Machining method for high-strength and high-abrasion-resistance stainless steel cold-rolled sheet

A processing method and technology for stainless steel plates, applied in metal processing equipment, manufacturing tools, metal rolling, etc., can solve the problems of uneven color of the plate surface, low added value, poor wear resistance, etc., and achieve high mechanical strength, electrolytic Uniform passivation and good wear resistance

Inactive Publication Date: 2017-05-24
ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The stainless steel cold-rolled plate produced by this process has uneven color on the surface of the plate and weak corrosion resistance. In addition, the surface of the plate is relatively rough, the added value is not high, the wear resistance is poor, and the strength is reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for processing a high-strength and high-wear-resistant stainless steel cold-rolled plate, using the following steps for processing:

[0027] (1) Raw material processing

[0028] Use a cleaning agent made of 2.3% sodium phosphate, 1.2% polyoxyethylene stearate, 5.5% sodium carbonate, and the rest as water to clean the surface of the stainless steel plate for 10 minutes, and then clean the stainless steel plate. Plates were dried at 80°C;

[0029] (2), rolling

[0030] When cold rolling starts, the temperature of the inlet stainless steel plate is kept at 50°C, and the emulsion is sprayed on the stainless steel plate during the cold rolling process. During the process, the temperature of the stainless steel plate was maintained at 48°C; the emulsion was made of the following components in parts by weight: suberic acid 3, cyclohexyl alcohol 0.2, lanolin 6, camellia seed oil 2, sodium tetraborate 3, Diacetyl tartaric acid monoglyceride 1, purified water 80;

[...

Embodiment 2

[0042] A method for processing a high-strength and high-wear-resistant stainless steel cold-rolled plate, using the following steps for processing:

[0043] (1) Raw material processing

[0044] Use a cleaning agent made of 2.5% sodium phosphate, 1.6% polyoxyethylene stearate, 5.8% sodium carbonate, and the rest as water to clean the surface of the stainless steel plate for 10 minutes, and then clean the stainless steel plate. Plates were dried at 80°C;

[0045] (2), rolling

[0046] When cold rolling starts, the temperature of the inlet stainless steel plate is kept at 50°C, and the emulsion is sprayed on the stainless steel plate during the cold rolling process. During the process, the temperature of the stainless steel plate was maintained at 48°C; the emulsion was made of the following ingredients in parts by weight: 5 suberic acid, 0.5 cyclohexanol, 8 lanolin, 6 camellia seed oil, 6 sodium tetraborate, Diacetyl tartrate monoglyceride 3, purified water 90;

[0047] (3),...

Embodiment 3

[0058] A method for processing a high-strength and high-wear-resistant stainless steel cold-rolled plate, using the following steps for processing:

[0059] (1) Raw material processing

[0060] Use a cleaning agent made of 2.4% sodium phosphate, 1.3% polyoxyethylene stearate, 5.6% sodium carbonate, and the rest as water to clean the surface of the stainless steel plate for 10 minutes, and then clean the stainless steel plate. Plates were dried at 80°C;

[0061] (2), rolling

[0062] When cold rolling starts, the temperature of the inlet stainless steel plate is kept at 50°C, and the emulsion is sprayed on the stainless steel plate during the cold rolling process. During the process, the temperature of the stainless steel plate was maintained at 48°C; the emulsion was made of the following components in parts by weight: suberic acid 4, cyclohexyl alcohol 0.3, lanolin 7, camellia seed oil 4, sodium tetraborate 5, Diacetyl tartrate monoglyceride 2, purified water 85;

[0063]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a machining method for a high-strength and high-abrasion-resistance stainless steel cold-rolled sheet. The machining method comprises the first step of raw material treatment, the second step of rolling, the third step of annealing and acid pickling, the fourth step of polishing and grinding and the fifth step of electrolysis passivation. The stainless steel cold-rolled sheet manufactured through the machining method is high in mechanical strength, good in abrasion resistance, strong acid and strong alkalinity resistance, high-temperature stability and machining performance, and the like. The sheet face is flat, colors are uniform, the surface appearance quality is greatly improved, more uniformity is achieved through electrolysis passivation, the density of a passivation layer is high, and the anti-corrosion capability of the stainless steel cold-rolled sheet can be greatly improved; and the surface can prevent oil dirt, and the dirt preventing and fingerprint pressing preventing capability of the surface of the stainless steel cold-rolled sheet is improved.

Description

technical field [0001] The invention relates to the field of stainless steel processing, in particular to a processing method for a high-strength and high-wear-resistant stainless steel cold-rolled plate. Background technique [0002] Since the production process of stainless steel cold-rolled sheets is not heated, there are no defects such as pits and scales that often occur in hot rolling, and the surface quality is good and the finish is high. Moreover, the dimensional accuracy of cold-rolled products is high, and the performance and structure of the products can meet some special requirements for use, such as electromagnetic properties and deep drawing properties. [0003] Cold-rolled strips are widely used, such as automobile manufacturing, electrical products, rolling stock, aviation, precision instruments, food cans, etc. [0004] China is currently the largest consumer and producer of stainless steel in the world. According to statistics from the China Stainless Ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D8/02C25D11/36C23G1/00B21B45/02
CPCC21D8/0273B21B45/0239B21B45/0242C23G1/00C25D11/36
Inventor 洪功正潘永刚蔡永波
Owner ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com