A kind of activation method of graphene oxide

An activation method, graphene technology, applied in chemical instruments and methods, carbon compounds, inorganic chemistry, etc., can solve problems such as large steric hindrance, property destruction, curling agglomeration, etc., to save energy and maintain properties.

Active Publication Date: 2019-11-15
SHANDONG OBO NEW MATERIAL CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large steric hindrance of graphene oxide, the conditions for directly modifying the surface of graphene oxide are harsh and the reaction time is long. However, graphene oxide is prone to curling and agglomeration under harsh conditions, destroying its sheet structure. lead to the destruction of its original characteristics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of activation method of graphene oxide
  • A kind of activation method of graphene oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0107] ①Add 0.75g graphene oxide slurry (mass fraction 28%) in a single-necked flask, add 100mL DMF, and ultrasonically stir for 30min to obtain a graphene oxide dispersion;

[0108] ②Add 9g of activated 5A molecular sieve to the graphene oxide dispersion in step ①, soak the dispersion for 24 hours and filter the dispersion into a three-necked flask;

[0109] ③Weigh 1.14g p-toluenesulfonyl chloride (the molar ratio of p-toluenesulfonyl chloride and graphene oxide is 3:1), add 10mL DMF to dissolve;

[0110] ④Under stirring condition, the solution obtained in step ③ is slowly added dropwise to the graphene oxide dispersion obtained in step ②;

[0111] ⑤Transfer the three-neck flask containing the dispersion liquid in step ④ to the oil bath, connect the condenser pipe and double-row pipe, and pass nitrogen for 20 minutes;

[0112] ⑥Weigh 1.212g of triethylamine (the molar ratio of triethylamine to graphene oxide is 6:1), add 10mL of DMF to dissolve;

[0113] ⑦Under nitrogen con...

Embodiment 2

[0126] ①Add 0.75g graphene oxide slurry (mass fraction 28%) in a single-necked flask, add 100mL DMF, and ultrasonically stir for 30min to obtain a graphene oxide dispersion;

[0127] ②Add 9g of activated 5A molecular sieve to the graphene oxide dispersion in step ①, soak the dispersion for 24 hours and filter the dispersion into a three-necked flask;

[0128] ③Weigh 1.128g of trifluoromethanesulfonic anhydride (the molar ratio of trifluoromethanesulfonic anhydride to graphene oxide is 2:1), add 10mL DMF to dissolve;

[0129]④Under stirring condition, the solution obtained in step ③ is slowly added dropwise to the graphene oxide dispersion obtained in step ②;

[0130] ⑤Transfer the three-neck flask containing the dispersion liquid in step ④ to the oil bath, connect the condenser pipe and double-row pipe, and pass nitrogen for 20 minutes;

[0131] ⑥Weigh 0.808g triethylamine (the molar ratio of triethylamine to graphene oxide is 4:1), add 10mL DMF to dissolve;

[0132] ⑦Under ...

Embodiment 3

[0136] ①Add 0.75g graphene oxide slurry (mass fraction 28%) in a single-necked flask, add 100mL DMF, and ultrasonically stir for 30min to obtain a graphene oxide dispersion;

[0137] ②Add 9g of activated 5A molecular sieve to the graphene oxide dispersion in step ①, soak the dispersion for 24 hours and filter the dispersion into a three-necked flask;

[0138] ③ Weigh 0.912g methanesulfonyl chloride (the molar ratio of methanesulfonyl chloride to graphene oxide is 4:1), add 10mL DMF to dissolve;

[0139] ④Under stirring condition, the solution obtained in step ③ is slowly added dropwise to the graphene oxide dispersion obtained in step ②;

[0140] ⑤Transfer the three-neck flask containing the dispersion liquid in step ④ to the oil bath, connect the condenser pipe and double-row pipe, and pass nitrogen for 20 minutes;

[0141] ⑥ Weigh 1.616g of triethylamine (the molar ratio of triethylamine to graphene oxide is 8:1), add 10mL of DMF to dissolve;

[0142] ⑦Under nitrogen condi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for activating graphene oxide, comprising the steps of first dispersing graphene oxide in a polar solvent to obtain a graphene oxide solution; then the graphene oxide solution obtained in the above steps, an activator and After the acid-binding agents are mixed, a reaction system is obtained; finally, the reaction system obtained in the above steps is heated and reacted under an oxygen-free condition to obtain activated graphene oxide. The present invention activates the hydroxyl groups on the surface of graphene oxide under mild conditions, and forms an easy-leaving group by combining the activator with the hydroxyl groups on the surface of graphene oxide, which activates the carbon-oxygen bond on the surface of graphene oxide and reduces the subsequent oxidative stress of graphene oxide. The difficulty of surface covalent bond modification provides a highly active intermediate for the surface functional modification of graphene oxide, so that the subsequent surface modification can be carried out without harsh conditions, which saves energy and saves energy. It can well maintain the sheet structure of graphene, thereby maintaining the characteristics of graphene.

Description

technical field [0001] The invention belongs to the technical field of graphene materials, and relates to a method for activating graphene oxide, in particular to a method for activating hydroxyl groups on the surface of graphene oxide. Background technique [0002] Graphene is a new material with a single-layer sheet structure composed of carbon atoms. It is a planar film composed of carbon atoms with sp2 hybrid orbitals forming a hexagonal honeycomb lattice, a two-dimensional material with a thickness of only one carbon atom. As a two-dimensional crystal composed of carbon atoms with only one layer of atomic thickness, it is the thinnest material and the strongest material currently in the application field, and its fracture strength is 200 times higher than that of steel, and it is also very good Excellent elasticity, the stretching range can reach 20% of its own size; at the same time, graphene has a huge theoretical specific surface area, stable physical and chemical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/198
Inventor 赵永彬张在忠蔡婷婷吴开付
Owner SHANDONG OBO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com