Electromagnetic wave absorbent large in radius-thickness ratio and preparation method thereof

A technology with large diameter-to-thickness ratio and electromagnetic waves, which is applied in metal processing equipment, inorganic material magnetism, transportation and packaging, etc., can solve the problems of high resistance of electromagnetic wave-absorbing materials, affect the electromagnetic wave absorption effect, and reduce product performance, so as to achieve high economy Value, energy consumption reduction, the effect of large diameter-thickness ratio

Active Publication Date: 2017-06-20
广州蓝磁新材料科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are generally the following deficiencies: 1. If a lubricant is added, due to the high requirements for dewaxing, if the dewaxing is not clean, the real part of the magnetic permeability will be seriously reduced, and the product performance will be reduced.
2. Especially when the content of lubricant or dispersant increases, although the flattening effect is good, but under the dewaxing pressure, the dewaxing is not clean, resulting in a decline in performance, and the gain outweighs the gain
3. In the existing process, the proportion of lubricant or dispersant must be strictly controlled within a range (<2%). During the high-speed flattening process, the alloy powder obtains a large amount of energy, resulting in The flattened powders form cold welding with each other, resulting in a large resistance of the electromagnetic absorbing material, which affects the absorption effect of electromagnetic waves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Step 1, solvent compounding: choose ethylene glycol and 120# solvent oil, mix and compound according to the ratio of 1:8.

[0029] Step 2, lubricant: use triglycerides of fatty acids, and the addition amount is 3% of the mass percentage of the magnetic powder, and the usage amount is adjusted.

[0030] Step 3, flattening ball milling: put the soft magnetic alloy powder and the mixed specific solvent into the ball mill according to the mass ratio of 20:1, and then add triglycerides of fatty acids according to 3% of the mass of the magnetic powder for flattening treatment, and the flattening treatment adopts directional The steel ball movement mode flattens the ball mill at the same speed.

[0031] Step 4, drying: the flattened material is separated from solid and liquid by a filter press, and then dried by a double-cone vacuum to further recover the solvent.

[0032] Step 5, dewaxing: The cavity of the dewaxing equipment is a vacuum treatment furnace with a multi-layer ...

Embodiment 2

[0036] Step 1, solvent compounding: choose propylene glycol and 90# solvent oil, mix and compound according to the ratio of 1:10.

[0037] Step 2, lubricant: use triglycerides of fatty acids, the addition amount is 5% of the mass percentage of the magnetic powder, and the usage amount is adjusted.

[0038] Step 3, flattening ball milling: Put the soft magnetic alloy powder and the mixed specific solvent into the ball mill according to the mass ratio of 20:1, and then add triglycerides of fatty acids according to 5% of the mass of the magnetic powder for flattening treatment, and the flattening treatment adopts directional The steel ball movement mode flattens the ball mill at the same speed.

[0039] Step 4, drying: the flattened material is separated from solid and liquid by a filter press, and then dried by a double-cone vacuum to further recover the solvent.

[0040] Step 5, dewaxing: The cavity of the dewaxing equipment is a vacuum treatment furnace with a multi-layer plu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an electromagnetic wave absorbent large in radius-thickness ratio and a preparation method thereof. The method comprises the steps that laminarization treatment is mainly conducted on magnetically soft alloy powder on the condition that a solvent medium and a specific proportion-specified and environmentally friendly lubricant exist, then, drying is conducted, and particularly after specified dewaxing process heat treatment, annealing treatment and other processes, the electromagnetic wave absorbent large in radius-thickness ratio is formed. The particle size and morphology are uniform, the surface is mellow, full and smooth, and the magnetic property is excellent.

Description

technical field [0001] The invention belongs to the field of magnetic materials, and in particular relates to an electromagnetic wave absorber with a large diameter-to-thickness ratio and a preparation method thereof. Background technique [0002] In a modern society with rapid development of science and technology, electronic products are changing with each passing day. While enriching people's life content, they also bring a magnetic field formed by electromagnetic waves, which makes electronic devices interfere with each other and exposes the human body to electromagnetic radiation. Finding various high-performance materials that can absorb or weaken electromagnetic waves, that is, microwave absorbers, has gradually become a goal pursued by material scientists. [0003] In the application field of wave absorbing agent, compared with other materials, the flat sheet of Fe-based soft magnetic alloy material has the characteristics of high magnetic permeability and low price....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F1/20B22F1/00
CPCH01F1/20B22F1/107B22F1/142
Inventor 汪涛
Owner 广州蓝磁新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap