A kind of preparation method of high-precision drill bit

A high-precision, drill bit technology, applied in the direction of manufacturing tools, casting molding equipment, metal processing equipment, etc., can solve the problems of uncontrollable drill bit processing errors, inability to accurately process workpieces, and low processing accuracy, so as to improve consistency and work Efficiency, increased coating performance, and good surface quality

Inactive Publication Date: 2019-01-18
宁波神钻工具有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of science and technology, the workpiece has higher and higher requirements for machining accuracy. However, the existing drill bit adopts the general casting method, which often has the problems of low machining accuracy and large error, and cannot accurately process the workpiece.
Chinese patent application (CN103752907A) discloses a hollow drill bit and a preparation method thereof, which are prepared by machining, surfacing, quenching and tempering heat treatment, and vacuum coating antirust treatment. The advantages of not easy to deform and durable, but it is obvious that the processing error of the drill cannot be controlled by this preparation method
However, due to the lost wax casting method, the mold shell often has problems such as poor strength and deformation during the casting process, and it cannot be completely accurate, and further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high-precision drill bit

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The preparation method of high-precision drill bit among the present invention, comprises the steps:

[0051] Preparation of coating: by weight, 20 parts of zircon powder, 40 parts of corundum powder, 13 parts of primary SiO 2 Sol, 25 parts of secondary SiO 2 Sol, 0.3 parts of carbon nanotubes, 0.8 parts of mesoporous calcium carbonate, 1.3 parts of wetting agent, 0.3 parts of defoamer are mixed evenly to make a basic coating, and the basic coating is diluted with water to make a first-grade coating with a viscosity of 3 cp and a viscosity of 10cp of secondary paint;

[0052] Among them, the mesh numbers of zircon powder and corundum powder are 200-400 mesh. Primary SiO 2 The colloidal particle size of the sol is 8-12nm, and the secondary SiO 2 The colloidal particle size of the sol is 15-20nm.

[0053] Shell making: Spray the primary coating on the surface of the preformed meltable wax pattern under a vacuum of 0.05MPa for the first coating and hanging, the rotati...

Embodiment 2

[0058] The preparation method of high-precision drill bit among the present invention, comprises the steps:

[0059] Preparation of coating: by weight, 30 parts of zircon powder, 35 parts of mullite, 11 parts of primary SiO 2 Sol, 24 parts of secondary SiO 2 Sol, 0.4 parts of carbon nanotubes, 1.0 parts of mesoporous calcium carbonate, 1.4 parts of wetting agent, and 0.4 parts of defoamer are mixed evenly to make a base paint, and the base paint is diluted with water to make a first-grade paint with a viscosity of 3.5 cp and a viscosity of 3.5 cp. A secondary paint of 9cp;

[0060] Among them, the mesh numbers of zircon powder and mullite are 200-300 mesh. Primary SiO 2 The colloidal particle size of the sol is 8-10nm, and the secondary SiO 2 The colloidal particle size of the sol is 15-18nm.

[0061] Shell making: Under the vacuum degree of 0.08MPa, spin-spray the primary paint on the surface of the preformed meltable wax type for the first time, the rotation speed is 60...

Embodiment 3

[0066] The preparation method of high-precision drill bit among the present invention, comprises the steps:

[0067] Preparation of coating: by weight, 20 parts of zircon powder, 20 parts of corundum powder, 30 parts of alumina powder, 12 parts of primary SiO 2 Sol, 20 parts of secondary SiO 2 Sol, 0.5 parts of carbon nanotubes, 1.2 parts of mesoporous calcium carbonate, 1.5 parts of wetting agent, and 0.5 parts of defoamer are mixed evenly to make a basic coating, and the basic coating is diluted with water to make a primary coating with a viscosity of 4 cp and a viscosity of 8.5cp of secondary paint;

[0068] Among them, the mesh numbers of zircon powder, corundum powder and alumina powder are 250-350 mesh. Primary SiO 2 The colloidal particle size of the sol is 10-12nm, and the secondary SiO 2 The colloidal particle size of the sol is 18-20nm.

[0069]Shell making: Spray the primary coating on the surface of the preformed meltable wax pattern under a vacuum of 0.10MPa ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparation method for a high-precision drilling bit, and belongs to the technical field of casting. The preparation method includes shell preparing, roasting, melting casting and postprocessing, wherein the shell preparing comprises the steps: spraying a coating on a surface of a preformed fusible wax molding, sandblasting, drying, then dewaxing, preparing a shell green body, spraying the coating, and repeating the sandblasting and drying step for 2 to 5 times; the roasting comprises the steps: putting the shell green body into a roasting furnace, and roasting under a vacuum degree with 0.08 to 0.20MPa to obtain a shell. The drilling bit prepared by the invention is small in error, accurate in size and smooth in surface.

Description

technical field [0001] The invention belongs to the technical field of casting, and relates to a preparation method of a high-precision drill bit. Background technique [0002] The drill bit is a commonly used tool for drilling. The structure of the drill bit is usually with a cutting edge at the front end and a chip removal groove on the cutter body. When in use, the cutting end mainly bears the cutting force, and the chips are discharged through the chip flute. With the development of science and technology, the workpiece has higher and higher requirements for machining accuracy, but the existing drill bit adopts the general casting method, which often has the problems of low machining accuracy and large error, and cannot accurately process the workpiece. Chinese patent application (CN103752907A) discloses a hollow drill bit and a preparation method thereof, which are prepared by machining, surfacing, quenching and tempering heat treatment, and vacuum coating antirust tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C9/04B22C3/00
CPCB22C3/00B22C9/04B22C9/043
Inventor 练炳方
Owner 宁波神钻工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com