Lead sulfide thin film with wide absorption spectrum and preparation method of lead sulfide thin film

A technology of absorption spectrum and lead sulfide, which is applied in the field of lead sulfide film with wide absorption spectrum and its preparation, can solve the problems of not being able to obtain products with broad-band absorption characteristics and restricting applications, and achieve simple and easy-to-operate processes and scientific preparation methods Effect

Active Publication Date: 2017-11-03
HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI +1
View PDF13 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this thin-film product has blue-shifted its light absorption edge to the ultraviolet band, there are shortcomings in both the preparation method and the product. First, the light absorption peak of the product is limited to the range of 300-600nm, which limits the application occasions; Secondly, the preparation method cannot obtain products with broadband absorption characteristics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lead sulfide thin film with wide absorption spectrum and preparation method of lead sulfide thin film
  • Lead sulfide thin film with wide absorption spectrum and preparation method of lead sulfide thin film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The concrete steps of preparation are:

[0038] Step 1, according to the volume ratio of 1.5mol / L sodium hydroxide solution, 2.1mol / L thiourea solution, 7mol / L triethanolamine, 0.6mol / L lead acetate solution and deionized water is 5:4:0.2 : 6:70 ratio, first add sodium hydroxide solution, thiourea solution and triethanolamine to lead acetate solution in sequence to obtain a mixed solution; then add deionized water to the mixed solution to obtain a reaction solution.

[0039] In step 2, first place the substrate in a stirred reaction solution at 70° C. for 4 hours to obtain a substrate with reactants placed on its surface; wherein, the substrate is a glass substrate, and the stirring rate is 200 r / min. Then, the substrate with the reactant placed on its surface is cleaned and dried; wherein, the cleaning is cleaned twice with deionized water, and the drying is natural drying. made as figure 1 and figure 2 The broad absorption spectrum of the lead sulfide thin film sh...

Embodiment 2

[0041] The concrete steps of preparation are:

[0042] Step 1, according to the volume ratio of 1.55mol / L sodium hydroxide solution, 2.05mol / L thiourea solution, 7.2mol / L triethanolamine, 0.55mol / L lead acetate solution and deionized water is 5.5:3.5: The ratio of 0.25:5.5:70, first add sodium hydroxide solution, thiourea solution and triethanolamine to the lead acetate solution in sequence to obtain a mixed solution; then add deionized water to the mixed solution to obtain a reaction solution.

[0043] In step 2, first place the substrate in a stirred reaction solution at 73° C. for 3.5 hours to obtain a substrate with reactants placed on its surface; wherein, the substrate is a glass substrate, and the stirring rate is 210 r / min. Then, the substrate with the reactant placed on its surface is cleaned and dried; wherein, the cleaning is cleaned twice with deionized water, and the drying is natural drying. made as figure 1 and figure 2 The broad absorption spectrum of the l...

Embodiment 3

[0045] The concrete steps of preparation are:

[0046] Step 1, according to the volume ratio of 1.6mol / L sodium hydroxide solution, 2mol / L thiourea solution, 7.3mol / L triethanolamine, 0.5mol / L lead acetate solution and deionized water is 6:3:0.3 : The ratio of 5:70, first add sodium hydroxide solution, thiourea solution and triethanolamine to the lead acetate solution in sequence to obtain a mixed solution; then add deionized water to the mixed solution to obtain a reaction solution.

[0047] In step 2, first place the substrate in a stirred reaction solution at 75° C. for 3 hours to obtain a substrate with reactants placed on its surface; wherein, the substrate is a glass substrate, and the stirring rate is 220 r / min. Then, the substrate with the reactant placed on its surface is cleaned and dried; wherein, the cleaning is washed three times with deionized water, and the drying is natural drying. made as figure 1 and figure 2 The broad absorption spectrum of the lead sulf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a lead sulfide thin film with the wide absorption spectrum and a preparation method of the lead sulfide thin film. The thickness of the thin film is 500-540nm. The particle diameter of each lead sulfide crystal grain is 6-10nm. At the wave band of 450-220nm, the thin film consisting of the lead sulfide crystal grains the diameter of each of which 6-10nm displays an absorption peak. According to the invention, by use of the chemical vapour deposition method: firstly successively adding the sodium hydroxide solution, the thiourea solution and the triethanolamine solution into the lead acetate solution so as to obtain a mixed solution; then adding the deionized water into the mixed solution to obtain a reaction solution; arranging a substrate into the stirred reaction solution of the 70 DEG C-80 DEG C for at least 2h so as to obtain the substrate with the reagent on the surface; and cleaning and drying the substrate with the reagent on the surface to prepare the target product. According to the invention, the thin film has the quite wide wave band absorption characteristic, and is quite easily, widely and commercially applicable to field of photodetection, solar energy coating absorption layers and gas sensing detection.

Description

technical field [0001] The invention relates to a lead sulfide film and a preparation method thereof, in particular to a lead sulfide film with a wide absorption spectrum and a preparation method thereof. Background technique [0002] Lead sulfide (PbS) is an important IV-VI semiconductor material, because of its large Bohr exciton radius (18nm) and small intrinsic bandgap (0.41eV), it is in the near-infrared spectral region ( 1-3μm) has a very good response effect; therefore, lead sulfide has important applications in the fields of infrared sensing and detection. At the same time, lead sulfide also has a large nonlinear optical coefficient, and the film is uniform and fine, and has excellent properties such as corrosion resistance, high temperature resistance, and oxidation resistance. In recent years, people have made some beneficial attempts and efforts in the research and development of lead sulfide nanomaterials based on the special properties of nanomaterials that are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/22G02B1/10C01G21/21
CPCC01G21/21C01P2002/72C01P2002/84G02B1/10G02B5/22
Inventor 费广涛谢秉合许少辉
Owner HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com