A kind of polypropylene foam material and preparation method thereof

A foaming material and polypropylene technology, applied in the field of foaming materials, can solve the problems of large cell diameter, insufficient low temperature resistance, environmental pollution, etc., and achieve the effect of 100% recycling and secondary pollution.

Inactive Publication Date: 2021-02-19
TIANJIN DALIN NEW MATERIAL TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, most of the existing polypropylene foam materials have poor cell uniformity, large cell diameter, poor toughness, and obviously insufficient low temperature resistance, which limits the application field of the material; and the preparation methods are mostly chemical methods. will cause some environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polypropylene foam material and preparation method thereof
  • A kind of polypropylene foam material and preparation method thereof
  • A kind of polypropylene foam material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of polypropylene foam material, comprises each component of following parts by weight:

[0047] Matrix resin: 40 parts by weight of high-melt strength polypropylene, 40 parts by weight of polypropylene random copolymer, and 5-30 parts by weight of low-density polyethylene;

[0048] The gas nucleating agent is talcum powder: add 0.2 parts by weight of talcum powder in every 100 parts by weight of matrix resin;

[0049] The physical blowing agent is supercritical butane: add 15 parts by weight of supercritical butane in the base resin of every 100 parts by weight;

[0050] The antioxidant is tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester: add 0.6 parts by weight in every 100 parts by weight of the base resin;

[0051] The cell stabilizer is monoglyceride: add 1.5 parts by weight per 100 parts by weight of the matrix resin.

[0052] The preparation method of polypropylene foam material in the present embodiment is:

[0053] (1) T...

Embodiment 2

[0058] A kind of polypropylene foam material, comprises each component of following parts by weight:

[0059] Matrix resin: 50 parts by weight of high-melt strength polypropylene, 45 parts by weight of polypropylene random copolymer, and 5 parts by weight of low-density polyethylene;

[0060] The gas nucleating agent is a 1:4 mixture of silicon dioxide and talcum powder: add 0.2 parts by weight in every 100 parts by weight of the matrix resin;

[0061] The physical blowing agent is a mixture of supercritical carbon dioxide and supercritical butane 1:6: add 3 parts by weight in the base resin of every 100 parts by weight;

[0062] The antioxidant is β-(3,5-di-tert-butyl-4-hydroxyphenyl) n-octadecyl propionate: add 0.6 parts by weight per 100 parts by weight of the base resin;

[0063] The cell stabilizer is monoglyceride: 1.1 parts by weight is added per 100 parts by weight of the matrix resin.

[0064] The preparation method of polypropylene foam material in the present embo...

Embodiment 3

[0070] A kind of polypropylene foam material, comprises each component of following parts by weight:

[0071] Matrix resin: 60 parts by weight of high melt strength polypropylene, 30 parts by weight of polypropylene random copolymer, and 10 parts by weight of low density polyethylene;

[0072] The gas nucleating agent is talcum powder: add 0.3 parts by weight in every 100 parts by weight of matrix resin;

[0073] The physical blowing agent is supercritical nitrogen: add 5 parts by weight of supercritical nitrogen in every 100 parts by weight of matrix resin;

[0074] The antioxidant is tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester: add 0.6 parts by weight in every 100 parts by weight of the base resin;

[0075] The cell stabilizer is monoglyceride: add 1.8 parts by weight per 100 parts by weight of the matrix resin.

[0076] The preparation method of polypropylene foam material in the present embodiment is:

[0077] (1) Add the high melt s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a polypropylene foam material and a preparation method thereof, wherein the polypropylene foam material comprises the following components in parts by weight: matrix resin: 30-70 parts by weight of high melt strength polypropylene, polypropylene random 10-50 parts by weight of copolymer, 5-30 parts by weight of low-density polyethylene; gas nucleating agent: 0.1-0.5 parts by weight of gas nucleating agent per 100 parts by weight of matrix resin; physical foaming agent: per 100 parts by weight Add 5 to 16 parts by weight of physical foaming agent in 10 parts of matrix resin; antioxidant: add 0.5 to 1 part by weight per 100 parts by weight of matrix resin; cell stabilizer: add 1 part by weight per 100 parts by weight of matrix resin ~10 parts by weight. The polypropylene foaming material described in the invention has good cell uniformity, high cell density, and does not cause secondary environmental pollution.

Description

technical field [0001] The invention belongs to the field of foam materials, and in particular relates to a polypropylene foam material and a method for preparing a polypropylene foam sheet or plate by a physical method. Background technique [0002] Foam plastic is a kind of polymer material formed by a large number of gas micropores dispersed in solid plastic. It has the characteristics of light weight, heat insulation, sound absorption, shock absorption, anti-corrosion, and low price, and its dielectric properties are better than matrix resin. Therefore, it is widely used in daily packaging, agriculture, industry, aerospace, transportation, military and other fields. [0003] Expanded polypropylene (EPP) is a high-crystallinity polypropylene / gas composite material with excellent performance. It has become the fastest-growing new environmental protection, pressure-resistant, cushioning and heat-insulating material in recent years due to its unique properties. . EPP produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/06C08K13/02C08K3/26C08K3/34C08K3/36C08J9/14C08J9/12B29C44/50B29C44/34
CPCB29C44/3442B29C44/50C08J9/122C08J9/141C08J2203/06C08J2203/08C08J2203/14C08J2203/182C08J2323/12C08J2323/14C08J2423/12C08J2423/14C08K2003/265C08L23/12C08L23/14C08L2203/14C08L2205/03C08L2205/24C08L2207/066C08L2207/14C08L23/06C08K13/02C08K3/26C08K3/34C08K3/36
Inventor 冷栋梁闫达陈丁猛杨丽含刘东方常秀娟
Owner TIANJIN DALIN NEW MATERIAL TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com