Adhesive glue for badminton ribbon and preparation method thereof

A technology of badminton and glue, applied in the direction of adhesive, starch adhesive, adhesive type, etc., can solve the problem of badminton scrapping, etc., and achieve the effect of good bonding stability, good adhesion, and strong environmental protection

Active Publication Date: 2019-01-18
安徽太阳体育用品有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a badminton ribbon adhesive glue with high adhesive strength and good stability to prevent the badminton from being scrapped because the ribbon is not firmly pasted and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive glue for badminton ribbon and preparation method thereof
  • Adhesive glue for badminton ribbon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Add 1kg of polyethylene oxide to 15kg of starch / polyvinyl alcohol copolymer, heat up to 115-120°C and mix for 15 minutes, then add 0.3kg of down fiber powder and 0.05kg of nano-zirconia, and continue to heat at 115-120°C Insulated and mixed for 15min to obtain material I;

[0028] (2) Add 2 kg of water-based polyvinyl butyral and 0.1 kg of sodium citrate to 5 kg of glutinous rice flour, mix well, heat up to 45-50°C and keep it for 30 minutes, then mix evenly to obtain material II;

[0029] (3) Add 5kg chitosan oligosaccharide / anionic polyacrylamide compound, 1kg activated clay and 0.5kg sepiolite fiber powder to 150kg water, mix well and let stand for 15min, then heat up to reflux state and mix for 15min, then add materials I and material II are fully mixed, transferred to 0-5 ℃ environment, sealed and left for 2 hours, and then heated up to reflux state and kept mixed for 15 minutes, and then naturally cooled to room temperature to obtain the ribbon adhesive glue. ...

Embodiment 2

[0035] (1) Add 2kg of polyethylene oxide to 20kg of starch / polyvinyl alcohol copolymer, heat up to 115-120°C and mix for 15 minutes, then add 0.5kg of down fiber powder and 0.05kg of nano-zirconia, and continue heating at 115-120°C Insulated and mixed for 15min to obtain material I;

[0036] (2) Add 3kg of water-based polyvinyl butyral and 0.2kg of sodium citrate to 3kg of glutinous rice flour, mix well, heat up to 45-50°C and keep it for 30 minutes, then mix evenly to obtain material II;

[0037](3) Add 10kg chitosan oligosaccharide / anionic polyacrylamide compound, 2kg activated clay and 0.5kg sepiolite fiber powder to 150kg water, mix well and let stand for 15min, then heat up to reflux state and keep mixed for 15min, then add materials I and material II are fully mixed, transferred to 0-5 ℃ environment, sealed and left for 2 hours, and then heated up to reflux state and kept mixed for 15 minutes, and then naturally cooled to room temperature to obtain the ribbon adhesive gl...

Embodiment 3

[0073] Use the same amount of ribbon glue made in Example 1, Example 2, Comparative Example 1, Comparative Example 2, Comparative Example 3 and Comparative Example 4 to paste ribbons on 100 shuttlecocks produced in the same batch, and wait until the glue is completely dry Then measure its shear strength and peel strength, and calculate the average shear strength and average peel strength, the results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses glue for pasting a color bar of a shuttlecock and a preparation method thereof, and relates to the technical field of the processing of shuttlecocks. The glue is prepared from the following raw materials in parts by weight: 15 to 20 parts of starch / polyvinyl alcohol copolymer, 5 to 10 parts of chitosan oligosaccharide / anionic polyacrylamide compound, 3 to 5 parts of glutinous rice flour, 2 to 3 parts of waterborne polyvinyl butyral, 1 to 2 parts of polyoxyethylene, 1 to 2 parts of active floridin, 0.5 to 1 part of sepiolite fiber powder, 0.3 to 0.5 part of down fiber powder, 0.1 to 0.3 part of sodium citrate, 0.05 to 0.1 part of nano zirconium oxide and 100 to 150 parts of water. According to the glue made by the preparation method, the water is used as a preparation solvent; the environmental friendliness is high; meanwhile, the adhesion is good; the color bar can be firmly conglutinated on the head of the shuttlecock; moreover, the adhesion stability is good, so as to avoid the scrapping of the shuttlecock, which is caused as the color bar is not firmly adhered; the service life of the shuttlecock is prolonged.

Description

Technical field: [0001] The invention relates to the technical field of badminton processing, in particular to a badminton ribbon sticking glue and a preparation method thereof. Background technique: [0002] Badminton is a sport that can be played both indoors and outdoors. The equipment consists of shuttlecocks and badminton rackets. Among them, the quality of the shuttlecock is very important, not only determines the service life of the shuttlecock, but also directly relates to the user's control of the shuttlecock. [0003] The ribbon is pasted on the ball head at the connection between the ball head and the feathers. It mainly serves as an aesthetic decoration, and it can also make the overall white shuttlecock easy to distinguish. The pasting of the ribbon requires the use of glue, and the firmness of the glue directly affects the normal function of the ribbon. If the adhesion of the glue is poor, the ribbon will peel off during the use of the shuttlecock, which will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J103/02C09J129/04C09J129/14C09J133/26C09J105/08C09J11/08C09J11/04C09J11/06
CPCC08K2003/2244C08K2201/011C08L2205/02C08L2205/035C08L2205/16C09J11/04C09J11/06C09J11/08C09J103/02C09J129/04C08L29/04C08L29/14C08L33/26C08L5/08C08L71/02C08L3/02C08L39/06C08L91/00C08K13/04C08K7/10C08K3/22C08K5/098C08K3/34
Inventor 沈在国
Owner 安徽太阳体育用品有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com