High-flame-retardancy liquid wallpaper and preparation method thereof

A liquid wallpaper, high flame retardant technology, used in coatings, buildings, fire-resistant coatings, etc., can solve the problems of poor construction performance and drying performance of coatings, lack of wear resistance and hardness, and unsatisfactory performance, and achieve construction efficiency. High, not easy to fall off, good stickiness and plasticity

Inactive Publication Date: 2017-06-23
HEFEI OAKS NEW BUILDING MATERIAL CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The production method of wallpaper paint is mainly composed of base material, filler, and additives. The base material generally uses epoxy resin, etc., and the additives often contain components such as heavy metals. Due to the large size of the powder, its performance often cannot meet the requirements. General liquid wallpaper needs
[0005] The coatings produced by existing wallpaper coatings generally only have a single coloring performance, and do not have good wear resistance and hardness; moreover, these coatings have poor construction performance and drying performance, and the coatings are easy to agglomerate. Difficult to use, long drying time, low construction efficiency, poor flame retardancy, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A highly flame-retardant liquid wallpaper and its preparation method according to the preferred embodiment of the present invention;

[0030] The high flame-retardant liquid wallpaper is prepared from the following raw materials in parts by weight:

[0031] 28 parts of polyacrylamide, 5 parts of graphene, 12 parts of attapulgite, 16 parts of titanium dioxide, 20 parts of nano calcium carbonate, 11 parts of bamboo charcoal fiber, 22 parts of limestone, 8 parts of antimony trioxide, 12 parts of chlorinated paraffin, 12 parts of shale diatom mud, 8 parts of licorice, 10 parts of rosemary, 3 parts of clove oil, 10 parts of mint, 8 parts of lemon peel, 5 parts of defoamer, 14 parts of filler, 7 parts of additives, and an appropriate amount of water.

[0032] The attapulgite is a paste-like attapulgite prepared after natural attapulgite is purified and thermally modified.

[0033] The reason for using attapulgite is that the paste-like attapulgite has good viscosity and pla...

Embodiment 2

[0044] A highly flame-retardant liquid wallpaper and its preparation method according to the preferred embodiment of the present invention;

[0045] The high flame-retardant liquid wallpaper is prepared from the following raw materials in parts by weight:

[0046] 20 parts of polyacrylamide, 3 parts of graphene, 10 parts of attapulgite, 12 parts of titanium dioxide, 15 parts of nano calcium carbonate, 5 parts of bamboo charcoal fiber, 18 parts of limestone, 6 parts of antimony trioxide, 10 parts of chlorinated paraffin, 7 parts of shale diatom mud, 3 parts of licorice, 5 parts of rosemary, 2 parts of clove oil, 8 parts of mint, 6 parts of lemon peel, 3 parts of defoamer, 10 parts of filler, 5 parts of additives, and an appropriate amount of water.

[0047] The attapulgite is a paste-like attapulgite prepared after natural attapulgite is purified and thermally modified.

[0048] The reason for using attapulgite is that the paste-like attapulgite has good viscosity and plastic...

Embodiment 3

[0059] A highly flame-retardant liquid wallpaper and its preparation method according to the preferred embodiment of the present invention;

[0060] The high flame-retardant liquid wallpaper is prepared from the following raw materials in parts by weight:

[0061] 35 parts of polyacrylamide, 8 parts of graphene, 15 parts of attapulgite, 20 parts of titanium dioxide, 30 parts of nano calcium carbonate, 16 parts of bamboo charcoal fiber, 36 parts of limestone, 15 parts of antimony trioxide, 20 parts of chlorinated paraffin, 15 parts of shale diatom mud, 10 parts of licorice, 12 parts of rosemary, 6 parts of clove oil, 15 parts of mint, 10 parts of lemon peel, 7 parts of defoamer, 18 parts of filler, 12 parts of additive, and appropriate amount of water.

[0062] The attapulgite is a paste-like attapulgite prepared after natural attapulgite is purified and thermally modified.

[0063] The reason for using attapulgite is that the paste-like attapulgite has good viscosity and pla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-flame-retardancy liquid wallpaper and a preparation method thereof. The liquid wallpaper comprises the following components: polyacrylamide, graphene, attapulgite, titanium white, nano calcium carbonate, bamboo charcoal fibers, limestone, antimony trioxide, chlorinated paraffin wax, shale diatom ooze, licorice root, rosemary, clove oil, mint, lemon peel, a defoamer, a filler, additives and a proper amount of water. The preparation method comprises the following steps: extracting the Chinese herbal medicine components to obtain an extract; modifying the polyacrylamide with graphene, adding the antimony trioxide and chlorinated paraffin wax, and reacting; and adding the titanium white, nano calcium carbonate, bamboo charcoal fibers, limestone, shale diatom ooze and pasty attapulgite, mixing, shearing, adding the Chinese herbal medicine extract and clove oil, carrying out ultrasonic treatment, and adding the rest components, thereby obtaining the liquid wallpaper. The liquid wallpaper has the characteristics of favorable flame-retardant effect, scratch resistance, high strength / toughness and other mechanical properties, high painting uniformity, low caking tendency and high construction efficiency.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high flame-retardant liquid wallpaper and a preparation method thereof. Background technique [0002] For the traditional wall decoration materials, wallpaper or wall cloth are used, which are produced by coating PVC plastic on the paper base or cloth base or using latex paint. Affected by paper and cloth, the flame retardant performance is not high, and the moisture-proof and mildew-proof effect Poor, the use is greatly restricted by the environment; the product structure is a combination of layers of materials with different expansion coefficients, resulting in adverse consequences such as edge warping, blistering and shedding during use; after the use of latex paint, the indoor odor Large, affecting the living environment. At the same time, because 107 glue, polyvinyl alcohol, etc. will be used in the construction process, it will contain heavy metals such as lea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/26C09D191/06C09D7/12C09D5/18E04F13/02
CPCC09D133/26C08K2201/011C08L2201/02C09D5/18C09D7/70E04F13/02C08L91/06C08K13/04C08K7/06C08K7/00C08K3/04C08K3/346C08K3/2279
Inventor 曹智远
Owner HEFEI OAKS NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products