A kind of preparation method of sintered NdFeB magnet

A sintered magnet, NdFeB technology, used in magnetic objects, inductance/transformer/magnet manufacturing, magnetic materials, etc., can solve problems such as low output, and achieve the effects of suppressing grain growth, low cost, and simple process

Active Publication Date: 2020-02-07
YANTAI ZHENGHAI MAGNETIC MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the problem that still remains is the low throughput associated with depositing metal coatings by sputtering etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1) Preparation of sintered magnets: Nd-23.8%, Pr-5%, Dy-0.6%, Tb -0.4%, Co-0.5%, Cu-0.13%, Ga-0.1%, Al-0.1%, Zr-0.12%, B-1%, the balance is iron and unavoidable impurities, in an inert gas environment The pouring is completed in the vacuum melting furnace under the furnace, the pouring temperature is 1450°C, the speed of the quenching roll is 60r / min, the cooling water is passed through the quenching roll, and the thickness of the obtained scales is about 0.3mm; then, the scales are made into a uniform Magnetic powder with a particle size of 3.4 μm; Orientation pressing at room temperature and an environment with a magnetic field strength of 2T orientation field to make a compact; put the compact into a sintering furnace under an Ar atmosphere, and sinter at 1100°C for 5 hours to obtain a green compact. The blank was aged at 500°C for 5 hours to obtain a sintered blank. The sintered blank is machined into a magnet with a size of 40mm*20mm*4mm. After degreasing, picklin...

Embodiment 2

[0033] 1) The weight ratio of neodymium, dysprosium, terbium, cobalt, copper, aluminum, boron: Nd-30.1%, Dy-0.5%, Co-0.8%, Cu-0.13%, Al-0.2%, B-1% Ratio, the balance is Fe and unavoidable impurities. The casting is completed in a vacuum melting furnace under an inert gas environment. The pouring temperature is 1450°C, the speed of the quenching roll is 60r / min, and cooling water is passed through the quenching roll. The thickness of the obtained scales is about 0.32 mm; Then, the scales were powdered by HD and jet milled to produce magnetic powder with an average particle size of 3.6 μm; orientation pressing was carried out at room temperature and in an environment with a magnetic field strength of 2T orientation field to make compacts; the compacts were placed in Ar In a sintering furnace under atmosphere, sinter at 1060° C. for 6 hours to obtain a green compact, and age the green compact at 510° C. for 4 hours to obtain a sintered blank. The sintered blank is processed into ...

Embodiment 3

[0041] 1) The weight ratio of neodymium, dysprosium, terbium, cobalt, copper, aluminum, boron: Nd-30.5%, Tb-0.5%, Co-1.1%, Cu-0.16%, Al-0.4%, B-1.02% Ratio, the balance is Fe and unavoidable impurities. The casting is completed in a vacuum melting furnace under an inert gas environment. The pouring temperature is 1460°C, the speed of the quenching roll is 65r / min, and cooling water is passed through the quenching roll. The thickness of the obtained scales is about 0.36 mm; then, the flakes are powdered by HD and jet milled to make magnetic powder with an average particle size of 3.0 μm; orientation pressing is carried out at room temperature and the magnetic field strength is 2T orientation field to make compacts; then the compacts are put into Sintering at 910°C for 1.5h in a vacuum hot-press furnace under Ar atmosphere. After the sintering is completed, the system starts to apply pressure for hot-pressing sintering. The hot-pressing temperature is 920° C., the pressure is 11...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a sintered NdFeB magnet, which comprises pretreating the sintered magnet R1-Fe-B-M; mixing heavy rare earth powder with metal Ga, and then mixing with an organic solvent to prepare a slurry, and mixing the powder The content of Ga in the medium is 0.5-20wt%; the heavy rare earth refers to Dy, Tb, the alloy of Dy and Tb, the compound of one or more hydrides of Dy or Tb; the obtained slurry is covered with The surface of the sintered magnet, the thickness of the slurry on the surface of the magnet is 20-200μm, and then the grain boundary diffusion treatment is performed after drying. The method of the present invention utilizes the self-adhesive effect of Ga in the slurry of the mixed powder, and overcomes the problem that the fluoride and hydride powders are easy to fall off when directly applied, and the excessive C and N together with the heavy rare earth caused by adding the binder Penetration into the magnet leads to the disadvantage of reducing the magnetic performance.

Description

technical field [0001] The invention relates to a method for preparing an NdFeB magnet, belonging to the technical field of magnet preparation technology. Background technique [0002] Since its discovery, NdFeB permanent magnet materials have been widely used in communications, medical, automotive, electronics, aviation and other fields due to their excellent magnetic properties and high cost performance; however, their low coercive force and poor temperature Stability and corrosion resistance seriously limit the expansion of its application range. With the development of science and technology, the requirements for the comprehensive performance of NdFeB magnets in various fields are getting higher and higher. Therefore, the development of high comprehensive performance NdFeB magnets has become a The inevitable trend. [0003] Typical indicators of magnet performance are remanence and coercive force. Coercive force is an important index to measure the magnetic properties ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/02H01F1/057H01F1/08
CPCH01F1/0571H01F1/0577H01F41/0293
Inventor 史丙强魏蕊杜伟
Owner YANTAI ZHENGHAI MAGNETIC MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com