High-toughness hot-shrinkage-resistant artificial board and preparation method thereof
A wood-based panel, high toughness technology, applied in the field of wood-based panel materials, can solve the problems of dimensional change rate, floor fracture, low bending strength of wood-based panels, etc., achieve the effect of reducing internal defects, increasing bending strength, and improving dimensional stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0017] A method for preparing a high-toughness heat-resistant shrinkable wood-based panel, comprising the following steps: (1) adding β-silicon nitride submicron particles into ethanol and isopropanol and a mixed solution, and the mass ratio of ethanol and isopropanol is 1: 3. Disperse evenly at a rotation speed of 1000r / min, then place it in a constant temperature water bath at 80°C, add titanate coupling agent, stir for 1 hour, then stand for 24 hours, wash and dry, among which titanate coupling agent: β-silicon nitride submicron particles: the mass ratio of the mixed solution is 3:120:500 to obtain modified silicon nitride; (2) Weigh the following components by weight: 90 parts of PVC, 50 parts of kaolin, modified nitrogen 40 parts of silicon dioxide, 25 parts of dioctyl phthalate, 0.2 parts of calcium zinc stabilizer, 0.6 parts of ultraviolet absorber UV-327, 1 part of toner, 0.02 parts of 4,4'-diaminodiphenylmethane , 2 parts of sodium alcohol ether carboxylate, 15 parts ...
Embodiment 2
[0019] A method for preparing a high-toughness heat-resistant shrinkable wood-based panel, comprising the following steps: (1) adding β-silicon nitride submicron particles into ethanol and isopropanol and a mixed solution, and the mass ratio of ethanol and isopropanol is 1: 3. Disperse evenly at a speed of 1500r / min, then place it in a constant temperature water bath at 60°C, add titanate coupling agent, stir for 4 hours, then stand for 24 hours, wash and dry, among which titanate coupling agent: β-silicon nitride submicron particles: the mass ratio of the mixed solution is 5:100:600 to obtain modified silicon nitride; (2) Weigh the following components by weight: 130 parts of PVC, 70 parts of kaolin, modified nitrogen 20 parts of silicon dioxide, 45 parts of dioctyl phthalate, 0.6 parts of calcium zinc stabilizer, 0.1 part of ultraviolet absorber UV-327, 4 parts of toner, 0.06 parts of 4,4'-diaminodiphenylmethane , 9 parts of sodium alcohol ether carboxylate, 10 parts of arte...
Embodiment 3
[0021] A method for preparing a high-toughness heat-resistant shrinkable wood-based panel, comprising the following steps: (1) adding β-silicon nitride submicron particles into ethanol and isopropanol and a mixed solution, and the mass ratio of ethanol and isopropanol is 1: 3. Disperse evenly at a rotation speed of 1200r / min, then place it in a constant temperature water bath at 75°C, add titanate coupling agent, stir for 2 hours, then stand for 24 hours, wash and dry, among which titanate coupling agent: β-silicon nitride submicron particles: the mass ratio of the mixed solution is 4:100:550 to obtain modified silicon nitride; (2) Weigh the following components by weight: 100 parts of PVC, 55 parts of kaolin, modified nitrogen 35 parts of silicon dioxide, 30 parts of dioctyl phthalate, 0.5 parts of calcium zinc stabilizer, 0.2 parts of ultraviolet absorber UV-327, 3 parts of toner, 0.05 parts of 4,4'-diaminodiphenylmethane , 8 parts of sodium alcohol ether carboxylate, 11 par...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap