A kind of transparent nano silicon dioxide-epoxy resin anticorrosion coating and preparation method thereof
A technology of nano-silica and epoxy resin, applied in the field of coatings, can solve the problems of large differences in surface molecular structure, agglomeration of fillers in anti-corrosion coatings, poor interface compatibility, etc., and achieve good transparency and corrosion resistance. Good, the effect of ensuring storage stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036] A reflux condenser is installed on a clean, airtight, heat-resistant container with a stirring device, and the components should be tightly connected to ensure the airtightness of the device. Add 100 grams of epoxy equivalents of 160 to 180 (g.mol -1 ) bisphenol F type epoxy resin, 1 gram of γ-aminopropyl trimethoxysilane, 1000 grams of acetone, turn on stirring and be warming up to acetone backflow, react under the condition of acetone backflow and stop reaction after 12 hours to obtain grafted epoxy resin Silane of the resin, after cooling to room temperature, add 300 grams of silica with a particle size of 70 nanometers, after ultrasonic treatment for 20 minutes, start stirring and heat up to maintain acetone reflux, react under the condition of acetone reflux for 6 hours, stop the reaction, cool After reaching room temperature, repeatedly washing with acetone, and centrifuging or filtering to remove unreacted silane of grafted epoxy resin, to obtain nano-silica fill...
Embodiment 2
[0039] Add 100 grams of epoxy equivalent 165-185 (g.mol -1 ) of bisphenol F-type epoxy resin, 100 grams of N-(2-aminoethyl)-3 aminopropyl methyl methoxy silane, 100 grams of xylene, open stirring and react at room temperature for 20 hours, continue to heat up to 110 After 4 hours of reaction at °C, the reaction was stopped to obtain silane grafted with epoxy resin. After cooling to room temperature, 1 gram of silica with a particle size of 30 nanometers was added. After ultrasonic treatment for 20 minutes, the stirring was turned on and the reaction was carried out at room temperature for 1 hour, and continued. The reaction was stopped after heating at 120° C. for 23 hours, and after cooling to room temperature, repeated washing with xylene, and centrifugation or filtration to remove unreacted silane of grafted epoxy resin to obtain nano-silica filler of grafted epoxy resin.
[0040] 0.01 gram of nano-silica filler grafted with epoxy resin, 100 grams of epoxy equivalent of 185...
Embodiment 3
[0042] Add 100 grams of epoxy equivalent 200-220 (g.mol -1 ) of aliphatic epoxy resin, 10 grams of bis(3-triethoxysilylpropyl) amine, 450 grams of toluene, open stirring and be warmed up to 55 ° C for 2 hours, continue to be warmed up to 110 ° C and react for 2 hours, after Stop the reaction to obtain the silane of the grafted epoxy resin, after cooling to room temperature, add 20 grams of silica with a particle size of 20 nanometers, start stirring and heat up at 60 ° C and react for 24 hours to stop the reaction, after cooling to room temperature, repeat with toluene Washing, centrifuging or filtering to remove unreacted epoxy resin grafted silane to obtain epoxy resin grafted nano silica filler.
[0043] 5 grams of nano-silica filler grafted epoxy resin, 100 grams of epoxy equivalent 455 ~ 556 (g.mol -1 ) of bisphenol F type epoxy resin, 0.5g defoamer, 0.5g leveling agent, 0.1g anti-skinning agent, 0.3g matting agent, 0.2g light stabilizer, 250g xylene, 50g isopropanol Pu...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com