PBT material for automobile door handles, and preparation method thereof

A technology for door handles and automobiles. It is applied in the field of PBT materials. It can solve the problems of non-antibacterial properties and not very suitable for car door handles, etc., and achieve the effects of prolonging service life, enhancing chemical corrosion resistance, and enhancing impact resistance.

Inactive Publication Date: 2017-10-20
DONGGUAN LIANZHOU INTPROP OPERATION MANAGEMENT CO LTD
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The PBT-based composite material used in automobiles provided by the invention has good hydrolysis resistance and can maintain good performance in high-

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A PBT material for an automobile door handle, in parts by weight, comprising the following components:

[0026] 100 parts of PBT, 28 parts of ABS, 30 parts of EMA, Ag + / SiO 2 / TiO 2 25 parts of composite material, 6 parts of polydioxanone, 14 parts of sepiolite fiber, 1 part of stearyl polyoxyethylene ether, 9 parts of TMPTA, 11 parts of ethylene-methyl acrylate copolymer, deposited white carbon black 8 parts, 2 parts of titanate coupling agent, 1 part of antioxidant, the antioxidant is the mixture of antioxidant 168 and antioxidant 264;

[0027] The Ag + / SiO 2 / TiO 2 The preparation method of composite material, comprises the following steps:

[0028] Add ethyl silicate and tetrabutyl titanate to absolute ethanol in sequence, stir vigorously, add a mixture of glacial acetic acid and absolute ethanol dropwise at 40°C to form a transparent sol, let it stand for 84 hours to form a gel, and then dry it , ground into powder, and calcined at 630°C for 6h to obtain S...

Embodiment 2

[0033] A PBT material for an automobile door handle, in parts by weight, comprising the following components:

[0034] 100 parts of PBT, 35 parts of ABS, 40 parts of EMA, Ag + / SiO 2 / TiO 2 32 parts of composite material, 12 parts of polydioxanone, 19 parts of sepiolite fiber, 2 parts of stearyl polyoxyethylene ether, 11 parts of TMPTA, 17 parts of ethylene-methyl acrylate copolymer, deposited white carbon black 15 parts, 7 parts of titanate coupling agent, 2 parts of antioxidant, antioxidant is the mixture of antioxidant 168 and antioxidant 264;

[0035] The Ag + / SiO 2 / TiO 2The preparation method of composite material, comprises the following steps:

[0036] Add ethyl silicate and tetrabutyl titanate to absolute ethanol in sequence, stir vigorously, add a mixture of glacial acetic acid and absolute ethanol dropwise at 60°C to form a transparent sol, let it stand for 84 hours to form a gel, and then dry it , ground into powder, and calcined at 630°C for 6h to obtain S...

Embodiment 3

[0038] A PBT material for an automobile door handle, in parts by weight, comprising the following components:

[0039] 100 parts of PBT, 28 parts of ABS, 40 parts of EMA, Ag + / SiO 2 / TiO 2 25 parts of composite material, 12 parts of polydioxanone, 14 parts of sepiolite fiber, 2 parts of stearyl polyoxyethylene ether, 9 parts of TMPTA, 17 parts of ethylene-methyl acrylate copolymer, deposited white carbon black 8 parts, 7 parts of titanate coupling agent, 1 part of antioxidant, the antioxidant is the mixture of antioxidant 168 and antioxidant 264;

[0040] The Ag + / SiO 2 / TiO 2 The preparation method of composite material, comprises the following steps:

[0041] Add ethyl silicate and tetrabutyl titanate to absolute ethanol in sequence, stir vigorously, add a mixture of glacial acetic acid and absolute ethanol dropwise at 50°C to form a transparent sol, let it stand for 84 hours to form a gel, and then dry it , ground into powder, and calcined at 630°C for 6h to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PBT material for automobile door handles, and a preparation method thereof. The PBT material comprises, by weight, 100 parts of PBT, 28-35 parts of ABS, 30-40 parts of EMA, 25-32 parts of a Ag<+>/SiO2/TiO2 composite material, 6-12 parts of poly(p-dioxanone), 14-19 parts of sepiolite fibers, 1-2 parts of polyethylene glycol monooctadecyl ether, 9-11 parts of a compatilizer, 11-17 parts of a toughener, 8-15 parts of a filler, 2-7 parts of acoupling agent and 1-2 parts of an antioxidant. The PBT material prepared in the invention has the advantages of good mechanical properties, high rigidity and good antibacterial property, and is very suitable for being used as an automobile door handle material.

Description

technical field [0001] The invention relates to the field of PBT materials, in particular to a PBT material for automobile door handles and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) is a crystalline linear saturated polyester resin with excellent mechanical, electrical, chemical corrosion resistance and low moisture absorption properties. It is a plastic with excellent comprehensive properties. PBT resin also has the advantages of easy crystallization and fast molding speed; good physical properties, high mechanical strength, stable size, good fatigue resistance, etc., and no double bonds in the molecular chain, excellent weather resistance and wear resistance. Therefore, PBT material has developed quite rapidly since its inception, and has been widely used in the fields of electronic appliances, automobile industry, machinery, instrumentation and household appliances. [0003] In recent years, the application of PBT materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L55/02C08L23/08C08K13/06C08K9/12C08K9/04C08K3/36C08K3/22C08K7/10C08K5/526C08K3/28
CPCC08L67/02C08K2003/2241C08K2201/014C08L2201/08C08L2205/025C08L2205/035C08L55/02C08L23/0869C08K13/06C08K9/12C08K9/04C08K3/36C08K3/22C08K7/10C08K5/526C08K3/28
Inventor 陈东进
Owner DONGGUAN LIANZHOU INTPROP OPERATION MANAGEMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap