation and heat preservation effect, high in glossiness, long in coating film life and the like.

Description

technical field [0001] The invention relates to a thermal insulation coating, in particular to a thermal insulation coating for building exterior walls and a preparation method thereof, belonging to the technical field of chemical composition and its preparation. Background technique [0002] Due to the increasingly developed world industry and the destruction of nature by humans, energy conservation and consumption reduction has attracted the attention and attention of countries all over the world. my country's building energy consumption accounts for more than 30% of human energy consumption. Improve the thermal insulation performance of buildings and improve The use function of buildings, energy saving and consumption reduction are another important considerations in the design of building material selection. In the field of architectural coatings, the development goals at home and abroad are also developing in the direction of high efficiency, energy and resource saving, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D5/33C09D5/32C09D5/18C09D5/08C09D5/14C09D7/12C09D7/06C09D7/00C09D7/47
CPCC09D4/06C09D5/004C09D5/08C09D5/14C09D5/18C09D5/32C09D7/20C09D7/47C09D7/61C09D7/62C09D7/63C09D7/65C09D7/67C09D7/70
Inventor 陈明贤谢彤
Owner 广西宾阳县荣良农业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap