Environment-friendly fluorine-carbon corrosion-prevention coating and preparation method thereof

An anti-corrosion coating, an environmentally friendly technology, applied in the direction of anti-corrosion coatings, coatings, etc., to achieve the effect of high hardness, good toughness, and fast drying speed

Inactive Publication Date: 2017-06-13
GUANGZHOU JULAN HEALTH IND RES INST CO LTD
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on the preparation of acrylic modified fluorocarbon coatings by modifying fluorocarbon coatings with a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly fluorine-carbon corrosion-prevention coating and preparation method thereof
  • Environment-friendly fluorine-carbon corrosion-prevention coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An environment-friendly fluorocarbon anti-corrosion coating, the coating is composed of the following components in parts by weight: 90 parts of acrylic modified fluorocarbon resin emulsion, 3 parts of propynyl alcohol auxiliary agent, 5 parts of graphene oxide powder Parts, 8 parts of nano-silica powder, 12 parts of film-forming agent polyethylene glycol, 5 parts of salt spray agent ZT-719 salt spray agent, 9 parts of pigment zinc aluminum phosphate, 12 parts of talcum powder, deionized water 70 servings.

Embodiment 2

[0021] An environment-friendly fluorocarbon anti-corrosion coating, the coating is composed of the following components in parts by weight: 80 parts of acrylic modified fluorocarbon resin emulsion, 2 parts of propynyl alcohol additives, 3 parts of graphene oxide powder 6 parts, 6 parts of nano-silica powder, 10 parts of film-forming aid propylene glycol phenyl ether, 3 parts of salt spray resistant agent ZT-719, 6 parts of pigment zinc phosphosilicate, 5 parts of talcum powder, deionized water 50 servings.

Embodiment 3

[0023] An environment-friendly fluorocarbon anticorrosion coating, the coating is composed of the following components in parts by weight: 100 parts of acrylic modified fluorocarbon resin emulsion, 4 parts of acetylenic alcohol auxiliary agent pentynyl alcohol, 6 parts of graphene oxide powder 10 parts of nano-silica powder, 15 parts of ethylene glycol butyl ether as a film-forming aid, 7 parts of salt-spray resistant agent ZT-719 salt-spray resistant agent, 12 parts of pigment zinc phosphosilicate, 15 parts of talcum powder, 80 parts of ionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides environment-friendly fluorine-carbon corrosion-prevention coating. The environment-friendly fluorine-carbon corrosion-prevention coating is prepared from the following components in parts by weight: 80-100 parts of acrylic modified fluorine-carbon resin emulsion, 2-4 parts of an alkynol auxiliary agent, 3-6 parts of graphene oxide powder, 6-10 parts of nano silicon dioxide powder, 10-15 parts of a film forming auxiliary agent, 3-7 parts of a salt mist resisting agent, 6-12 parts of a pigment, 5-15 parts of talcum powder and 50-80 parts of de-ionized water. The product provided by the invention has extremely high adhesive force; the binding force between a coating layer and a matrix is high; in a coating composition, a dense interface transition layer is formed by the coating layer with the help of a metal oxide nano material and graphene powder, so that the comprehensive thermodynamic property of the coating is matched with the matrix; and the coating can be sprayed and molded on any curve surface, any inclined surface and any vertical plane and does not have a sagging phenomenon.

Description

technical field [0001] The invention belongs to the field of water-based coatings, in particular to an environment-friendly fluorocarbon anticorrosion coating and a preparation method thereof. Background technique [0002] Environmental problems are becoming more and more serious in today's world. A large amount of harmful substances are released during the processing and production of coatings, which will cause environmental pollution and damage the health of construction workers. In order to control pollution and protect the health of construction workers, my country has formulated a series of measures to limit the use of high VOC coatings. Therefore, environmentally friendly anti-corrosion coatings have become the focus of coating development. Among many environmentally friendly coatings, water-based coatings are an important direction of development. However, there are still some technical problems in the current water-based coatings, so improving the corrosion resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D151/00C09D5/08C09D7/12
CPCC09D151/003C08K3/04C08K3/34C08K3/36C08K5/05C08K13/06C08K2201/011C09D5/08C09D7/61C09D7/63C08L71/02
Inventor 杨凯
Owner GUANGZHOU JULAN HEALTH IND RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap