Polishing solution for front and rear covers of electric motor

A technology of electric motor and polishing liquid, which is applied in the field of polishing liquid, can solve the problems of high cost and affecting color, etc., and achieve good decontamination ability, good polishing performance, and silvery white surface

Inactive Publication Date: 2017-07-14
舒城久联精密机械有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among these methods, mechanical polishing has a high cost in terms of high-temperature pickling and mechanical polishing equipment, auxiliary materials, and power consumption; although electrochemical polishing has a better polishing effect, the cost is relatively high, and it is easily limited by the distribution of power lines. Affect the colo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The additive is prepared by the following method: 108 parts of water, 7 parts of graphite, 3 parts of magnesium oxide, 3 parts of dibutyl phosphite, 3 parts of polyethylene glycol monooctyl phenyl ether, sodium diethylamine tetraacetate iron salt Mix 2 parts, 6 parts of zinc fluorosilicate, 2.4 parts of lanthanum nitrate hexahydrate, 2.8 parts of sorbitol monolaurate, and 6 parts of hydroxypropyl cellulose, heat and stir at 63°C for 1.6 hours, cool and grind to obtain ;

[0014] The weight ratio of sodium benzotriazolyl butylphenol sulfonate, phosphonobutane tricarboxylic acid and ethylenediamine tetramethylene phosphonic acid in the derusting additive is 1:0.25:0.13.

[0015] For the polishing solution of the front and rear covers of the motor, 9 parts of phosphoric acid, 6 parts of graphitic acid, 3 parts of heptadecane fluorooctanesulfonic acid, 7 parts of linseed oil, 6.3 parts of sodium fluoroborate, 0.7 parts of ammonium bicarbonate, sodium phosphate dodecahydrate...

Embodiment 2

[0017] The additive is prepared by the following method: 109 parts of water, 7 parts of graphite, 3 parts of magnesium oxide, 2 parts of dibutyl phosphite, 2.9 parts of polyethylene glycol monooctyl phenyl ether, sodium diethylamine tetraacetate iron salt Mix 1.2 parts, 5 parts of zinc fluorosilicate, 2.2 parts of lanthanum nitrate hexahydrate, 3 parts of sorbitol monolaurate, and 5.4 parts of hydroxypropyl cellulose, heat and stir at 62°C for 1.8 hours, cool and grind to obtain ;

[0018] The weight ratio of sodium benzotriazolyl butylphenol sulfonate, phosphonobutane tricarboxylic acid and ethylenediamine tetramethylene phosphonic acid in the derusting additive is 1:0.7:0.14.

[0019] For the polishing solution of the front and rear covers of the motor, 10 parts of phosphoric acid, 5 parts of graphitic acid, 2.4 parts of heptadecafluorooctanesulfonic acid, 7 parts of linseed oil, 5 parts of sodium fluoroborate, 0.8 parts of ammonium bicarbonate, sodium phosphate dodecahydrat...

Embodiment 3

[0021] The additive is prepared by the following method: 110 parts of water, 8 parts of graphite, 2 parts of magnesium oxide, 4 parts of dibutyl phosphite, 2 parts of polyethylene glycol monooctyl phenyl ether, sodium diethylamine tetraacetate iron salt Mix 2.4 parts, 8 parts of zinc fluorosilicate, 3 parts of lanthanum nitrate hexahydrate, 2.1 parts of sorbitol monolaurate, and 5 parts of hydroxypropyl cellulose, heat and stir at 62°C for 1.8 hours, cool and grind to obtain ;

[0022] The weight ratio of sodium benzotriazolyl butylphenol sulfonate, phosphonobutane tricarboxylic acid and ethylenediamine tetramethylene phosphonic acid in the derusting additive is 1:0.24:0.18.

[0023] For the polishing solution of the front and rear covers of the motor, 9 parts of phosphoric acid, 7 parts of graphitic acid, 3 parts of heptadecane fluorooctane sulfonic acid, 6 parts of linseed oil, 7 parts of sodium fluoroborate, 0.57 parts of ammonium bicarbonate, sodium phosphate dodecahydrate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides polishing solution for front and rear covers of an electric motor. The polishing solution is prepared from the following raw materials: phosphoric acid, graphitic acid, heptadecafluorooctanesulfonic acid, linseed oil, sodium fluoborate, ammonium bicarbonate, disodium phosphate dodecahydrate, 4,4-diaminodiphenyl sulfide, polyethylene glycol stearate, trimethyl borate, derusting assistant, an additive and deionized water. The polishing solution provided by the invention is used for polishing the front and rear covers of the electric motor and is excellent in polishing performance; surfaces of the polished front and rear covers of the electric motor are silvery white and light; the added derusting assistant can effectively remove rust on the surfaces; the added additive has better dirt-removing power.

Description

technical field [0001] The invention relates to a polishing liquid for the front and rear covers of a motor. Background technique [0002] At present, the methods of polishing stainless steel in the metal processing industry mainly include mechanical polishing, chemical polishing and electrochemical polishing. [0003] Learn to polish etc. Among these methods, mechanical polishing has a high cost in terms of high-temperature pickling and mechanical polishing equipment, auxiliary materials, and power consumption; although electrochemical polishing has a better polishing effect, the cost is relatively high, and it is easily limited by the distribution of power lines. Affect the color; chemical polishing is a kind of chemical corrosion under special conditions. It selectively dissolves the stainless steel surface by controlling the surface, so that the microscopic protruding parts of the stainless steel surface are preferentially dissolved compared with the concave parts, so a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09G1/04
CPCC09G1/04
Inventor 蒋能新
Owner 舒城久联精密机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap