Preparation method of high-strength colored glass fiber

A glass fiber and high-strength technology, applied in the field of preparation of high-strength colored glass fibers, can solve the problems of color loss, unstable properties of inorganic coloring substances, unstable coloring of colored glass fibers, etc., to achieve consistent internal and external colors, not easy to spread and Shedding, color stability and uniform effect

Inactive Publication Date: 2017-08-04
德阳金戈达玻璃纤维厂
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The colored glass fibers in the above-mentioned prior art are dyed by inorganic coloring substances, but the properties of the inorganic coloring substances are unstable, which will lead to unstable coloring of the colored glass fibers, and high-strength stretching will accelerate the color loss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The surface of glass fiber is dense and smooth and contains less active groups, which is not conducive to the absorption and diffusion of dye molecules, which seriously affects the coloring performance of the fiber. In order to produce colored glass fibers, the present invention does not dye the glass fibers after the glass fibers are formed, but adds non-ferrous alloys to the raw materials of the glass fibers to produce the required colored glass fibers. In order to ensure the coloring of non-ferrous alloys, a color-fixing agent is added to fix the color, so that the solution has color, and then drawn to form colored glass fibers.

[0036] High-strength colored glass fibers refer to glass fibers whose tensile strength is at least higher than 2500MPa.

[0037] The inert gas system in the present invention refers to a closed environment filled with inert gas.

[0038] The specific process of the present invention is as follows.

[0039] A preparation method of high-str...

Embodiment 2

[0052] A preparation method of high-strength red glass fiber is characterized in that: comprising the following steps:

[0053] A. Preparation of spinning solution

[0054] Select raw materials according to the following molar ratio: SiO 2 for 55 parts, Al 2 o 3 is 6 parts, CaO is 1 part, MgO is 1 part, K 2 O is 1.5 parts, Li 2 CO 3 for 10 copies, B 2 o 3 for 5 parts, CeO 2 7 parts; the above raw materials are mixed and then melted into a spinning solution;

[0055] B, preparation of copper alloy spraying liquid

[0056] Dilute silica, silane coupling agent, color fixing agent and water-soluble epoxy with deionized water respectively, then add copper alloy powder with a particle size of 80nm and stir evenly to form a copper alloy spray coating with a light transmittance of 7%. liquid;

[0057] C, dry spinning

[0058] The spinning solution prepared in step A and the copper alloy spraying solution prepared in step B are mixed into a uniform mixed solution, and the m...

Embodiment 3

[0065] A kind of preparation method of high-strength blue glass fiber is characterized in that: comprises the following steps:

[0066] A. Preparation of spinning solution

[0067] Select raw materials according to the following molar ratio: SiO 2 for 58 parts, Al 2 o 3 is 7 parts, CaO is 1 part, MgO is 1 part, K 2 O is 0.5 parts, Li 2 CO 3 for 9 parts, B 2 o 3 for 6 parts, CeO 2 6 parts; the above raw materials are mixed and then melted into a spinning solution;

[0068] B. Preparation of blue and white galvanized alloy spraying liquid

[0069] Dilute silica, silane coupling agent, color fixing agent and water-soluble epoxy with deionized water, then add blue-white galvanized alloy powder with a particle size of 1nm and stir evenly to form a light transmittance of 7%- 12% blue and white galvanized alloy spraying fluid;

[0070] C, dry spinning

[0071] Mix the spinning solution prepared in step A with the blue-white galvanized alloy spray solution prepared in step...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Granularityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of high-strength colored glass fiber, and discloses a preparation method of producing high-strength colored glass fiber by coloring with a non-ferrous alloy and then heat-treating. The colored alloy of the invention is evenly mixed with the color fixing agent to make the coloring uniform, and then the high-strength colored glass fiber is obtained through dry spinning, laminar flow plasma spraying and heat treatment. Heat treatment does not change the shape and overall chemical composition of the workpiece, but by changing the microstructure inside the workpiece, or changing the chemical composition of the surface of the workpiece, endows or improves the performance of the workpiece, and improves the toughness and strength of the colored glass fiber. The color of the high-strength colored glass fiber produced by the invention is stable and uniform, and is not easy to spread.

Description

technical field [0001] The invention belongs to the field of preparation of glass fiber surface treatment and dyeing coating, in particular to a preparation method of high-strength colored glass fiber. Background technique [0002] Glass fiber is an inorganic non-metallic material with excellent performance and a wide range of uses. It is an important part of the new technological revolution marked by materials, energy and information. Its products involve various fields and are widely used in various industrial sectors, such as fiberglass, flooring, wall insulation, waterproof materials, concrete materials, highways, fireproof materials, sound-absorbing materials, etc. In the large-scale application of glass fiber downstream, people have higher and higher visual requirements for product appearance, so the development of colored glass fiber can expand the use range of glass fiber and increase its economic value. [0003] The surface of glass fiber is dense and smooth and co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03B37/06C03C25/46C03C13/00
CPCC03B37/06C03C13/00C03C25/46C03C25/475
Inventor 金思宇杨黎黎金维荣
Owner 德阳金戈达玻璃纤维厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com