Low-density outdoor wood plastic floor

A wood-plastic floor, low-density technology, used in buildings, building structures, floors, etc., can solve the problems of heavy weight, low mechanical properties, and reduced dimensional stability of materials, and achieve light weight, low density, shrinkage and other problems. Effect with low expansion rate

Inactive Publication Date: 2017-11-10
浙江坤鸿新材料有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As a building material, wood-plastic flooring has been widely used in outdoor decoration, but its mechanical properties are not high. In order to improve the mechanical properties of outdoor wood-plastic flooring, at this stage the market mostly uses wollastonite, short glass fibers and other materials with a certain length-to-diameter ratio. Fiber, these inorganic fillers can improve the tensile strength and bending strength of wood-plastic flooring, but the dimensional stability of the material decreases significantly, and the product density increases, resulting in heavy weight, which needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A low-density outdoor wood-plastic floor, the raw materials of which include by weight: 100 parts of main ingredients, 50 parts of fillers, 1 part of polyethylene glycol compound, 1.2 parts of maleic anhydride, 0.5 parts of titanate coupling agent, 2 parts of microcrystalline paraffin, 1 part of zinc stearate, 1.5 parts of antioxidant, 0.5 part of anti-ultraviolet light absorber, 1.5 parts of fireproofing agent, 0.5 part of antifreezing agent, and 1.5 parts of antifungal agent.

[0020] Among them: the main material includes PE particles, wood powder, polyurethane and is composed of 5:8:0.1 weight ratio.

Embodiment 2

[0022] An outdoor wood-plastic floor with low density, its raw materials include by weight: 140 parts of main materials, 40 parts of fillers, 4 parts of polyethylene glycol compound, 0.5 parts of maleic anhydride, 1.2 parts of titanate coupling agent, 1 part of microcrystalline paraffin, 2 parts of zinc stearate, 22460.5 parts of antioxidant, 1.5 parts of anti-ultraviolet light absorber, 0.5 part of fireproofing agent, 1.5 parts of antifreezing agent, and 0.5 part of antifungal agent.

[0023] Among them: the main material includes PE particles, wood powder, polyurethane and is composed of 10:6:0.5 weight ratio.

[0024] The polyethylene glycol complex is prepared by the following process: mix polyethylene glycol and water evenly, add chitosan and glacial acetic acid, stir at a temperature of 86°C, add toluene and pyridine, stir at a temperature of 68°C, add p-methyl Benzenesulfonyl chloride, stirred at a temperature of 84°C, washed with sodium bicarbonate solution, and dried ...

Embodiment 3

[0026] An outdoor wood-plastic floor with low density, its raw materials include by weight: 120 parts of main materials, 44 parts of fillers, 2 parts of polyethylene glycol compound, 1 part of maleic anhydride, 0.8 parts of titanate coupling agent, 1.6 parts of microcrystalline paraffin, 1.4 parts of zinc stearate, 1.2 parts of antioxidant, 0.8 part of anti-ultraviolet light absorber, 1 part of fireproofing agent, 0.8 part of antifreezing agent, and 1 part of antifungal agent.

[0027] Among them: the main material includes PE particles, wood powder, polyurethane and is composed of 8:7.5:0.2 weight ratio.

[0028] The filler includes white carbon black, short glass fibers, activated nano kaolin, and activated calcium carbonate. The weight ratio of white carbon black, short glass fiber, activated nano kaolin and activated calcium carbonate is 10:6:2:5.

[0029] The sheet thickness of activated nano kaolin is 20-50nm.

[0030] Among the short glass fibers, the fiber diameter i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
warpageaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-density outdoor wood plastic floor. Raw materials of the floor comprise, by weight, 100-140 parts of a main material, 40-50 parts of a filler, 1-4 parts of a polyethylene glycol compound, 0.5-1.2 parts of maleic anhydride, 0.5-1.2 parts of a titanate coupling agent, 1-2 parts of microcrystalline paraffin, 1-2 parts of zinc stearate, 0.5-1.5 parts of an antioxidant, 0.5-1.5 parts of an anti-ultraviolet light absorbent, 0.5-1.5 parts of a fire retardant, 0.5-1.5 parts of an antifreeze agent and 0.5-1.5 parts of a mildew inhibitor, wherein the main material includes PE particles, wood powder and polyurethane according to a weight ratio of (5-10):(6-8):(0.1-0.5). The floor has the advantages of guaranteed dimension stability, light weight and low cost.

Description

technical field [0001] The invention relates to the technical field of wood-plastic floors, in particular to an outdoor wood-plastic floor with low density. Background technique [0002] As a building material, wood-plastic flooring has been widely used in outdoor decoration, but its mechanical properties are not high. In order to improve the mechanical properties of outdoor wood-plastic flooring, at this stage the market mostly uses wollastonite, short glass fibers and other materials with a certain length-to-diameter ratio. Fiber, these inorganic fillers can improve the tensile strength and bending strength of wood-plastic flooring, but the dimensional stability of the material decreases significantly, and the product density increases, resulting in heavy weight, which needs to be solved urgently. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a low-density outdoor wood-plastic floor, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/06C08L75/04C08L5/08C08L71/02C08L91/06C08K13/02C08K5/098C08K7/14C08K3/36C08K3/34C08K3/26C08K5/10E04F15/10
CPCC08L97/02C08K2003/265C08K2201/003C08K2201/004C08K2201/011C08L23/06C08L2205/035C08L2205/04C08L2205/16E04F15/102C08L75/04C08L5/08C08L71/02C08L91/06C08K13/02C08K5/098C08K7/14C08K3/36C08K3/346C08K3/26C08K5/10
Inventor 沈国兴
Owner 浙江坤鸿新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap