Texturization method of monocrystalline silicon wafer

A single-crystal silicon wafer, texturing technology, applied in chemical instruments and methods, crystal growth, final product manufacturing, etc., can solve problems such as wide distribution, and achieve the effects of small size, cost reduction, and narrow distribution

Inactive Publication Date: 2017-06-13
DEQING LIJING ENERGY TECH CO LTD
View PDF18 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The size of the pyramids prepared by the conventional

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1

[0016] The process steps are as follows:

[0017] 1. Configuration of texturing additives: 0.05g sodium perfluorooctyl sulfonate, 1g polyvinylpyrrolidone, 0.5g acrylic acid-maleic anhydride copolymer, 5g propylene glycol methyl ether, 0.1g sodium benzoate and 0.25g p-toluenesulfonic acid Sodium was dissolved in 100ml of deionized water in turn.

[0018] 2. Configure lye: dissolve 10g of sodium hydroxide in 990g of deionized water to obtain a 1% aqueous solution of sodium hydroxide.

[0019] 3. Configure alkaline texturing liquid: mix the texturing additive obtained in step 1 and the lye obtained in step 2 with a mass ratio of 0.5:100.

[0020] 4. Texturing process: immerse the monocrystalline silicon wafers for solar cells in the alkaline texturing liquid prepared in step 3 for surface texturing, the texturing temperature is 85°C, and the texturing time is 900s.

[0021] The formed pyramids are small in size, about 0.8-2μm, and have a narrow distribution. In addition...

Example Embodiment

[0022] Example 2

[0023] The process steps are as follows:

[0024] 1. Configure texturing additives: Dissolve 0.1g sodium perfluorooctanoate, 5g polyvinylpyrrolidone, 1g acrylic acid-maleic anhydride copolymer, 3g propylene glycol methyl ether, 0.2g sodium benzoate and 0.5g sodium p-toluenesulfonate to 100ml in turn Ionized water.

[0025] 2. Configure lye: Dissolve 15 g of potassium hydroxide in 985 g of deionized water to obtain a potassium hydroxide aqueous solution with a concentration of 1.5%.

[0026] 3. Configure alkaline texturing liquid: mix the texturing additive obtained in step 1 and the lye obtained in step 2 at a mass ratio of 1:100.

[0027] 4. Texturing process: immerse the monocrystalline silicon wafers for solar cells in the alkaline texturing liquid prepared in step 3 for surface texturing, the texturing temperature is 80°C, and the texturing time is 1200s.

Example Embodiment

[0028] Example 3

[0029] The process steps are as follows:

[0030] 1. Configure texturing additives: 0.2g sodium perfluorononenoxybenzene sulfonate, 0.3g perfluorooctylsulfonyl diethanolamine, 1g polyvinylpyrrolidone, 0.1g acrylic acid-maleic anhydride copolymer, 2g propylene glycol Methyl ether, 0.2g sodium benzoate and 2g sodium p-toluenesulfonate were sequentially dissolved in 100ml deionized water.

[0031] 2. Configure lye: dissolve 20 g of sodium hydroxide in 980 g of deionized water to obtain an aqueous solution of sodium hydroxide with a concentration of 2%.

[0032] 3. Configure alkaline texturing liquid: mix the texturing additive obtained in step 1 and the lye obtained in step 2 with a mass ratio of 0.1:100.

[0033] 4. Texturing process: immerse monocrystalline silicon wafers for solar cells in the alkaline texturing liquid prepared in step 3 for surface texturing, the texturing temperature is 88°C, and the texturing time is 600s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of monocrystalline silicon wafer tools, and particularly relates to a texturization method of a monocrystalline silicon wafer. The method comprises the following steps: 1) preparing atexturizationadditive; 2) preparing atexturization solution; and 3) putting the monocrystalline silicon wafer into thetexturization solution prepared in the step 2), and carrying out texturization at 80-88 DEG C for 600-1200 seconds. The method has excellent texturization effect; and the pyramids on thetexturizedsurface have smaller size and narrower distribution, and can reduce the light reflection, thereby enhancing the photoelectric conversion efficiency of the assembled solar cell.

Description

technical field [0001] The invention belongs to the technical field of monocrystalline silicon wafer tools, in particular to a texturing method for monocrystalline silicon wafers. Background technique [0002] In the preparation process of solar cells, reducing the reflection of light by silicon wafers as much as possible and increasing the absorption of light by silicon wafers will effectively improve the conversion efficiency of solar cells. Among them, texturing the surface of silicon wafers is a common way to increase the light absorption of crystalline silicon. In industrial production, a large amount of isopropanol or ethanol is often added to the alkaline texturing solution to improve the texturing effect. For example, Chinese invention patents CN201010195103.X and CN201010195095.9 respectively report two monocrystalline silicon wafer texturing additives and their usage methods. However, it should be pointed out that isopropanol and ethanol belong to low-boiling poi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C30B33/10H01L31/18
CPCC30B33/10H01L31/18Y02P70/50
Inventor 姜翰钦
Owner DEQING LIJING ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap